A benchmark of mechanical properties and operational parameters of different steel filler metals for wire arc additive manufacturing

  • ORIGINAL ARTICLE
  • Published:
The International Journal of Advanced Manufacturing Technology Aims and scope Submit manuscript

Abstract

Additive manufacturing processes play a disruptive role in several industrial sectors. Among them, wire arc additive manufacturing (WAAM) is a very promising process for the production of large-scale steel components and structures. As a common characteristic of innovative technologies, this process requires additional research and experimental work in order to understand how its thermal cycles will modify the mechanical and metallurgical properties of the manufactured components. Considering the lack of literature on the properties of WAAM components from specific steel alloys, the present work proposes a benchmark evaluation of five different steel filler metals based on their mechanical properties and operational parameters when applied for additive manufacturing. The mechanical properties, such as the tensile strength, yield strength, elongation, Charpy impact toughness, and hardness, were evaluated together with operational parameters such as cost, printability, spatter, and fume formation during manufacturing, defect-free printing, and heat input. These were analyzed in order to obtain a full evaluation and comparison of the five filler metals. The experimentally determined results of every above-mentioned aspect were higher or similar to the values found in the literature for generic steel filler metals used in additive manufacturing. This means that a designer or welding engineer can select the WAAM steel filler metal for further testing based on the welding wire datasheet. Besides that, a comparison was performed between blocks manufactured by WAAM with some frequently used base metals, in plate format, confirming its applicability.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10
Fig. 11
Fig. 12
Fig. 13
Fig. 14
Fig. 15

Similar content being viewed by others

References

  1. Thompson MK, Moroni G, Vaneker T, Fadel G, Campbell RI, Gibson I, Bernard A, Schulz J, Graf P, Ahuja B, Martina F (2016) Design for additive manufacturing: trends, opportunities, considerations, and constraints. CIRP Ann Manuf Technol 65(2):737–760

    Article  Google Scholar 

  2. Buchanan C, Gardner L (2019) Metal 3D printing in construction: a review of methods, research, applications, opportunities and challenges. Eng Struct 180:332–348

    Article  Google Scholar 

  3. Guo N, Leu MC (2013) Additive manufacturing: technology, applications and research needs. Front Mech Eng 8(3):215–243

    Article  Google Scholar 

  4. Treuler K, Wesling V (2021) The current state of research of wire arc additive manufacturing (WAAM): a review. Appl Sci 11:8619

    Article  Google Scholar 

  5. ISO/ASTM 52900, Additive manufacturing – general principles – terminology, ASTM International, West Conshohocken, PA, 2015

  6. Queguineur A, Ruckert G, Cortial F, Hascoet JY (2018) Evaluation of wire arc additive manufacturing for large-sized components in naval applications. Welding in the World. 62:259–266

    Article  Google Scholar 

  7. Wesling V, Bohn C, Ehlers R, Esderts A, Hartmann S, Lohrengel A, Lorenz S, Rausch A, Rembe C, Inkermann D et al. (2021) Werkstofforientierte Prozesskette für Multimaterielle, Lichtbogenadditiv Gefertigte (WAAM) Strukturbauteile; Collaborative Research Center of the German Research Foundation (DFG): Clausthal-Zellerfeld, Germany

  8. Treutler K, Wesling V (2021) The current state of research of wire arc additive manufacturing (WAAM): a review. Appl Sci 11:8619

    Article  Google Scholar 

  9. Selvi S, Vishvaksenan A, Rajasekar E (2018) Cold metal transfer (CMT) technology – an overview. Defence Technol 14 (1). https://doi.org/10.1016/j.dt.2017.08.002

  10. Galeazzi D, Silva RHG, Pigozzo I, Rosa AF, Pereira AS, Marques C (2022) Analysis of current pulse during short-circuit phase in CMT version of GMAW process under a view of additive manufacturing. Welding in the World

  11. ISO/TR 25901–1:2016. Welding and allied processes — vocabulary — Part 1: General terms

  12. Hunko WS, Payton LN (2016) Development of wire 3D (Wir3D) printing parameters 1–8

  13. Nemani AV, Ghaffari M, Nasiri A (2020) On the post-printing heat treatment of a wire arc additively manufactured er70s part. Materials (Basel) 13:1–13

    Google Scholar 

  14. Ron T, Levy GK, Dolev O, Leon A, Shirizly A, Aghion E (2019) Environmental behavior of low carbon steel produced by a wire arc additive manufacturing process. Metals (Basel) 9

  15. Müller J, Grabowski M, Müller C, Hensel J, Unglaub J, Thiele K, Kloft, Dilger K (2019) Design and parameter identification of wire and arc additively manufactured (WAAM) steel bars for use in construction, Metals (Basel). 9

  16. Dirisu P, Ganguly S, Mehmanparast A, Martina F, Williams S (2019) Analysis of fracture toughness properties of wire + arc additive manufactured high strength low alloy structural steel components. Mater Sci Eng A 765:138285

