Abstract
Earth-abundant and non-toxic Kesterite-based Cu2ZnSnS4 (CZTS) thin film solar cells are successfully fabricated on flexible Molybdenum (Mo) foil substrates by an electrodeposition-annealing route. A well-adherent, densely packed, homogeneous, compact, and mirror-like CZT precursor is initially produced through electrodeposition by using a rotating working electrode. Subsequently, the co-electrodeposited CuZnSn (CZT) precursor is sulfurized in quartz tube furnace at 550 °C for 2 h in N2 atmosphere with the presence of elemental sulfur in order to form CZTS. Different characterization techniques like XRD, SEM, HR-TEM, Raman, and Photoluminescence demonstrate that almost phase-pure CZTS formed after sulfurization. A flexible Al/Al-ZnO/i-ZnO/CdS/CZTS/Mo foil solar cell is produced, where CdS is deposited by chemical bath deposition and transparent conducting oxide (TCO) is deposited by DC sputtering. The CZTS solar device shows a 0.55% power conversion efficiency on flexible Mo foil substrate and it constitutes the first prototype of this kind of solar cell produced by electrodeposition-annealing route without any surface modification of the Mo substrate.
Graphic abstract
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Introduction
In order to make a real impact on worldwide energy demand (at the TW level), solar materials should be cheap, non-toxic, and earth-abundant, and they should provide high functional lifetime with high power conversion efficiency (PCE). Over the last few decades, thin film technologies based on direct band gap metal chalcogenides have shown the potential to produce photovoltaic (PV) cells with low cost along with easy fabrication routes. Kesterites-based chalcogenides like CZTS (Cu2ZnSnS4), CZTSe (Cu2ZnSnSe4), and mixed sulfo-selenide CZTSSe (Cu2ZnSn(S, Se)4) are attracting much attention nowadays from researchers as promising alternatives to existing commercialized CIGS (Cu(In, Ga)Se2) and CdTe absorber layers. This is due to the low cost of their mass production, as constituent elements in Kesterites are non-toxic and abundant in the earth’s crust compared to CIGS and CdTe. Moreover, they have suitable direct band gap near to 1.45 eV (CZTS), around 1 eV (CZTSe), and 1.0–1.5 eV (CZTSSe, depending on the S/(S + Se) ratio) together with high absorption coefficient (> 1 × 104 cm−1), which make them ideal among all the second generation thin film solar cells [1,2,3,4]. Furthermore, theoretical conversion efficiencies of Kesterites-based solar cells are around 32% like chalcopyrite according to Shockley-Queisser photon balance calculations [5]. Due to the rapid progress of the kesterite material development, the conversion efficiency of the Kesterites-based thin films solar cells have already advanced to 9.4% (CZTS) [6], 11.6% (CZTSe) [7], and 12.6% (CZTSSe) [8]. They are still far behind the theoretical conversion efficiency, despite these remarkable developments.
A suitable fabrication method is important to achieve high-quality Kesterites without having any defects, which ultimately govern the conversion efficiency. The volatile nature of some of their elemental constituents and related binary chalcogenides make the synthesis of stoichiometric Kesterites difficult [9, 10]. In addition, it is difficult to fabricate single-phase Kesterites as they exist within a narrow composition field which is normally known as a Cu-poor (Cu/(Zn + Sn) ≈ 0.7—0.9) and Zn-rich (Zn/Sn ≈ 1.1—1.4) range, according to the phase diagram [9,10,11,12]. Besides inappropriate chemical composition of the metallic precursors, binary/ternary chalcogenide phases could also be created due to decomposition of Kesterites at high temperature during sulfurization or selenization [13].Till now, different vacuum and non-vacuum deposition techniques have been deployed to fabricate Kesterites (CZTS, CZTSe and CZTSSe). Both vacuum and non-vacuum techniques are very much in competition on conversion efficiency, and in some cases, non-vacuum processes are even more efficient, contrary to the case of CIGS cells where vacuum-based techniques deliver higher conversion efficiencies [8]. Several non-vacuum techniques like sol–gel, electrodeposition, solution-based method etc. have been widely studied to fabricate Kesterites thin films [13,14,15].
