Abstract
An effective photocatalyst obtained from composite nanofibers CA/GO fabricated by electrospinning technique followed by chemical crosslinking surface modified TiO2 nanoparticles (NPs) was used for removing the organic dyes Indigo carmine (IC) and Methylene blue (MB) from an aqueous solution under UV irradiation light. The crystalline structure and morphologies of CA–GO/TiO2–NH2 composite nanofibers were characterized by SEM, TEM, XRD, and FTIR. The prepared CA–GO/TiO2–NH2 composite nanofibers displayed significantly enhanced photocatalytic activity for photodegradation the organic dyes IC and MB under UV irradiation after 150 and 250 min respectively. The pH value of the solution was studied from 2 to 8 and obtained results showed a clear improvement of photocatalytic activity at pH 2. The results indicated that the activated CA–GO/TiO2–NH2 composite nanofibers functioned as an adsorbent for the removal of IC and MB from aqueous solutions. In addition, the results showed a high adsorption capacity remain up to 65% after five consecutive capacity cycles.
Similar content being viewed by others
References
Aboamera NM, Mohamed A, Salama A et al (2017) Characterization and mechanical properties of electrospun cellulose acetate/graphene oxide composite nanofibers. Mech Adv Mater Struct. https://doi.org/10.1080/15376494.2017.1410914
Al-Degs Y, Khraisheh MAM, Allen SJ, Ahmad MNA (2001) Sorption behavior of cationic and anionic dyes from aqueous solution on different types of activated carbons. Sep Sci Technol 36:91–102
Azizi S, Ahmad M, Mahdavi M, Abdolmohammadi S (2013) Preparation, characterization, and antimicrobial activities of ZnO nanoparticles/cellulose nanocrystal nanocomposites. BioResources 8:1841–1851
Bubacz K, Choina J, Dolat D, Morawski AW (2010) Methylene blue and phenol photocatalytic degradation on nanoparticles of anatase TiO2. Pol J Environ Stud 19:685–691. https://doi.org/10.1016/j.matlet.2011.06.005
Compd JA (2011) Enhanced photocatalytic degradation of methylene blue by ZnO-reduced graphene oxide composite synthesized via microwave. J Alloys Compund. https://doi.org/10.1016/j.jallcom.2011.08.045
Cong Y, Li X, Qin Y et al (2011) Carbon-doped TiO2 coating on multiwalled carbon nanotubes with higher visible light photocatalytic activity. Appl Catal B Environ 107:128–134. https://doi.org/10.1016/j.apcatb.2011.07.005
Dadvar E, Kalantary RR, Ahmad Panahi H, Peyravi M (2017) Efficiency of polymeric membrane graphene oxide-TiO2 for removal of azo dye. J Chem 2017:6217987. https://doi.org/10.1155/2017/6217987
Dula T, Siraj K, Kitte SA (2014) Adsorption of hexavalent chromium from aqueous solution using chemically activated carbon prepared from locally available waste of bamboo (Oxytenanthera abyssinica)
Geçgel Ü, Özcan G, Gürpınar GÇ (2013) Removal of methylene blue from aqueous solution by activated carbon prepared from pea shells (Pisum sativum). J Chem 2013:614083. https://doi.org/10.1155/2013/614083
Gopiraman M, Fujimori K, Zeeshan K et al (2013) Structural and mechanical properties of cellulose acetate/graphene hybrid nanofibers: spectroscopic investigations. Express Polym Lett 7:554–563. https://doi.org/10.3144/expresspolymlett.2013.52
Haque MM, Bahnemann D, Muneer M (2003) photocatalytic degradation of organic pollutants. Mech Kinet 3
Jung JY, Lee D, Lee YS (2015) CNT-embedded hollow TiO2 nanofibers with high adsorption and photocatalytic activity under UV irradiation. J Alloys Compd 622:651–656. https://doi.org/10.1016/j.jallcom.2014.09.068
Kabiri R, Namazi H (2014) Nanocrystalline cellulose acetate (NCCA)/graphene oxide (GO) nanocomposites with enhanced mechanical properties and barrier against water vapor. Cellulose. https://doi.org/10.1007/s10570-014-0366-4
Karim SA, Mohamed A, Abdel-Mottaleb MM et al (2018) Mechanical properties and the characterization of polyacrylonitrile/carbon nanotube composite nanofiber. Arab J Sci Eng. https://doi.org/10.1007/s13369-018-3065-x
Karthikeyan T, Rajgopal S, Miranda LR (2005) Chromium (VI) adsorption from aqueous solution by Hevea Brasilinesis sawdust activated carbon. J Hazard Mater 124:192–199
Khalil W, Mohamed A, Bayoumi M, Osman TA (2016) Tribological properties of dispersed carbon nanotubes in lubricant. Fuller Nanotub Carbon Nanostruct. https://doi.org/10.1080/1536383X.2016.1188804
Lee C, Wei X, Kysar JW, Hone J (2008) Measurement of the elastic properties and intrinsic strength of monolayer graphene. Science 321:385–388. https://doi.org/10.1126/science.1157996
Liu C, Bai R (2006) Adsorptive removal of copper ions with highly porous chitosan/cellulose acetate blend hollow fiber membranes. J Memb Sci 284:313–322
Liu G, Liu S, Lu Q et al (2014) BiVO4/cobalt phthalocyanine (CoPc) nanofiber heterostructures: synthesis, characterization and application in photodegradation of methylene blue. RSC Adv 4:53402–53406. https://doi.org/10.1039/C4RA08759C
Liu H, Zhang Y, Yang H et al (2016) Study on synthesis and photocatalytic activity of porous titania nanotubes. Adv Mater Sci Eng. https://doi.org/10.1155/2016/3532817
