Abstract
This is a method developed by RILEM in the light of the results of an international trial. This trial showed that the method can reliably differentiate reactive and non-reactive combinations for a range of aggregate compositions from around the world.
Access this chapter
Tax calculation will be finalised at checkout
Purchases are for personal use only
Similar content being viewed by others
References
Lindgård, J, Nixon, P J, Borchers, I, Schouenborg, B, Wigum, B J, Haugen M, Åkesson, U, The EU Partner project – European standard tests to prevent alkali reactions in aggregates, Cement and Concrete Research, 40 (2010) 611–635.
LCPC, Recommendations for the prevention of damage by the alkali-aggregate reaction, Paris, France, 1994.
AFNOR NF P 18–454, Reactivity of a concrete formula with regard to the alkali-aggregate reaction, Association Française de Normalisation, Paris, France, December 2004.
AFNOR NF P 18-456, Reactivity of a concrete formula with regard to the alkali-aggregate reaction - Criteria for interpretation of the performance test results, Association Française de Normalisation, Paris, France November 2004.
ASTM C136-06, Standard test method for the sieve analysis of coarse and fine aggregates.
EN 480-1:2014, Admixtures for concrete, mortar and grout. Test methods. Reference concrete and reference mortar for testing.
EN 12390-2:2009, Testing hardened concrete. Making and curing specimens for strength tests.
ASTM C192/C192 M-07, Standard practice for making concrete test specimens in the laboratory.
EN 197-1:2011, Cement. Composition, specifications and conformity criteria for common cements.
ASTM C150-07, Standard specification for Portland cement.
EN 12620:2013, Aggregates for concrete.
ASTM C33/C33 M-08, Standard specification for concrete aggregates.
EN 1097-6:2013, Tests for mechanical and physical properties of aggregates. Determination of particle density and water absorption.
ASTM C127-04, Standard test method for density, relative density (specific gravity), and absorption of coarse aggregate.
ISO 7033:1987 (R08), Fine and coarse aggregates for concrete - Determination of the particle mass-per-volume and water absorption - Pycnometer method.
ASTM C128-07, Standard test method for density, relative density (specific gravity), and absorption of fine aggregate.
EN 1097-5:2008, Tests for mechanical and physical properties of aggregates. Determination of water content by drying in a ventilated oven.
ASTM C566-97(2004), Standard test method for total evaporable moisture content of aggregate by drying.
EN 12350-7:2009, Testing fresh concrete. Air content. Pressure methods.
ASTM C1170-06, Standard test method for determining consistency and density of roller compacted concrete using a vibrating table.
EN 12350-6: 2009, Testing fresh concrete. Density.
ASTM C173-01, Standard test method for air content of freshly mixed concrete by the volumetric method.
ASTM C231-04, Standard test method for air content of freshly mixed concrete by the pressure method.
Author information
Authors and Affiliations
Consortia
Corresponding author
Editor information
Editors and Affiliations
Annex A—Additional Information
Annex A—Additional Information
(Comments relate to clauses as numbered in the method)
1.1 A4.8 Casting and Measurement Environment
Cooling to a standard temperature is necessary to obtain reproducible results. In countries with hot climates, however, it may occasionally be necessary to allow the casting and measurement to be carried out in a room maintained at a temperature higher than the preferred 20 °C, up to a maximum of 27 ± 2 °C and not less that 65 ± 5 % RH.
Note A16: A controlled temperature of 20 °C is preferred and strongly recommended for this stage of the test. Whatever standard temperature might be adopted (20 °C or another value up to 27 °C) for a particular test, it is essential that the same procedure and the same temperature are used consistently throughout the test. However, use of a temperature other than 20 °C will necessitate reconsideration of the expansion limits.
1.2 A5.2 Calculation of Sodium Hydroxide to Be Added to the Mixing Water
Example calculation to determine the amount of sodium hydroxide (NaOH) to be added to the mixing water to increase the alkali content up to 1.25 % sodium oxide equivalent by mass of cement:
1.3 A5.3 Aggregate—Standard Aggregate Materials Test
The aggregate fractions should be combined in mass proportions calculated on a saturated surface dry basis according to Table A.1 given below, which gives the recommended aggregate grading curve range to achieve a matrix suited for production of workable and stable concrete. In order to meet these requirements, it is necessary to know the particle size distribution curve of each aggregate.
Note A17: Gaps between two fractions should be avoided. For example, sand 0/2 (2–0 mm) should not be tested with an aggregate 8/16 (16–8 mm).
Note A18: With some reactive aggregates it has been found that there is a proportion of reactive constituents in the aggregate that leads to a maximum expansion. This proportion is called the ‘pessimum’ content, and the relationship between expansion and content of reactive constituents is called the ‘pessimum behaviour’ of the reactive aggregate.
