Abstract
Copper (II) ions (Cu2+) are one of the widely spread heavy metals in the environment causing ecological and human health risk. Among the conventional methods of Cu2+ removal, adsorption is observed as the most favorable. Biochar, a product of pyrolysis, has a relatively structured carbon matrix with high degree of porosity and extensive surface area, like activated carbon suggesting its suitability to be used as an adsorbent material. In this study, biochar was synthesized using an industrial type pyrolyzer and low-cost agricultural waste materials; saw dust and paddy husk as feedstocks. Six sets of biochar were made adhering to three temperature ranges: 350–450, 450–550 and 550–650 °C with a resident time of 30 min. Further, the effect of solution pH on the adsorption of Cu was tested. All the biochar materials exhibit similar trend of maximizing adsorptive removal at pH = 6. At lower pH values the surface charge of the biochar materials is positive creating unfavorable grounds for Cu2+ removal. As pH increases above 6.5, Cu2+ precipitates as Cu(OH)2 lowering the amount of soluble Cu2+ in the solution. Thus, the negative adsorptive removal efficiencies can be observed at the pH values above 6. The trend followed the shape of a maximum graph for almost all biochar materials where the removal maximizes at 450–550 °C pyrolysis temperature as lower temperatures favor more functional groups while the higher temperatures favor the development of higher specific surface area. At most pH values, the saw dust biochar shows higher removal percentage compared to the paddy husk biochar. Hence, a positive indication of Cu removal is present at lower pH values. The kinetics follow the pseudo-second order model suggesting that chemisorption is dominant. However, isotherms of adsorption, surface characterization of the materials, tests for leaching of adsorbed pollutants must be performed before field applications are done with the developed biochar materials.
This is a preview of subscription content, log in via an institution to check access.
Access this chapter
Tax calculation will be finalised at checkout
Purchases are for personal use only
References
Abd Hamid S, Azha SF, Sellaoui L, Bonilla-Petriciolet A, Ismail S (2020) Adsorption of copper (II) cation on polysulfone/zeolite blend sheet membrane: synthesis, characterization, experiments and adsorption modelling. Colloids Surf 601. https://doi.org/10.1016/j.colsurfa.2020.124980
Chen X, Chen G, Chen L, Chen Y, Lehmann J, Mcbride MB, Hay AG (2011) Adsorption of copper and zinc by biochars produced from pyrolysis of hardwood and corn straw in aqueous solution. Bioresour Technol 102:8877–8884
Dai Y, Zhang N, Xing C, Cui Q, Sun Q (2019) The adsorption, regeneration and engineering applications of biochar for removal organic pollutants: a review. Chemosphere 223:12–27
Gong J-L, Wang X-Y, Zeng G-M, Chen L, Deng J-H, Zhang X-R, Niu Q-Y (2012) Copper (II) removal by pectin–iron oxide magnetic nanocomposite adsorbent. Chem Eng J 185–186:100–107
Hegazi HA (2019) Removal of heavy metals from wastewater using agricultural and industrial wastes as adsorbents. HBRC J 9:276–282
Inyang MI, Gao B, Yao Y, Xue Y, Zimmerman A, Mosa A, Pullammanappallil P, Ok YS, Cao X (2015) A review of biochar as a low-cost adsorbent for aqueous heavy metal removal. Crit Rev Environ Sci Technol 46:406–433
Kołodyńska D, Wnętrzak R, Leahy JJ, Hayes MHB, Kwapiński W, Hubicki Z (2012) Kinetic and adsorptive characterization of biochar in metal ions removal. Chem Eng J 197:295–305
