Abstract
In order to maximize the use of copper slag, a new idea that copper slag is reduced to smelt copper-containing antimicrobial stainless steel was proposed. But copper-iron reduced from copper slag contains a large number of copper matte, making sulfur content high. In this article, desulfurization of copper-iron was studied. The Fact-Sage software was used to calculate ΔG of the desulfurization reaction. Calcium oxide, calcium carbide and ferromanganese were used as desulfurization agent. The results show that desulfurization capacity of calcium oxide is poor, but with addition of carbon, desulfurization effect of calcium oxide will be enhanced. Calcium carbide and ferromanganese have good desulfurization effect.
Access this chapter
Tax calculation will be finalised at checkout
Purchases are for personal use only
References
Cao H, Zhang L, Fu N et al (2009) Review of copper slag impoverishment. J Mater Metall 8:33–39
Gorai B, Jana RK, Premchand (2003) Characteristics and utilisation of copper slag—a review. Resour Conserv Recycl 39:299–313
Murari K, Siddique R, Jain KK (2015) Use of waste copper slag, a sustainable material. J Mater Cycles Waste Manage 17:13–26
Mostafa K, Ali B (2009) Mechanical properties of high-strength concrete incorporating copper slag as coarse aggregate. Constr Build Mater 23:2183–2188
Wei W, Zhang W, Ma G (2010) Optimum content of copper slag as a fine aggregate in high strength concrete. Mater Des 31:2878–2883
Shi C, Meyer A Behnood (2008) Utilization of copper slag in cement and concrete. Resour Conser Recycl 2008(52):1115–1120
Moskalyk RR, Alfantazi AM (2003) Review of copper pyrometallurgical practice: today and tomorrow. Miner Eng 2003(16):893–919
Zhang T, Niu L, Dou Z et al. (2014) A method molten iron reduced from copper slag directly smelt copper antimicrobial stainless steel. Chinese Patent, Patent No. CN 1041203510 A, 2014
Zhang B, Niu L, Zhang T et al (2017) Alternative reduction of copper matte in reduction process of copper slag. ISIJ Int 57:775–781
Lindstrom D, Sichen D (2015) Study on desulfurization abilities of some commonly used desulfurization agents. Steel Res Int 86:73–83
Hao X, Wang X, Wang W (2015) Study on desulfurization ability of CaO-Al2O3-SiO2 and CaO-CaF2 slags at 1600 degrees C. Steel Res Int 86:1455–1460
Wu Y (1996) elementary introduction of the thermodynamics and kinetics in the process of desulphurization. Steelmaking 2:44–52
Feng J, Zhao W, Ma G et al. (2009) Analysis of desulphurization of injection and stirring for hot metal pretreatment. Metall Equip, 32–35
Acknowledgements
This research was supported by the Basic Research Universities Special Fund Operations (N140204013, N130102002, N130702001); the Education Department of Liaoning Province (LZ2014021); National Natural Science Foundation of China (51374064).
Author information
Authors and Affiliations
Corresponding author
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 2018 The Minerals, Metals & Materials Society
About this paper
Cite this paper
Zhang, Bj., Zhang, Ta., Niu, Lp., Dou, Zh., Li, Zq., Zhang, Dl. (2018). Desulfurization of Copper-Iron Reduced from Copper Slag. In: Lambotte, G., Lee, J., Allanore, A., Wagstaff, S. (eds) Materials Processing Fundamentals 2018. TMS 2018. The Minerals, Metals & Materials Series. Springer, Cham. https://doi.org/10.1007/978-3-319-72131-6_2
Download citation
DOI: https://doi.org/10.1007/978-3-319-72131-6_2
Published:
Publisher Name: Springer, Cham
Print ISBN: 978-3-319-72130-9
Online ISBN: 978-3-319-72131-6
eBook Packages: Chemistry and Materials ScienceChemistry and Material Science (R0)