    Article  Google Scholar 

  17. Le VT, Mai DS, Hoang QH (2020) A study on wire and arc additive manufacturing of low-carbon steel components: process stability, microstructural and mechanical properties. J Brazilian Soc Mech Sci Eng 42:1–11

    Article  Google Scholar 

  18. Michl D, Sydow B, Bambach M (2020) Ring rolling of pre-forms made by wire-arc additive manufacturing. Procedia Manuf 47:342–348

    Article  Google Scholar 

  19. Aldalur E, Veiga F, Suárez A, Bilbao J, Lamikiz A (2020) Analysis of the wall geometry with different strategies for high deposition wire arc additive manufacturing of mild steel. Metals (Basel) 10:1–19

    Article  Google Scholar 

  20. Aldalur E, Veiga F, Suárez A, Bilbao J, Lamikiz A (2020) High deposition wire arc additive manufacturing of mild steel: strategies and heat input effect on microstructure and mechanical properties. J Manuf Process 58:615–626

    Article  Google Scholar 

  21. Le VT, Banh TL, Nguyen DT, Le VT (2020) Wire arc additive manufacturing of thin-wall low-carbon steel parts: microstructure and mechanical properties. Int J Mod Phys B 34:1–5

    Article  Google Scholar 

  22. Dirisu P, Supriyo G, Martina F, Xu X, Williams S (2020) Wire plus arc additive manufactured functional steel surfaces enhanced by rolling. Int J Fatigue 130:105237

    Article  Google Scholar 

  23. Lizarazu J, Göbel L, Linne S, Kleemann S, Lahmer T, Rößler C, Hildebrand J (2020) Experimental characterization and numerical analysis of additively manufactured mild steel under monotonic loading conditions. Prog Addit Manuf 5:295–304

    Article  Google Scholar 

  24. Ron T, Levy GK, Dolev O, Leon A, Shirizly A, Aghion E (2020) The effect of microstructural imperfections on corrosion fatigue of additively manufactured ER70S-6 alloy produced by wire arc deposition. Metals (Basel) 10:98

    Article  Google Scholar 

  25. Ermakova A, Mehmanparast A, Ganguly S, Razavi J, Berto F (2020) Investigation of mechanical and fracture properties of wire and arc additively manufactured low carbon steel components. Theor Appl Fract Mech 109:102685

    Article  MATH  Google Scholar 

  26. Vahedi Nemani A, Ghaffari M, Nasiri A (2020) Comparison of microstructural characteristics and mechanical properties of shipbuilding steel plates fabricated by conventional rolling versus wire arc additive manufacturing. Addit Manuf 32

  27. Ahsan MRU, Tanvir ANM, Seo GJ, Bates B, Hawkins W, Lee C, Liaw PK, Noakes M, Nycz A, Kim DB (2020) Heat-treatment effects on a bimetallic additively manufactured structure (BAMS) of the low-carbon steel and austenitic-stainless steel. Addit Manuf 32:101036

    Google Scholar 

  28. Astarita A, Campatelli G, Corigliano P, Epasto G, Montevecchi F, Scherillo F, Venturini G (2021) Microstructure and mechanical properties of specimens produced using the wire-arc additive manufacturing process. Proc Inst Mech Eng Part C J Mech Eng Sci 235:1788–1798

    Article  Google Scholar 

  29. Xiong X, Qin X, Ji F, Hu Z, Hua L (2021) Microstructure and mechanical properties of wire + arc additively manufactured mild steel by welding with trailing hammer peening, Steel Res Int 2100238

  30. Ayan Y, Kahraman N (2021) wire arc additive manufacturing of low-carbon mild steel using two different 3D printers. Phys Met Metallogr

  31. Reisgen U, Sharma R, Mann S, Oster L (2020) Increasing the manufacturing efficiency of WAAM by advanced cooling strategies. Weld World 64:1409–1416

    Article  Google Scholar 

  32. Smismans T, Chernovol N, Lauwers B, Van Rymenant P, Talemi R (2021) Influence of post-heat treatments on fatigue response of low-alloyed carbon-manganese steel material manufactured by direct energy deposition-arc technique. Mater Lett 302:130465

    Article  Google Scholar 

  33. Ermakova A, Mehmanparast A, Ganguly S, Razavi J, Berto F (2021) Fatigue crack growth behaviour of wire and arc additively manufactured ER70S-6 low carbon steel components. Int J Fract

  34. Henckell P, Gierth M, Ali Y, Reimann J, Bergmann JP (2020) Reduction of energy input in wire arc additive manufacturing (WAAM) with gas metal arc welding (GMAW). Materials (Basel) 13

  35. Le VT, Paris H (2021) On the use of gas-metal-arc-welding additive manufacturing for repurposing of low-carbon steel components: microstructures and mechanical properties. Weld World 65:157–166

    Article  Google Scholar 

  36. Haden CV, Zeng G, Carter FM, Ruhl C, Krick BA, Harlow DG (2017) Wire and arc additive manufactured steel: tensile and wear properties. Addit Manuf 16:115–123