Liu M, Liu Y, Zhang D et al (2017) Facile fabrication of H2BDC-NH2 modified anatase TiO2 for effective photocatalytic degradation of azo dyes. Can J Chem Eng 95:1–9. https://doi.org/10.1002/cjce.22740
Lu M-C, Roam G-D, Chen J-N, Huang CP (1993) Factors affecting the photocatalytic degradation of dichlorvos over titanium dioxide supported on glass. J Photochem Photobiol A Chem 76:103–110
Makama AB, Salmiaton A, Saion EB et al (2016) Synthesis of CdS sensitized TiO2 photocatalysts: methylene blue adsorption and enhanced photocatalytic activities. Int J Photoene. https://doi.org/10.1155/2016/2947510
Miller SM, Spaulding ML, Zimmerman JB (2011) Optimization of capacity and kinetics for a novel bio-based arsenic sorbent, TiO2-impregnated chitosan bead. Water Res 45:5745–5754
Mohamed A, El-sayed R, Osman TA et al (2016a) Composite nano fibers for highly efficient photocatalytic degradation of organic dyes from contaminated water. Environ Res 145:18–25. https://doi.org/10.1016/j.envres.2015.09.024
Mohamed A, Osman TA, Toprak MS et al (2016b) Visible light photocatalytic reduction of Cr(VI) by surface modified CNT/titanium dioxide composites nanofibers. J Mol Catal A: Chem 424:45–53. https://doi.org/10.1016/j.molcata.2016.08.010
Mohamed A, Nasser WS, Osman TA et al (2017a) Removal of chromium (VI) from aqueous solutions using surface modified composite nanofibers. J Colloid Interface Sci. https://doi.org/10.1016/j.jcis.2017.06.066
Mohamed A, Osman TA, Toprak MS et al (2017b) Surface functionalized composite nano fibers for effi cient removal of arsenic from aqueous solutions. Chemosphere 180:108–116. https://doi.org/10.1016/j.chemosphere.2017.04.011
Mohamed A, Yousef S, Ali M et al (2017c) Photocatalytic degradation of organic dyes and enhanced mechanical properties of PAN/CNTs composite nanofibers. Sep Purif Technol 182:219–223. https://doi.org/10.1016/j.seppur.2017.03.051
Pan JH, Walcarius A, Pan JH et al (2010) Advanced materials for water treatment porous photocatalysts for advanced water purifications. J Mater Chem. https://doi.org/10.1039/b925523k
Peng S, Meng H, Ouyang Y, Chang J (2014) Nanoporous magnetic cellulose–chitosan composite microspheres: preparation, characterization, and application for Cu (II) adsorption. Ind Eng Chem Res 53:2106–2113
Salama A, Mohamed A, Aboamera NM et al (2017) Characterization and mechanical properties of cellulose acetate/carbon nanotube composite nanofibers. Adv Polym Technol. https://doi.org/10.1002/adv.21919
Salama A, Mohamed A, Aboamera NM et al (2018) Photocatalytic degradation of organic dyes using composite nanofibers under UV irradiation. Appl Nanosci 8:155–161. https://doi.org/10.1007/s13204-018-0660-9
Swaminathan S, Muthumanickkam A, Imayathamizhan NM (2014) An effective removal of methylene blue dye using polyacrylonitrile yarn waste/graphene oxide nanofibrous composite. J Environ Sci Technol. https://doi.org/10.1007/s13762-014-0711-z
Thunberg J (2015) Chemical modification of electrospun cellulose nanofibers. Chalmers University of Technology, Gothenburg
Uhl FM, Wilkie CA (2002) Polystyrene/graphite nanocomposites: effect on thermal stability. Polym Degrad Stab 76:111–122
Umar M, Aziz HA (2013) Photocatalytic degradation of organic pollutants in water
VanderHart DL, Hyatt JA, Atalla RH, Tirumalai VC (1996) Solid-state 13C NMR and Raman studies of cellulose triacetate: oligomers, polymorphism, and inferences about chain polarity. Macromolecules 29:730–739. https://doi.org/10.1021/ma9501860
Wang XH, Li J-G, Kamiyama H et al (2006) Wavelength-sensitive photocatalytic degradation of methyl orange in aqueous suspension over iron (III)-doped TiO2 nanopowders under UV and visible light irradiation. J Phys Chem B 110:6804–6809
Wu F, Lu Y, Shao G et al (2012) Preparation of polyacrylonitrile/graphene oxide by in situ polymerization. Polym Int. https://doi.org/10.1002/pi.4221
Xiang C, Yang F, Li M et al (2013) Experimental and statistical analysis of surface charge, aggregation and adsorption behaviors of surface-functionalized titanium dioxide nanoparticles in aquatic system. J nanoparticle Res 15:1293
Yousef S, Mohamed A, Tatariants M (2018) Mass production of graphene nanosheets by multi-roll milling technique. Tribol Int 121:54–63
Yuan Y, Zhang G, Li Y et al (2013) Poly (amidoamine) modified graphene oxide as an efficient adsorbent for heavy metal ions. Polym Chem 4:2164–2167
Zaleska A (2008) Doped-TiO2: a review. Recent patents Eng 2:157–164
Zhu Y, Murali S, Cai W et al (2010) Graphene and graphene oxide: synthesis, properties, and applications. Adv Mater 22:3906–3924
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Aboamera, N.M., Mohamed, A., Salama, A. et al. An effective removal of organic dyes using surface functionalized cellulose acetate/graphene oxide composite nanofibers. Cellulose 25, 4155–4166 (2018). https://doi.org/10.1007/s10570-018-1870-8
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10570-018-1870-8