Most of the Kesterites-based thin films solar cells have been fabricated till now on typical Mo-coated soda lime glass (SLG). There are only few reports on fabrication of Kesterites-based solar cells on the flexible substrate like metallic foils or polyimides, irrespective to the fabrication processes [16,17,18,19,20,21,22,23,24]. Fabrication of Kesterites-based thin film solar cells on the flexible substrate has huge potential in order to minimize production cost due to roll-to-roll manufacturing on the flexible substrate which enables the use of compact size deposition equipment with high throughput [25]. It is, however, important to point out that, in the case of flexible solar cells, efficiency depends on bending radius. Normally, an increase in efficiency for concave bending and a decrease in the case of convex bending is observed [26, 27]. Flexible metal foil substrates like molybdenum (Mo), stainless steel, aluminum (Al), titanium (Ti) etc. are potential candidates of back contact as they are cheap, durable, lightweight, and sustainable at high-temperature sulfurization or selenization processes. In addition to this, a metallic back contact layer is not required when metal substrate is used. On the other hand, the maximum operating temperature of polyimide is typically below 500 °C which makes it unsuitable for those fabrication processes where high-temperature annealing is involved in the presence of sulfur or selenium. Mo foil can be a better choice among all the flexible metallic foil substrates considering its capability to withstand very high temperature along with high conductivity and compatible coefficient of thermal expansion (5.2·10–6 K−1) [19]. Moreover, unlike stainless steel, it does not need any diffusion barrier layer to prevent migration of substrate atom during sulfurization or selenization. Till now, maximum power conversion efficiency of CZTS on flexible Mo foil substrate is 3.82% [19], whereas maximum conversion efficiency of CZTS on Mo-coated SLG is 9.4% [6]. On the other hand, maximum power conversion efficiency of CZTS solar cell on flexible stainless steel was reported to be 4.2% through sputtering-H2S reactive annealing process with the incorporation of alkali doping [18]. CZTS thin film solar cells on Mo foil achieving the efficiency of 3.82% have been fabricated through electrodeposition-annealing route. Point to be noted, before deposition of CZTS on Mo foil, 800 nm Mo back contact was deposited on Mo foil using DC sputtering in their work. Meanwhile, power conversion efficiencies of CZTS and CZTSe on Mo-coated SLG have already reached 8.1% [28] and 8.2% [29], respectively, through electrodeposition-annealing route. It has been demonstrated that alkali doping at the interface of CZTS and Mo has significant effects on the conversion efficiency of the solar cells which has already been observed in CIGS thin film solar cells [30]. On the other hand, formation of MoS2 at the interface of CZTS has also substantial effects on conversion efficiency as it is an indirect bandgap semiconductor with a gap of 1.3 eV which creates a back contact blocking (Schottky) barrier that restricts hole transport across the CZTS/Mo interface [31]. Compared to a variety of vacuum-based techniques and wet chemical methods, the material utilization rate in electrodeposition is better than 90%, partly due to the selectivity and partly because there is extensive know-how on the reuse and recycle of electroplating bath [32].
In this work, we fabricated 0.55% efficient CZTS thin film solar cells on flexible Mo foil substrate through electrodeposition-annealing route. Initially, a Cu–Zn-Sn (CZT) precursor is deposited on flexible Mo foil through co-electrodeposition, without sputtering a preliminary Mo layer. Other works reporting precursors deposition on unmodified Mo substrates are available in the literature [33, 34]. The present work, however, presents important elements of innovation and uniqueness. The most important is the approach followed for the deposition step, in which a single alkaline electrolyte is employed to directly deposit CZT. Kalinauskas et al. [33] and Stanchik et al. [34], on the contrary, report CZTS fabrication starting from multilayer precursors of the kind CuSn/Zn or Cu/Zn/Sn, all deposited from acidic electrolytes. Moreover, Stanchik et al. report CZTSe rather than CZTS fabrication. Finally, both Kalinauskas et al. and Stanchik et al. limit the investigation to material fabrication, without producing complete solar cells. Following electrodeposition, the CZT layer is sulfurized at high temperature to get CZTS. Good quality of CZTS depends on the quality of the CZT precursor, and for this reason, high-quality CZT precursor is prepared using rotating working electrode during co-electrodeposition. No sputtering steps are employed on Mo foil before co-electrodeposition of CZT unlike other works in the literature [19]. Following this approach, fabrication process can be considerably simplified and optimized in terms of cost and time.
2 Experimental section
2.1 Electrodeposition of the CZT precursor on Mo foil
Co-electrodeposition of Cu–Zn-Sn (CZT) was carried out under galvanostatic control in a conventional electrochemical cell assembly at room temperature. Formulation of electrolyte bath has already been described in the existing literature [35]. Briefly, such electrolyte contained 2.5 g/l CuSO4 5H2O, 15 g/l ZnSO4 7H2O, 10.5 g/l Na2SnO3 3H2O, 200 g/l K4P2O7, and 0.4 g/l CH3(CH2)11OSO3Na. A rotating working electrode was used in place of the simple vertical working electrode (at a rotation speed of 25–35 rpm). Its characteristics are detailed in the supporting materials (figure S1). Flexible Mo foil substrates (200 µm thick, Goodfellow) with an exposed area of 1.6 × 2.0 cm2 and titanium mesh were used as a working electrode and counter inert electrode, respectively. Mo substrates were cleaned in acetone, immersed in 32% wt. HCl for 10 min to remove oxide, washed in distilled water, and finally dried under N2 atmosphere. Mo foil was then mounted on the rotating electrode and the Mo surface was immersed horizontally in the electrolyte. A 30 rpm rotation speed was employed during electrodeposition. Electrodeposition experiments were accomplished by using an AMEL Model-549 Potentiostat. Electrodeposition runs have been performed by using 4.5 – 5.5 mA/cm2 current density for 7–8 min, while keeping the pH of the solution at 11. The electrolyte was dummied for 30 min at 5 mA/cm2 using the same anode/cathode configuration in order to eliminate impurities.
