Abstract
Twin-roll cast (TRC) AZ31 alloy (Mg-3wt.%Al-1wt.%Zn) was subjected to heat treatment at 420 °C. As a result, the intensity of the original basal texture was reduced considerably. Crystallographic orientation analysis revealed that such a change in the texture is due to particle-stimulated nucleation of new grains with random orientations. The tensile test results indicate that annealing slightly increases ultimate tensile strength (UTS), however, dramatically improves the elongation.
This is a preview of subscription content, log in via an institution to check access.
Access this chapter
Tax calculation will be finalised at checkout
Purchases are for personal use only
Preview
Unable to display preview. Download preview PDF.
References
I. H. Jung, W. Bang, I. J. Kim, H. I. Sung, W. J. Park, D. Choo, S. Ahn, Magnesium Technology, R. Beals, A. Luo, N.R. Neelameggham, M.O. Pekguleryuz, Eds, TMS, Warrendale, PA, 2007, pp. 85–88.
C. Yang, P. Ding, D. Zhang, F. Pan, Mater. Sci. Forum, 2005, pp. 427–430.
H. Watari, T. Haga, N. Koga, K. Davey, J. Mater. Process. Technol., 2007, 192–193, pp. 300–305..
A. Jager, P. Lukac, V. Gartnerova, J. Haloda, M. Dopita, Mat. Sci. Eng. A, 2006, 432, pp. 20–25.
F. B. Kaiser, D. Letzig, K. U. Kainer, A. Sfyczynski, C. Hartig, Adv.Eng. Mater., 2003. 5(12): pp. 891–896.
M. R. Barnett, M. D. Navea, C. J. Bettlesb, Mater. Sci. Eng. A, 2004, 386, pp. 205–211.
A. S. Khan, A. Pandey, T. Gnäupel-Herold, R. K. Mishra, Int. J. Plast. 2011, 27 (5), pp.688–706
F. J. Humphreys, M. Hatherly, 2 ed. 2004: Great Britain by Galliard Ltd., UK.
R. K. Mishra, A. K. Gupta, P. R. Rao, A. K. Sachdev, A. M. Kumar and A. A. Luo, Script. Mater., 2008, 59(5), pp. 562–565.
J. Bohlen, M. R. Nurnberg, J. W. Senn, D. Letzig, S. R. Agnew, Acta Mater., 2007, 55(6), pp.2101–2112.
N. Stanford, M. Barnett, Script. Mater., 2008. 58(3), pp. 179–182.
L. W. F. Mackenzie, M. O. Pekguleryuz, Script. Mater., 2008, 59(6), pp. 665–668.
M. Masoumi, M. Hoseini, M. Pekguleryuz, Mater. Sci. & Eng. A, 528(7–8) (2011) 122–3129.
L.W.F. Mackenzie, M. Pekguleryuz, Mat. Sci. Eng A, vol. 480(1–2), 2008, pp. 189–197.
M. Masoumi, M. Pekguleryuz, Mater. Sci. and Eng. A, vol. 529, 2011, pp. 207–214.
G.F. Vander Voort, Editor, Metallography and Microstructures, vol. 9 ASM International, Materials Park, OH (2004).
P. Cao, D.H. StJohn and M. Qian. Mater. Sci. Forum, 488–489 (2005), pp. 139–142.
R. E. Reed-Hill, R. Abbaschian, Third ed., 20 Park Plaza, Boston, MA: PWS.
Author information
Authors and Affiliations
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 2014 TMS (The Minerals, Metals & Materials Society)
About this chapter
Cite this chapter
Masoumi, M., Zarandi, F., Pekguleryuz, M.O. (2014). Effect of Annealing on Microstructure, Texture and Tensile Properties of Twin-Roll Cast AZ31B. In: Alderman, M., Manuel, M.V., Hort, N., Neelameggham, N.R. (eds) Magnesium Technology 2014. Springer, Cham. https://doi.org/10.1007/978-3-319-48231-6_46
Download citation
DOI: https://doi.org/10.1007/978-3-319-48231-6_46
Publisher Name: Springer, Cham
Print ISBN: 978-3-319-48589-8
Online ISBN: 978-3-319-48231-6
eBook Packages: Chemistry and Materials ScienceChemistry and Material Science (R0)