Li H, Dong X, Da Silva EB, De Oliveira LM, Chen Y, Ma LQ (2017) Mechanisms of metal sorption by biochars: biochar characteristics and modifications. Chemosphere 178:466–478
Li Y, Zhou Q, Ren B, Luo J, Yuan J, Ding X, Bian H, Yao X (2020) Trends and health risks of dissolved heavy metal pollution in global river and lake water from 1970 to 2017. Rev Environ Contam Toxicol 251:1–24
Mohan D, Pittman CU Jr, Bricka M, Smith F, Yancey B, Mohammad J, Steele PH, Alexandre-Franco MF, Gomez-Serrano V, Gong H (2007) Sorption of arsenic, cadmium, and lead by chars produced from fast pyrolysis of wood and bark during bio-oil production. J Colloid Interface Sci 310:57–73
Mullaney J, Lucke T (2014) Practical review of pervious pavement designs. CLEAN Soil, Air, Water 42:111–124
Muthu M, Santhanam M, Kumar M (2018) Pb removal in pervious concrete filter: effects of accelerated carbonation and hydraulic retention time. Constr Build Mater 174:224–232
Pellera FM, Giannis A, Kalderis D, Anastasiadou K, Stegmann R, Wang JY, Gidarakos E (2012) Adsorption of Cu(II) ions from aqueous solutions on biochars prepared from agricultural by-products. J Environ Manage 96:35–42
Perera KKCK, Rathnasiri PG, Senarath SAS, Sugathapala AGT, Bhattacharya SC (2005) Assessment of sustainable energy potential of non-plantation biomass resources in Sri Lanka. Biomass Bioenerg 29:199–213
Shen Z, Zhang Y, Jin F, Mcmillan O, Al-Tabbaa A (2017) Qualitative and quantitative characterisation of adsorption mechanisms of lead on four biochars. Sci Total Environ 609:1401–1410
Štefelová J, Zelenka T, Slovák V (2017) Biosorption (removing) of Cd(II), Cu(II) and methylene blue using biochar produced by different pyrolysis conditions of beech and spruce sawdust. Wood Sci Technol 51:1321–1338
Stets EG, Sprague LA, Oelsner GP, Johnson HM, Murphy JC, Ryberg K, Vecchia AV, Zuellig RE, Falcone JA, Riskin ML (2020) Landscape Drivers of Dynamic Change in Water Quality of U.S. Rivers. Environ Sci Technol 54:4336–4343
Tan X, Liu Y, Zeng G, Wang X, Hu X, Gu Y, Yang Z (2015) Application of biochar for the removal of pollutants from aqueous solutions. Chemosphere 125:70–85
Tripathi M, Sahu JN, Ganesan P (2016) Effect of process parameters on production of biochar from biomass waste through pyrolysis: a review. Renew Sustain Energy Rev 55:467–481
Zhang C, Liu L, Zhao M, Rong H, Xu Y (2018) The environmental characteristics and applications of biochar. Environ Sci Pollut Res Int 25:21525–21534
Acknowledgements
Authors would like to acknowledge the NORAD WaSo-Asia Project for the financial support given to conduct this research.
Author information
Authors and Affiliations
Corresponding author
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 2022 The Author(s), under exclusive license to Springer Nature Singapore Pte Ltd.
About this paper
Cite this paper
Wijeyawardana, H.M.P., Pramanik, B., Karunarathna, A.K., Gunasekara, C., Law, D., Nanayakkara, K.G.N. (2022). Variation of Copper Adsorption with Initial pH and Pyrolysis Temperature by Saw Dust and Paddy Husk Biochar Made in an Industrial Type Pyrolizer. In: Dissanayake, R., Mendis, P., Weerasekera, K., De Silva, S., Fernando, S. (eds) ICSBE 2020. Lecture Notes in Civil Engineering, vol 174. Springer, Singapore. https://doi.org/10.1007/978-981-16-4412-2_50
Download citation
DOI: https://doi.org/10.1007/978-981-16-4412-2_50
Published:
Publisher Name: Springer, Singapore
Print ISBN: 978-981-16-4411-5
Online ISBN: 978-981-16-4412-2
eBook Packages: EngineeringEngineering (R0)