2.2 CZT sulfurization process
After electroplating CZT precursor, the sample was sulfurized at 550 °C for 2 h in a quartz tube furnace with the presence of 25 mg of elemental sulfur powder (Sigma Aldrich; reagent grade, 100 mesh particle size). During sulfurization, a heating rate of 20 °C/minute was used and a very small flow of N2 was maintained throughout the process [12, 35]. At the end of the process, CZTS was allowed to naturally cooldown.
2.3 CZTS solar cell construction
In order to form the p–n junction, n-type semiconductor CdS (≈70 nm) was deposited by chemical bath deposition on top of CZTS. An 80 nm intrinsic i-ZnO buffer layer, which acts to prevent any shunts, was then deposited by RF sputtering. Later, a TCO layer consisting of 350 nm Al-doped ZnO (AZO) was grown by DC-pulsed (2 kHz) sputtering. Finally, cells were completed by evaporating an Al grid contact on top of it. In this way, Al/Al-ZnO/i-ZnO/CdS/CZTS/Mo foil device has been prepared. 6 single cells, each characterized by a 0.15 cm2 area, were fabricated on each CZTS coated Mo foil. No anti-reflection coating was used during the measurement of the cells.
2.4 Characterization techniques
Composition, morphology, crystalline phases, and roughness of the CZT precursors and sulfurized CZTS films were investigated by SEM, Laser Profilometry, XRD, SEM, TEM, and Raman spectroscopy. Material band gap was investigated by Photoluminescence (PL) spectroscopy. The formation of impurity and MoS2 at the interface of CZTS and Mo was evaluated through HR-TEM and electron energy loss spectroscopy (EELS). The crystallographic phase of sulfurized films was analyzed by X-ray diffraction (XRD), using a Philips X-pert MPD instrument with CuKα1 radiation (1.5406 Å).The morphology and chemical compositions of the samples were studied by Scanning Electron Microscopy (Model Zeiss EVO 50) together with Energy Dispersive X-ray Spectroscopy (EDS) (Oxford instrument, Model 7060). UBM laser profilometer was used for assessing the roughness parameters. Raman measurements were carried out in the air at room temperature with a micro-Raman spectrometer (Horiba Jobin–Yvon Labram HR800) in the backscattering configuration. The 785 nm excitation wavelength has been used during the Raman characterization of the samples. To avoid the laser heating of the sample, the laser power density was kept as low as possible. The laser power was reduced from 100 to 1 mW at the sample passing through a suitable filtering system with spot size about 1 µm diameter. Here, the beam was focused on the sample using an objective lens with 50 × magnification. Photoluminescence (PL) spectra of the films have been acquired at 15 K temperature with above bandgap excitation (λexc = 805 nm). All PL measurements were performed with a spectral resolution of 6.6 nm using a standard lock-in technique in conjunction with a single grating monochromator and an InGaAs detector. Selected Area Electron Diffraction (SAED) and TEM observation were performed with a JEOL 2100F (Schottky) microscope equipped with a high-resolution pole piece, operated at 200 keV. EELS was acquired with a GIF Quantum and direct-detection sensor with a collection angle of 30 mrad [36]. Solar cell J-V characteristics were taken under Air Mass 1.5 conditions (simulating terrestrial applications) with a Abet Lot-Oriel Solar simulator with the constant incident power density of 1 Sun (100 mW/cm2) and with Keithley 2440 source meter. Representative data from each characterization technique are reported in the results section.
3 Results and discussion
3.1 CZT deposition on Mo flexible foil
Due to the large reduction potential window among Cu, Zn, and Sn metal ions, it is very difficult to co-electrodeposit CZT from single electrolyte. In our previous work, we were able to electrodeposit them together from single electrolyte where pyrophosphate was used as an only single complexing agent [35]. In order to obtain better precursors in terms of homogeneous distribution of elements and minimum roughness of the film with respect to previous works, here improved bath with rotating working electrode was employed during electrodeposition. It is possible to provide constant mass flux to the cathode surface using rotating working electrode which is very important to get homogeneous and smooth films. Moreover, it is believed that composition of various elements in the deposited film remains independent of the deposition times when the rotating working electrode is employed during co-electrodeposition [37].
