Graphite cathode materials used in aluminum reduction cells are of porous structure. During aluminum electrolysis, the melt and sodium will penetrate into the cathode block leading to its expansion and deterioration. This work is aimed to give a better understanding of the relationship between the pore structure and the sodium expansion and to improve control of the cathode quality through quantitative image analysis.
Experiments with graphite cathode materials were carried out using a modified Rapoport apparatus. Image analysis results indicate that the porosity, pore diameter and pore connectivity after electrolysis can be related to the sodium expansion, while the aspect ratio and the fractal dimension seem to be unchanged. X-ray Diffraction (XRD) measurement for interlayer spacing (d 002) was also found to correlate to the degree of such expansion. Quantitative information on the correlation between the sodium expansion and porous structures can serve both the cathode producer and the smelter for product selection and performance evaluation of cathode blocks.
This is a preview of subscription content, log in via an institution to check access.
Access this chapter
Tax calculation will be finalised at checkout
Purchases are for personal use only
Preview
Unable to display preview. Download preview PDF.
References
M. Sorlie and H. A. Øye, Cathodes in Aluminium Electrolysis (Aluminium-Verlag), 1994, 127–132.
L. P. Lossius and H. A. Øye, “Melt Penetration and Chemical Reactions in 16 Industrial Aluminum Carbon Cathodes,” Metallurgical and Materials Transactions B, 31B (12) (2000), 1213–1224.
D. S. Newman et al, “A Technique for Measuring In Situ Cathode Expansion (Rapoport Test) during Aluminum Electrolysis,” Light Metals 1986, 1986, 685–688.
A. Zolochevsky et al, “Creep and Sodium Expansion in a Semigraphitic Cathode Carbonn,” Light Metals 2003, 2003, 602.
J. G. Hop, “Sodium Expansion and Creep of Cathode Carbon,” (Ph.D. thesis, Norwegian University of Science and Technology, 2003), 90–103.
J. M. Peyneau and J. R. Gaspard, “Laboratory Testing of the Expansion under Pressure due to Sodium Intercalation in Carbon Cathode Materials for Aluminium Smelters,” Light Metals 1992, 1992, 801–808.
A. Zolochevsky et al, “Rapoport-Samoilenko Test for Cathode Carbon Materials I. Experimental Results and Constitutive Modeling,” Carbon, 41 (2003), 497–505.
J. Xue, Q. Liu and W. Ou, “Sodium Expansion in Carbon /TiB2 Cathodes during Aluminum Electrolysis,” Light Metals 2007, 2007, 1061–1066.
S. Rorvik, H. A. Øye and M. Sorlie, “Characterization of Porosity in Cokes by Image Analysis,” Light Metals 2001, 2001, 601–609.
S. Rorvik, A. P. Ratvik and T. Foosnas, “Characterization of Green Anode Materials by Image Analysis,” Light Metals 2006, 2006, 553–558.
J. G. Hop and H. A. Øye, “In-Situ Strength Reduction of Anthracitic Cathode Carbon and Crack Quantifying by the Use of Image Analysis,” Light Metals 2001, 2011, 717–722.
Y. Gao et al, “Characterization of Sodium and Fluoride Penetration into Carbon Cathodes by Image Analysis and SEM-EDS Techniques,” Light Metals 2011, 2011, 1103–1107.
X. Li et al, “Analysis of Porous Structures of Graphitic Cathode Materials and the Correlation to Penetrated Sodium,” Light Metals 2012, 2012, 1319–1324.
M. B. Rapoport and V. N. Samoilenko, “Deformation of Cathode Blocks in Aluminium Baths during Process of Electrolysis,” Tsvet Met, 30 (2) (1957), 44–51.
J. Thonstad and S. Rolseth, “On the Cathodic Overvoltage on Aluminium in NaF - AlF3 - Al2O3 Melts - II,” Electrochimica Acta, 23 (1978), 233–241.
Author information
Authors and Affiliations
Editor information
Rights and permissions
Copyright information
© 2016 The Minerals, Metals & Materials Society
About this chapter
Cite this chapter
Li, X., Xue, J., Chen, T. (2016). Characterization of Porous Structure and its Correlation to Sodium Expansion of Graphite Cathode Materials Using Image Analysis. In: Sadler, B.A. (eds) Light Metals 2013. The Minerals, Metals & Materials Series. Springer, Cham. https://doi.org/10.1007/978-3-319-65136-1_213
Download citation
DOI: https://doi.org/10.1007/978-3-319-65136-1_213
Publisher Name: Springer, Cham
Print ISBN: 978-3-319-65135-4
Online ISBN: 978-3-319-65136-1
eBook Packages: Chemistry and Materials ScienceChemistry and Material Science (R0)