    Google Scholar 

  37. Prado-Cerqueira JL, Camacho AM, Diéguez JL, Rodríguez-Prieto Á, Aragón AM, Lorenzo-Martín C, Yanguas-Gil Á (2018) Analysis of favorable process conditions for the manufacturing of thin-wall pieces of mild steel obtained by wire and arc additive manufacturing (WAAM). Materials (Basel) 11

  38. Sridharan N, Noakes MW, Nycz A, Love LJ, Dehoff RR, Babu SS (2018) On the toughness scatter in low alloy C-Mn steel samples fabricated using wire arc additive manufacturing. Mater Sci Eng A 713:18–27

    Article  Google Scholar 

  39. Shassere B, Nycz A, Noakes MW, Masuo C, Sridharan N (2019) Correlation of microstructure and mechanical properties of metal big area additive manufacturing. Appl Sci 9

  40. Ghaffari M, VahediNemani A, Rafieazad M, Nasiri A (2019) Effect of solidification defects and HAZ softening on the anisotropic mechanical properties of a wire arc additive-manufactured low-carbon low-alloy steel Part. Jom 71:4215–4224

    Article  Google Scholar 

  41. Liu W, Jia C, Guo M, Gao J, Wu C (2019) Compulsively constricted WAAM with arc plasma and droplets ejected from a narrow space. Addit Manuf 27:109–117

    Google Scholar 

  42. Nagasai BP, Malarvizhi S, Balasubramanian V (2022) Effect of welding processes on mechanical and metallurgical characteristics of carbon steel cylindrical components made by wire arc additive manufacturing (WAAM) technique. CIRP J Manuf Sci Technol 36:100–116

    Article  Google Scholar 

  43. Teixeira FR, Scotti FM, Vilarinho LO, da Mota CAM, Scotti A (2022) Transferability of the working envelope approach for parameter selection and optimization in thin wall WAAM. Int J Adv Manuf Technol 119:969–989

    Article  Google Scholar 

  44. Tripathi U, Saini N, Mulik RS, Mahapatra MM (2022) Effect of build direction on the microstructure evolution and their mechanical properties using GTAW based wire arc additive manufacturing. CIRP J Manuf Sci Technol 37:103–109

    Article  Google Scholar 

  45. Huang C, Kyvelou P, Zhang R, Britton TB, Gardner L (2022) Mechanical testing and microstructural analysis of wire arc additively manufactured steels. Mater Design 216

  46. ISO 5178:2019. Destructive tests on welds in metallic materials — longitudinal tensile test on weld metal in fusion welded joints

  47. ISO 6892–1:2019. Metallic materials — tensile testing — Part 1: Method of test at room temperature

  48. ISO 9016:2022. Destructive tests on welds in metallic materials — impact tests — test specimen location, notch orientation and examination

  49. ISO 148–1:2016. Metallic materials — Charpy pendulum impact test — Part 1: Test method

  50. ISO 3785:2006. Metallic materials — designation of test specimen axes in relation to product texture

Download references

Acknowledgements

The presented results were achieved during the WAAMMEC project: “Wire + Arc Additive Manufacturing (WAAM): Weldability and Mechanical Properties for Structural Components.”

Funding

This project is funded by FOD Economie under the Grant Agreement CNN / NBN / PN20A07.

Author information

Authors and Affiliations

  1. Belgian Welding Institute, 9050, Ghent, Belgium

    Rafael Nunes, Nelis Vandermeiren & Wim Verlinde

  2. Department of Electromechanical, Systems and Material Engineering, Ghent University, 9050, Ghent, Belgium

    Dibakor Boruah, Robin Motte & Wim De Waele

Authors
  1. Rafael Nunes
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Nelis Vandermeiren
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Wim Verlinde
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Dibakor Boruah
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Robin Motte
    View author publications

    You can also search for this author in PubMed Google Scholar

  6. Wim De Waele
    View author publications

    You can also search for this author in PubMed Google Scholar

Contributions

Conceptualization: Rafael Nunes, Nelis Vandermeiren, Wim Verlinde, Dibakor Boruah, Robin Motte, Wim De Waele. Experiments: Rafael Nunes, Nelis Vandermeiren, Dibakor Boruah, Robin Motte. Analysis of research: Rafael Nunes, Nelis Vandermeiren, Wim Verlinde, Dibakor Boruah, Robin Motte, Wim De Waele. Writing—original draft preparation: Rafael Nunes, Dibakor Boruah. Review and editing: Rafael Nunes, Wim Verlinde, Dibakor Boruah, Wim De Waele. All authors read and approved the final manuscript.

Corresponding author

Correspondence to Rafael Nunes.

Ethics declarations

Conflict of interest

The authors declare no competing interests.

Additional information

Publisher's note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Nunes, R., Vandermeiren, N., Verlinde, W. et al. A benchmark of mechanical properties and operational parameters of different steel filler metals for wire arc additive manufacturing. Int J Adv Manuf Technol 127, 599–613 (2023). https://doi.org/10.1007/s00170-023-11520-z

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s00170-023-11520-z

Keywords

Search

Navigation