It is well known that Cu-poor, Zn-rich precursor composition is necessary to obtain good kesterite CZTS film due to the narrow composition range for CZTS formation. This happens due to the volatile nature of S, SnS, and Zn during sulfurization which can vary the relative percentage of the elements to a great extent [9, 10, 12] and may result in poor kesterite films, characterized by the extensive formation of secondary phases. For this reason, in this study, Cu-poor and Zn-rich precursor (Cu 43.5 at. %, Zn 33 at. % and Sn 23.5 at. %; Cu/(Zn + Sn) = 0.77 and Zn/Sn = 1.4) has been employed for the fabrication of CZTS. Such CZT composition resulted in quasi-stoichiometric CZTS after annealing [12]. Figure 1 shows the surface morphology and cross-sectional view of the as-deposited CZT film observed by SEM. It is evident that the electrodeposited CZT film is quite homogenous, dense, and continuous, without visible porosity in the cross-section, unlike other results reported in the literature [38]. Moreover, CZT adhesion to the Mo substrate was found to be excellent. Average roughness of the CZT film was around 94 nm, while substrate roughness was around 100 nm, which is quite commendable for the co-electrodeposition of CZT.
3.2 Characterization of sulfurized CZTS on flexible Mo foil
Figure 2a shows the XRD diffractogram of sulfurized kesterite CZTS film. Here, the CZT precursor was sulfurized at 550 °C for 2 h with a heating rate of 20 °C/minute. All the XRD peaks of sulfurized sample correspond to the typical polycrystalline kesterite structure of CZTS (JCPDS card 26–0575) with intense (112) peak at 28.53° which is in agreement with findings of other studies [19, 35, 39,40,41]. The sharpness of the diffraction peaks indicates the high crystallinity of the film. Diffraction peaks of CZTS can also be attributed to the ternary phase Cu2SnS3, since they have similar lattice parameters, or to ZnS [42]. As a result, complementary Raman spectroscopy (Fig. 2b) was employed to further characterize the sample. In order to have the better understanding of the formation of CZTS along the film thickness, the 785 nm excitation wavelength has been used. According to previous studies [43], the penetration depth of the 785 nm laser beam in CZTS film is approximately 400 nm and this allows to explore deeper the sample with respect to the 514 nm excitation line with a penetration depth of only 150 nm.
Figure 2b displays the Raman spectrum of the sulfurized CZTS thin film measured at room temperature using the 785 nm excitation wavelength. All the main Raman peaks associated with CZTS were observed at 266 cm−1, 287 cm−1, 338 cm−1, 366 cm−1, and 376 cm−1 Raman shift including main intense peak at 338 cm−1 which is commonly mentioned in the literature [41, 43,44,45] and has been associated to the vibration of sulfur atoms [46]. The appearance of two distinct peaks around 367 cm−1 and 375 cm−1 is typical of Raman spectra of CZTS acquired with excitation laser wavelength of 785 nm [39, 43]. At lower excitation wavelengths, only a broad peak at 367 cm−1 is evident. In the Raman spectrum, some additional weaker peaks are also observed at 303 cm−1 (cubic Cu2SnS3) and 314 cm−1 (SnS2) as reported by other authors [43, 44]. Despite the presence of some secondary phases in film, crystalline CZTS is the largely dominant constituent of the film as the peak intensity of the secondary phases is very weak.
Further insight into the structural properties of the sulfurized CZTS film was gained through high-resolution TEM (HR-TEM) and EELS analysis of a focused ion beam (FIB) prepared using the cross-sectional sample. Figure 3 depicts the HR-TEM of the regions adjacent to the CZTS/Mo interface. TEM imaging and SAED show that the sample is primarily composed of CTZS grains several hundred nm in diameter, in agreement with XRD and Raman results (Fig. 3a and S2). Many twin boundaries and dislocations are visible inside the grains of the CZTS phase, as observed in other studies (Fig. S3 and S4) [47].
The interface between Mo and CZTS was analyzed thoroughly by using HR-TEM and electron energy loss spectroscopy (EELS). In addition to the CZTS, TEM revealed the presence of two secondary phases. As shown in Fig. 3, TEM imaging found a continuous and uniform layer separating the Mo substrate and CZTS film. EELS analysis of this layer shows only Mo and S (Fig. 4b, c), and HR-TEM shows a measured lattice spacing of 6.2 Angstroms (Fig. 3b). Given that the lattice constant of MoS2 is 6.11 Angstroms, the EELS and HR-TEM data indicate a layer of MoS2 formed between the Mo substrate and CZTS film. A third phase is observed in TEM, consisting of nanograin clusters. This phase has a relatively low concentration throughout the CZTS film (Fig. S5 and S6), but the concentration increases considerably near the Mo substrate (Fig. 3a). SAED of this phase is consistent with SnO2 (Fig. S5). Agreeing with this measurement, EELS shows that this phase only contains Sn and O (Fig. S6). We note that it is difficult to independently extract the O and Sn EELS signals since the O K edge overlaps the Sn M edge. However, Fig. 4d shows a map of the EELS signal from 470–590 eV, which includes both the O K and Sn M edges. Clearly, there is a large increase in the combined concentration and O + Sn within this third phase, and Mo, Cu, and S are all absent. By comparing EELS spectra extracted from the CZTS phase and the SnO2 phase, it is clear that both phases contain Sn, but O is only present within the SnO2 phase (Fig. S6). The spectra taken from the SnO2 region closely match those found in the literature [48]. HR-TEM of this phase shows a lattice spacing of 3.2 Angstroms, consistent with the expected value of 3.18 Angstroms for SnO2.
