Abstract
The steady-state energy release rate for tunneling cracks under mixed-mode loading is determined using finite element analyses. The balanced and symmetric laminate layup \([0/\theta /0/-\theta ]_s\) is investigated, where the tunneling crack is located parallel to the fiber direction of the central off-axis oriented layer. It is found that for the steady-state situation, a simple energy balance calculation of the released energy of the separated crack surfaces for a fully developed crack gives the same value as the average value of a detailed J-integral analysis of the crack front. Furthermore, the crack front mode-mixity, obtained by the same energy balance calculation, was found to give a good prediction of the average mode-mixity found from a detailed stress intensity calculation along the crack-tip. Based on this simplified energy balance approach, the energy release rate is determined for all angles \(\theta \in {]}0;90]^{\circ }\) for orthotropic elastic properties ranging from typical low modulus glass fiber reinforced polymers to high modulus carbon fiber reinforced polymers. The predicted results can be used to investigate the influence of the layup angles on static and fatigue tunnel crack evolution in composite materials used within, e.g. automotive, aerospace, and wind energy applications.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
Abaqus ABAQUS (2019) Theory manual. Online Documentaion Help, Dassault Systmes, p 2019
Bao G, Ho S, Suo Z, Fan B (1992) The role of material orthotropy in fracture specimens for composites. Int J Solids Struct 29(9):1105–1116. https://doi.org/10.1016/0020-7683(92)90138-J
Beuth JL (1992) Cracking of thin bonded films in residual tension. Int J Solids Struct 29(13):1657–1675. https://doi.org/10.1016/0020-7683(92)90015-L
Ho S, Suo Z (1993) Tunneling cracks in constrained layers. J Appl Mech 60:890–894
Hutchinson J, Suo Z (1992) Mixed mode cracking in layered materials. Adv Appl Mech 29:63–191
Jamison R, Schulte K, Reifsnider K, Stinchcomb W (1984) Characterization and Analysis of Damage Mechanisms in Tension-Tension Fatigue of Graphite/Epoxy Laminates. Astm Special Technical Publication, pages 21–55
Jespersen KM, Mikkelsen LP (2017) Three dimensional fatigue damage evolution in non-crimp glass fibre fabric based composites used for wind turbine blades. Compos Sci Technol 153:261–272. https://doi.org/10.1016/j.compscitech.2017.10.004
Jespersen KM, Glud JA, Zangenberg J, Hosoi A, Kawada H, Mikkelsen LP (2018) Uncovering the fatigue damage initiation and progression in uni-directional non-crimp fabric reinforced polyester composite. Compos A 109:481–497. https://doi.org/10.1016/j.compositesa.2018.03.002
Mikkelsen LP (2020) The fatigue damage evolution in the load-carrying composite laminates of wind turbine blades. In A. P. Vassilopoulos, editor, Fatigue Life Prediction of Composites and Composite Structures (Second Edition), Woodhead Publishing Series in Composites Science and Engineering, pages 569 – 603. Woodhead Publishing, second edition edition, ISBN 978-0-08-102575-8. https://doi.org/10.1016/B978-0-08-102575-8.00016-4
Mikkelsen LP, Klitgaard SJ, Niordson CF, Sørensen BF (2020) Tunneling cracks in arbitrary oriented off-axis lamina [data set]. Zenodo. https://doi.org/10.5281/zenodo.3633618
Nakamura T, Kamath SM (1992) Three-dimensional effects in thin film fracture mechanics. Mech Mater 13(1):67–77. https://doi.org/10.1016/0167-6636(92)90037-E
Quaresimin M, Carraro P, Mikkelsen L, Lucato N, Vivian L, Brøndsted P, Sørensen B, Varna J, Talreja R (2014) Damage evolution under cyclic multiaxial stress state: a comparative analysis between glass/epoxy laminates and tubes. Compos B 61:282–290. https://doi.org/10.1016/j.compositesb.2014.01.056
Reifsnider K, Jamison R (1982) Fracture of fatigue-loaded composite laminates. Int J Fatigue 4(4):187–197. https://doi.org/10.1016/0142-1123(82)90001-9
Shih CF, Asaro RJ (1988) Elastic-Plastic Analysis of Cracks on Bimaterial Interfaces: Part I - Small Scale Yielding. J Appl Mech 2:299. https://doi.org/10.1115/1.3173676
Shih CF, Moran B, Nakamura T (1986) Energy release rate along a three-dimensional crack front in a thermally stressed body. Int J Fract 30(2):79–102. https://doi.org/10.1007/BF00034019
Sørensen BF, Jacobsen TK (2009) Characterizing delamination of fibre composites by mixed mode cohesive laws. Compos Sci Technol 69(3):445–456. https://doi.org/10.1016/j.compscitech.2008.11.025
Suo Z, Bao G, Fan B, Wang T (1991) Orthotropy rescaling and implications for fracture in composites. Int J Solids Struct 28(2):235–248. https://doi.org/10.1016/0020-7683(91)90208-W
Talreja R (1981) Fatigue of composite materials: damage mechanisms and fatigue-life diagrams. Proc R Soc A 378(1775):461–475. https://doi.org/10.1098/rspa.1981.0163
Tong J (2000) Three stages of fatigue crack growth in GFRP composite laminates. J Eng Mater Technol 123(1):139–143. https://doi.org/10.1115/1.1286234 02
Tong J, Guild F, Ogin S, Smith P (1997) On matrix crack growth in quasi-isotropic laminates — I Experimental investigation. Compos Sci Technol 57(11):1527–1535. https://doi.org/10.1016/S0266-3538(97)00080-8
Varna J, Joffe R, Akshantala NV, Talreja R (1999) Damage in composite laminates with off-axis plies. Compos Sci Technol 59(14):2139–2147. https://doi.org/10.1016/S0266-3538(99)00070-6 ISSN 02663538
Wang Y, Mikkelsen LP, Pyka G, Withers P (2018) Time-lapse helical X-ray computed tomography (CT) study of tensile fatigue damage formation in composites for wind turbine blades. Materials 11:2340. https://doi.org/10.3390/ma11112340
Zangenberg J, Brøndsted P, Gillespie JW (2013) Fatigue damage propagation in unidirectional glass fibre reinforced composites made of a non-crimp fabric. J Compos Mater 48:2711–2727. https://doi.org/10.1177/0021998313502062
Acknowledgements
The tunnelling crack problem is central in the CASMaT (Villum Center for Advanced Structural and MAterial Testing) Initiation Project.
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Mikkelsen, L.P., Klitgaard, S.J., Niordson, C.F. et al. Tunneling cracks in arbitrary oriented off-axis lamina. Int J Fract 226, 161–179 (2020). https://doi.org/10.1007/s10704-020-00485-9
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10704-020-00485-9