1.4 A6 Concrete Mix Design
Preparation of the aggregates
Pre-wetted fine aggregates are used in order to ensure a workable and homogeneous concrete. This shall be done using the following procedure:
Determine the water absorption (WAf) and initial water content (Wi) of the fine aggregate according to the standards/methods valid in the place of use. Weigh out a sufficient quantity of the fine aggregate, place it into a tray and add a sufficient amount of water calculated to achieve a water content of 5 ± 2 %. Mix the wetted fine aggregate thoroughly and store in sealed containers for at least 16 h. Measure the final water content (Wf) of the fine aggregate.
The coarse aggregate should be used without pre-wetting, but the water absorption (WAc) and the water content (Wc) should be measured.
The amount of water added to the mix to achieve the prescribed free water content of 220 kg/m3 is then calculated, taking into account both the water absorption and the measured water content of the fine and coarse aggregates. The water absorptions of most fine aggregates will be less than the intended water content (i.e. 5 ± 2 %). For most coarse aggregates, the water content will be lower than their water absorptions. In the cases where the water content (W) is higher than the water absorption (WA), the contribution from the aggregate (Wfree) to the free water content of the mix can be calculated as:
or
In the case of where the water absorption of the aggregate is higher than its water content, the extra water needed (Wextra) at the mixing stage, to bring the aggregate to a saturated surface dry state, can be calculated as:
or
Concrete Mix Design
A worked example is presented below, see Tables A.2, A.3, A.4, A.5 and A.6.
Example of concrete mix design calculation made with one coarse and one fine aggregate is shown (the calculation is the same for more aggregates).
For the mix design it is necessary to know:
-
The water absorption (WA) of each aggregate. The values can be determined according to EN 1097-6 [13], ASTM C127 [14] or ISO 7033 [15];
-
The densities on an oven dry (ρrd) and saturated surface dry (ρssd) basis of all fractions. The values can be determined according to EN 1097-6 [13], ASTM C127 [14] and 128 [16] or ISO 7033 [15];
-
The water content (W) of each aggregate. The values can be determined according to EN 1097-5 [17] or ASTM C566 [18].
Assume that the content of superplasticizer (with density 1.1 kg/m3 and water content 80 %) required is 2.0 kg/m3 and that the amount of technical grade NaOH (with density 2.1 kg/m3) required is 1.4 kg/m3—see example in Annex A5.2.
The volumetric weight and the air content of the fresh concrete should be measured, according respectively to EN 12350-7 [19]/ASTM C1170 [20] and EN 12350-6 [21]/ASTM C173 [22]/ASTM C231 [23]. The ratio between the theoretical and the measured volumetric weights of the fresh concrete should be 1.000 ± 0.015 (which corresponds to 440 ± 6 kg of cement). This will ensure the correct amount of alkali from the cement in the fresh concrete.
Calculation of the quantity (X) of coarse aggregate (saturated surface dry) in 1 m3 of concrete:
Calculation of the quantity (4/6 × X) of fine aggregate (saturated surface dry) in 1 m3 of concrete:
\( 4/ 6 { } \times {\text{ X }} = { 4}/ 6 { } \times {\text{ 995 kg}}/{\text{m}}^{ 3} = {\text{ 663 kg}}/{\text{m}}^{ 3} \)
The contribution from the fine aggregate (Wfree-f) to the free water content can be calculated according to Eq. A.1:
The extra water needed (Wextra-c) at the mixing stage to bring the coarse aggregate to a saturated surface dry state can be calculated according to Eq. A.2:
Example of fresh concrete properties measured:
Slump = 120 mm (target is 100–180 mm)
Air content = 1.4 % (target <3 %)
Measured volumetric weight = 2327 kg/m3
Ratio between the theoretical and measured volumetric weights = (2320/2327) = 0.997 (target is 0.985–1.015).
If the ratio is outside the range, the quantity of aggregate should be increased/decreased (without changing the proportion between the different aggregates) in order to meet the requirement of the weight ratio (0.985–1.015).
Rights and permissions
Copyright information
© 2016 RILEM
About this chapter
Cite this chapter
On behalf of the membership of RILEM TC 219-ACS., Nixon, P.J., Sims, I. (2016). RILEM Recommended Test Method: AAR-4.1—Detection of Potential Alkali-Reactivity—60 °C Test Method for Aggregate Combinations Using Concrete Prisms. In: Nixon, P., Sims, I. (eds) RILEM Recommendations for the Prevention of Damage by Alkali-Aggregate Reactions in New Concrete Structures. RILEM State-of-the-Art Reports, vol 17. Springer, Dordrecht. https://doi.org/10.1007/978-94-017-7252-5_6
Download citation
DOI: https://doi.org/10.1007/978-94-017-7252-5_6
Published:
Publisher Name: Springer, Dordrecht
Print ISBN: 978-94-017-7251-8
Online ISBN: 978-94-017-7252-5
eBook Packages: EngineeringEngineering (R0)