The presence of MoS2 and SnO2 were not detected by XRD or Raman analysis. However, it is possible that these phases were not detected with XRD because of their nanometric size and very low amount. It is also possible that they were located too deep in the CZTS layer to contribute to the Raman signal, provided that their content was above the detection limit of Raman spectroscopy. The source of the SnO2 clusters is presently unclear; it might be guessed that their formation was caused by the oxidizing impurities of the nitrogen gas used in the sulfurization step. SnO2 is a large bandgap oxide and a VB offset of approximately 1.5 eV is predicted to exist at the boundary between CZTS and SnO2; hence this interface might act as a barrier to hole transport [49, 50].
3.3 Complete CZTS solar cell characterization
After the morphological investigation of the formed CZTS layer, complete cells were fabricated. Figure 5 shows the SEM cross-sectional image of the CZTS solar cell, which demonstrates that CZTS possesses bimodal grain distribution where smaller grains are located near the interface with Mo and larger grains at the top of the CZTS.
In order to make sure that fabricated CZTS absorber layers are applicable to photonic devices (i.e., solar cells), samples were further characterized by Photoluminescence Spectroscopy (PL). A typical photoluminescence spectrum of CZTS films at 15 K is reported in Fig. S7, which shows an asymmetric broad band at 1.21 eV. Similar asymmetric emissions were observed in CZTS fabricated through various methods by different groups [45, 51,52,53]. According to the literature [51, 52], this band is associated to a quasi-donor–acceptor pair (QDAP) transition, which involves potential fluctuations, as commonly observed in highly defective and compensated semiconductors. It was also demonstrated that the presence of a QDAP emission with saturated peak energy position towards 1.18 eV in the PL spectrum of CZTS layers indicates them as efficient PV absorbers [54].
In order to test the efficiency of the grown layers as PV absorbers, CZTS thin films solar cells were fabricated on Mo foil with classical configuration (Al/Al-ZnO/i-ZnO/CdS/CZTS/Mo foil). Figure 6a shows the current–voltage (J-V) characteristics of CZTS solar cells measured under AM 1.5 illumination. As fabricated Al/Al-ZnO/i-ZnO/CdS/CZTS/Mo foil device shows 0.55% power conversion efficiency (PCE) with Jsc = 7.60 mA/cm2, Voc = 203.98 mV and FF = 35.68%. The low fill factor can come from high series resistance due to back contact electrical characteristics. In addition to this, non-adherence between various layers and morphological problems because of elemental losses during sulfurization can also contribute to lowering both Jsc and FF [55]. On the other hand, the small value of Voc is most probably related to the presence of recombination paths may be associated with grain boundaries or other defects. Formation of interfacial MoS2 during sulfurization process may affect the VOC and alter the band alignment between the CZTS film and MoS2/Mo. Hence, it may reduce the conversion efficiency of the solar cells since it is in inverse proportion to the solar cell characteristics after the certain limit. It was reported that the formation of MoS2 interfacial layer at the CZTS/Mo interface enhances the quasi-ohmic electrical contact when it forms with appreciable thickness [56]. On the other hand, a thick MoS2 layer at the CZTS/Mo interface can influence the total series resistance of the device [41]. However, Zhang et al. recently demonstrated 7.2% efficient CZTS solar cells without having any MoS2 layer [57]. By the way, HR-TEM suggest around 50 nm of MoS2 has been formed in our solar cells (Fig. 3). Moreover, the effect of alkali metals (Na, K) on the conversion efficiency of chalcogenide thin film solar cells cannot be ignored, as it has already been reported that alkali incorporation to CIGS increases its open circuit voltage and fill factor [58]. Though the alkali effect on the conversion efficiency was not extensively investigated for CZTS/CZTSe, results similar to those reported for CIGS have been found in case of CZTS also [59, 60]. Alkali incorporation in CZTS can affect the grain size of the final film, the (112) texturing, the free carrier concentration, the hole density and mobility of the film [58]. Yang et al. demonstrated that there is a directly proportional relationship between CZTS thin film solar cells efficiency and Na content in Mo layer. This is probably one of the main reasons why the efficiency of CZTS solar cells on the flexible substrate is far behind that of CZTS solar cells on Mo-coated SLG substrate. Recently Lopez-Marino et al. reported that an improvement in the conversion efficiency of CZTSe solar cells from 2.2% to 4.3% is possible using Mo-Na (Na doped Mo) layer sandwiched between regular Mo layers. After further optimizing the Cr diffusion barrier layer, they reported a record efficiency of 6.1% for a CZTSe solar cell on flexible stainless steel substrate prepared by the sputtering-annealing process [17]. Point to be noted, the device described in the present work is the first prototype of CZTS solar cells on flexible Mo substrate that is realized through electrodeposition-annealing route without any surface modification, to the best of our knowledge.
