Drop-weight impact test and small-mass impact test were carried out on composite laminates. The contact force and AE signal were measured during the tests, and the correspondence between AE signals and damage were analyzed respectively. For the drop-weight impact test, the contact force dropped and the frequency of the AE signal increased suddenly when the delamination appeared. Then the AE signal was decomposed using empirical mode decomposition (EMD). The amplitude anomaly were found in the first several intrinsic mode functions (IMFs), which could be used as a signal to characterize damage.; In the small-mass impact test, the contact force and AE signal were investigated in the same way. Additionally, Fourier transform (FFT) was used to find whether there is delamination. Results reveal that when laminates suffers the drop-weight impact, AE signals, combined with EMD, can be used for real-time health monitoring, For the plates impacted by small-mass objects, AE signal, EMD and Fourier transform can be used to determine whether there is delamination in the laminate.
Access this chapter
Tax calculation will be finalised at checkout
Purchases are for personal use only
References
Olsson, R. (2000). Mass criterion for wave controlled impact response of composite plates [J]. Composites: Part A, 31(8), 879–887.
Zheng, D., & Binienda, W. K. (2007). Effect of permanent indentation on the delamination threshold for small mass impact on plates [J]. International Journal of Solids and Structures, 44, 8143–8158.
Wenxun, Y., Zhefeng, Y., Baojun, N., et al. (2017). Contact force measurement and response to damage of composite laminates subjected to small-mass impact [J]. Science Technology and Engineering, 17(24), 13–19.
Mahdian, A., Yousefi, J., Nazmdar, M., et al. (2016) Damage evaluation of laminated composites under low-velocity impact tests using acoustic emission method [J]. Journal of Composite Materials, 51(4).
Hao, C., Xiaoyan, T., Leijang, Y., et. al. (2010). Acoustic emission characteristics of composite laminates under low velocity impact[J]. Mechanical Science and Technology for Aerospace Engineering, 29(11), 1557–1560.
Mal, A. K., Shih, F., Banerjee, S. (2003). Acoustic emission waveforms in composite laminates under low velocity impact [J]. Proc Spie, 5047.
Johnson, M., Gudmundson, P., Johnson, M., et al. (2001). Experimental and theoretical characterization of acoustic emission transients in composite laminates [J]. Composites Science & Technology, 61(10), 1367–1378.
Fu, T., Liu, Y., Li, Q., et al. (2009). Fiber optic acoustic emission sensor and its applications in the structural health monitoring of CFRP materials[J]. Optics and Lasers in Engineering, 47(10), 1056–1062.
MartÃnez-Jequier, J. (2015). Real-time damage mechanisms assessment in CFRP samples via acoustic emission Lamb wave modal analysis [J]. Composites Part B, 68(4), 317–326.
Selman, E., Ghiami, A., & Alver, N. (2015). Study of fracture evolution in FRP-strengthened reinforced concrete beam under cyclic load by acoustic emission technique: An integrated mechanical-acoustic energy approach [J]. Construction and Building Materials, 95, 832–841.
Mccrory, J. P., Al-Jumaili, S. K., Crivelli, D., et al. (2015). Damage classification in carbon fibre composites using acoustic emission: A comparison of three techniques[J]. Composites Part B Engineering, 68(5), 424–430.
Yang, Y., Sun, X., Yang, S., et al. (2012). Experimental study on compressive failure mechanism of low-velocity-impact-damaged composite aminates[J]. Acta Materiae Compositae Sinica, 29(3):197–202.
Zhang, D.L., Xu, D.G., wang, Y. (2000). Demarcation in space domain for local flaw signals of wire ropes and feature extraction in frequency domain based on wavelet transform [J].ACTA ELECTRONICA SINICA, (07), 59–62.
Sun, L. Y., Li,Y. B., Qu, Z. G., et al. (2007). Study on acoustic emission detection for pipeline leakage based on EMD signal analysis method [J]. Journal of Vibration and Shock, 26(10), 161–164.
Lifeng, Z., Xiaoliang, Z., & Jie, S. (2003). Application of EMD and wavelet transform to the detection of signal singularity [J]. Journal of Ocean University of Qingdao, 33(5), 759–763.
Huang, N. E., et al. (1998). The empirical mode decomposition and the Hilbert spectrum for nonlinear and non-stationary time series analysis. In Proceedings of the Royal Society Lond. A, 44, p 903–995.
Shi, Y., Jin-yang, Z., Xia-mei, L. U., et al. (2014) Low-velocity impact response of 3D braided composites by acoustic emission[J]. Journal of Materials Engineering, (7), 92–97.
Author information
Authors and Affiliations
Corresponding author
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 2019 Springer Nature Singapore Pte Ltd.
About this paper
Cite this paper
You, Q., Yu, Z., Fang, J. (2019). Detection of Acoustic Emission Signal Due to Impact Damage of Composite Materials Based EMD. In: Jing, Z. (eds) Proceedings of International Conference on Aerospace System Science and Engineering 2018. ICASSE 2018. Lecture Notes in Electrical Engineering, vol 549. Springer, Singapore. https://doi.org/10.1007/978-981-13-6061-9_9
Download citation
DOI: https://doi.org/10.1007/978-981-13-6061-9_9
Published:
Publisher Name: Springer, Singapore
Print ISBN: 978-981-13-6060-2
Online ISBN: 978-981-13-6061-9
eBook Packages: EngineeringEngineering (R0)