Figure 6b shows the external quantum efficiency (EQE) spectrum of our CZTS solar cell between 350 and 1000 nm. The EQE demonstrates a low overall spectrum response with the maximum value of 38.5% (at 510 nm) indicating a high recombination rate, in agreement with Voc value obtained by J-V characterization. The reduction of EQE spectrum in the short wavelength portion is ascribed to the absorption losses in the window and buffer layers (Al-ZnO, i-ZnO, CdS) [41]. On the other hand, recombination processes contribute to lower the EQE values in the long wavelength region.
4 Conclusions
A CZTS thin film solar cell was successfully synthesized on flexible Mo foil substrate by the electrodeposition-annealing method with 0.55% power conversion efficiency. A high-quality CZT precursor without any void or crevice was fabricated by the co-electrodeposition route using rotating working electrode. Formation of MoS2 at the interface, together with SnO2 formation near to MoS2, can explain the low performances of the final device. Moreover, the absence of alkali metal doping at the substrate can be also associated with such low efficiency of the cell. Nevertheless, first power conversion device based on CZTS thin film solar cell on flexible Mo foil substrate, which has been produced by electrodeposition-annealing route without any surface modification, was demonstrated. In perspective, the good adhesion obtained between the CZTS layer and the Mo substrate constitutes a suitable starting point to perform tests at controlled bending angle and defined number of bending cycles, since it will reasonably prevent active layer delamination. The CZTS cells obtained following the methodology described in the present work constitute, thus, a promising starting point for further process optimization and for additional testing under bending conditions.
References
Ito K, Nakazawa T (1988) Electrical and optical properties of stannite-type quaternary semiconductor thin films. Jpn J Appl Phys 27:2094
Nakayama N, Ito K (1996) Sprayed films of stannite Cu2ZnSnS4. Appl Surf Sci 92:171–175
Khalate SA, Kate RS, Deokate RJ (2018) A review on energy economics and the recent research and development in energy and the Cu2ZnSnS4 (CZTS) solar cells: A focus towards efficiency. Sol Energy 169:616–633
Pal K, Singh P, Bhaduri A, Thapa KB (2019) Current challenges and future prospects for a highly efficient (> 20%) kesterite CZTS solar cell: A review. Sol Energy Mater Sol Cells 196:138–156
Shockley W, Queisser HJ (1961) Detailed balance limit of efficiency of p-n junction solar cells. J Appl Phys 32:510–519
Tajima S, Umehara M, Hasegawa M et al (2017) Cu2ZnSnS4 photovoltaic cell with improved efficiency fabricated by high-temperature annealing after CdS buffer-layer deposition. Prog Photovoltaics Res Appl 25:14–22
Lee YS, Gershon T, Gunawan O et al (2015) Cu2ZnSnSe4 thin-film solar cells by thermal co-evaporation with 11.6% efficiency and improved minority carrier diffusion length. Adv Energy Mater 5(7):1401372
Wang W, Winkler MT, Gunawan O et al (2014) Device characteristics of CZTSSe thin-film solar cells with 12.6% efficiency. Adv Energy Mater 4:1301465
Scragg JJ, Ericson T, Kubart T et al (2011) Chemical insights into the instability of Cu2ZnSnS4 films during annealing. Chem Mater 23:4625–4633
Redinger A, Berg DM, Dale PJ, Siebentritt S (2011) The consequences of kesterite equilibria for efficient solar cells. J Am Chem Soc 133:3320–3323
Olekseyuk ID, Dudchak IV, Piskach LV (2004) Phase equilibria in the Cu2S–ZnS–SnS2 system. J Alloys Compd 368:135–143
Khalil MI, Bernasconi R, Ieffa S et al (2015) Effect of co-electrodeposited Cu-Zn-Sn precursor compositions on sulfurized CZTS thin films for solar cell. ECS Trans 64:33–41
Delbos S (2012) Kësterite thin films for photovoltaics: a review. EPJ Photovoltaics 3:35004
Toura H, Khattak YH, Baig F et al (2019) Effect of complexing agent on the morphology and annealing temperature of CZTS kesterite thin films by electrochemical deposition. Curr Appl Phys 19:606–613
Khattak YH, Baig F, Toura H et al (2019) Single step electrochemical deposition for the fabrication of CZTS kesterite thin films for solar cells. Appl Surf Sci 497:143794
López-Marino S, Neuschitzer M, Sánchez Y et al (2014) Earth-abundant absorber based solar cells onto low weight stainless steel substrate. Sol energy Mater Sol cells 130:347–353
López-Marino S, Sánchez Y, Espíndola-Rodríguez M et al (2016) Alkali doping strategies for flexible and light-weight Cu 2 ZnSnSe 4 solar cells. J Mater Chem A 4:1895–1907
Bras P, Sterner J, Platzer-Björkman C (2015) Influence of hydrogen sulfide annealing on copper–zinc–tin–sulfide solar cells sputtered from a quaternary compound target. Thin Solid Films 582:233–238
Zhang Y, Ye Q, Liu J et al (2014) Earth-abundant and low-cost CZTS solar cell on flexible molybdenum foil. Rsc Adv 4:23666–23669
Peng C-Y, Dhakal TP, Garner S et al (2014) Fabrication of Cu2ZnSnS4 solar cell on a flexible glass substrate. Thin Solid Films 562:574–577
Tian Q, Xu X, Han L et al (2012) Hydrophilic Cu 2 ZnSnS 4 nanocrystals for printing flexible, low-cost and environmentally friendly solar cells. CrystEngComm 14:3847–3850
Zhou Z, Wang Y, Xu D, Zhang Y (2010) Fabrication of Cu2ZnSnS4 screen printed layers for solar cells. Sol Energy Mater Sol Cells 94:2042–2045
Khalil MI, Bernasconi R, Pedrazzetti L et al (2017) Co-electrodeposition of metallic precursors for the fabrication of CZTSe thin films solar cells on flexible Mo foil. J Electrochem Soc 164:D302–D306
Sun K, Liu F, Huang J et al (2018) Flexible kesterite Cu2ZnSnS4 solar cells with sodium-doped molybdenum back contacts on stainless steel substrates. Sol Energy Mater Sol Cells 182:14–20
Reinhard P, Chirilă A, Blösch P, et al (2012) Review of progress toward 20% efficiency flexible CIGS solar cells and manufacturing issues of solar modules. In: 2012 IEEE 38th Photovoltaic Specialists Conference (PVSC) PART 2. IEEE, pp 1–9
Moaven S, Naji L, Taromi FA, Sharif F (2015) Effect of bending deformation on photovoltaic performance of flexible graphene/Ag electrode-based polymer solar cells. RSC Adv 5:30889–30901
Pei L, Yu H, Zhang Q et al (2020) Concave and Convex Bending Influenced Mechanical Stability in Flexible Perovskite Solar Cells. J Phys Chem C 124(4):2340–2345
Jiang F, Ikeda S, Tang Z et al (2015) Impact of alloying duration of an electrodeposited Cu/Sn/Zn metallic stack on properties of Cu2ZnSnS4 absorbers for thin-film solar cells. Prog Photovoltaics Res Appl 23:1884–1895
Vauche L, Risch L, Sánchez Y et al (2016) 8.2% pure selenide kesterite thin-film solar cells from large-area electrodeposited precursors. Prog Photovoltaics Res Appl 24:38–51
Yang K, Sim J, Jeon B et al (2015) Effects of Na and MoS2 on Cu2ZnSnS4 thin-film solar cell. Prog Photovoltaics Res Appl 23:862–873
Shin B, Zhu Y, Bojarczuk NA et al (2012) Control of an interfacial MoSe2 layer in Cu2ZnSnSe4 thin film solar cells: 8.9% power conversion efficiency with a TiN diffusion barrier. Appl Phys Lett 101:53903
Deligianni H, Ahmed S, Romankiw LT (2011) The next frontier: electrodeposition for solar cell fabrication. Electrochem Soc Interface 20:47
Kalinauskas P, Norkus E, Mockus Z et al (2020) The Influence of Removal of Secondary Phases and Dissolution By-Product from the Surface of Cu2ZnSnS4 Film on the Photoelectrochemical Response of This Film. J Electrochem Soc 167:26513
Stanchik AV, Gremenok VF, Bashkirov SA et al (2018) Microstructure and Raman scattering of Cu 2 ZnSnSe 4 thin films deposited onto flexible metal substrates. Semiconductors 52:215–220
Khalil MI, Bernasconi R, Magagnin L (2014) CZTS layers for solar cells by an electrodeposition-annealing route. Electrochim Acta 145:154–158
Hart JL, Lang AC, Leff AC et al (2017) Direct detection electron energy-loss spectroscopy: a method to push the limits of resolution and sensitivity. Sci Rep 7:1–14
Colombara D, Crossay A, Vauche L et al (2015) Electrodeposition of kesterite thin films for photovoltaic applications: Quo vadis? Phys status solidi 212:88–102
Kondrotas R, Juškėnas R, Naujokaitis A et al (2015) Characterization of Cu2ZnSnSe4 solar cells prepared from electrochemically co-deposited Cu–Zn–Sn alloy. Sol energy Mater Sol cells 132:21–28
Khalil MI, Atici O, Lucotti A et al (2016) CZTS absorber layer for thin film solar cells from electrodeposited metallic stacked precursors (Zn/Cu-Sn). Appl Surf Sci 379:91–97
Marchionna S, Garattini P, Le Donne A et al (2013) Cu2ZnSnS4 solar cells grown by sulphurisation of sputtered metal precursors. Thin Solid Films 542:114–118
Ahmed S, Reuter KB, Gunawan O et al (2012) A high efficiency electrodeposited Cu2ZnSnS4 solar cell. Adv Energy Mater 2:253–259
Walsh A, Chen S, Wei S, Gong X (2012) Kesterite thin-film solar cells: Advances in materials modelling of Cu2ZnSnS4. Adv Energy Mater 2:400–409
Fernandes PA, Salomé PMP, Da Cunha AF (2011) Study of polycrystalline Cu2ZnSnS4 films by Raman scattering. J Alloys Compd 509:7600–7606
Lin X, Kavalakkatt J, Kornhuber K et al (2013) Structural and optical properties of Cu2ZnSnS4 thin film absorbers from ZnS and Cu3SnS4 nanoparticle precursors. Thin Solid Films 535:10–13
Altosaar M, Raudoja J, Timmo K et al (2008) Cu2Zn1–x Cdx Sn (Se1–y Sy) 4 solid solutions as absorber materials for solar cells. Phys status solidi 205:167–170
Himmrich M, Haeuseler H (1991) Far infrared studies on stannite and wurtzstannite type compounds. Spectrochim Acta Part A Mol Spectrosc 47:933–942
Kattan N, Hou B, Fermín DJ, Cherns D (2015) Crystal structure and defects visualization of Cu2ZnSnS4 nanoparticles employing transmission electron microscopy and electron diffraction. Appl Mater Today 1:52–59
Lorenz H, Zhao Q, Turner S et al (2010) Preparation and structural characterization of SnO2 and GeO2 methanol steam reforming thin film model catalysts by (HR) TEM. Mater Chem Phys 122:623–629
Ge J, Yu Y, Ke W et al (2016) Improved Performance of Electroplated CZTS Thin-Film Solar Cells with Bifacial Configuration. Chemsuschem 9:2149–2158
Kim JH, Choi S, Choi M et al (2016) Atomic-scale observation of oxygen substitution and its correlation with hole-transport barriers in Cu2ZnSnSe4 thin-film solar cells. Adv Energy Mater 6:1501902
Le Donne A, Marchionna S, Garattini P, et al (2015) Effects of CdS buffer layers on photoluminescence properties of Cu2ZnSnS4 solar cells. Int J Photoenergy 2015:
Leitão JP, Santos NM, Fernandes PA et al (2011) Study of optical and structural properties of Cu2ZnSnS4 thin films. Thin Solid Films 519:7390–7393
Tanaka K, Miyamoto Y, Uchiki H et al (2006) Donor-acceptor pair recombination luminescence from Cu2ZnSnS4 bulk single crystals. Phys status solidi 203:2891–2896
Gershon T, Shin B, Gokmen T et al (2013) Relationship between Cu2ZnSnS4 quasi donor-acceptor pair density and solar cell efficiency. Appl Phys Lett 103:193903
Vauche L, Dubois J, Laparre A et al (2015) Rapid thermal processing annealing challenges for large scale Cu2ZnSnS4 thin films. Phys Status Solidi 212:103–108
Habas SE, Platt HAS, Van Hest MFAM, Ginley DS (2010) Low-cost inorganic solar cells: from ink to printed device. Chem Rev 110:6571–6594
Zhang Z, Yao L, Zhang Y et al (2018) Modified back contact interface of CZTSe thin film solar cells: elimination of double layer distribution in absorber layer. Adv Sci 5:1700645
Salomé PMP, Rodriguez-Alvarez H, Sadewasser S (2015) Incorporation of alkali metals in chalcogenide solar cells. Sol Energy Mater Sol Cells 143:9–20
Oo WMH, Johnson JL, Bhatia A et al (2011) Grain size and texture of Cu 2 ZnSnS 4 thin films synthesized by cosputtering binary sulfides and annealing: effects of processing conditions and sodium. J Electron Mater 40:2214
Prabhakar T, Jampana N (2011) Effect of sodium diffusion on the structural and electrical properties of Cu2ZnSnS4 thin films. Sol Energy Mater Sol Cells 95:1001–1004
Acknowledgements
MLT and JLH acknowledge funding in part from the Engineers As Global Leaders for Energy Sustainability EU-Atlantis Program supported by the US Department of Education, and in part from the National Science Foundation’s Major Research Instrumentation Program with award #1429661.
Funding
Open access funding provided by Politecnico di Milano within the CRUI-CARE Agreement.
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Below is the link to the electronic supplementary material.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Khalil, M.I., Bernasconi, R., Lucotti, A. et al. CZTS thin film solar cells on flexible Molybdenum foil by electrodeposition-annealing route. J Appl Electrochem 51, 209–218 (2021). https://doi.org/10.1007/s10800-020-01494-1
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10800-020-01494-1