Pyramidal I <c+a> slip ({10–11}<11–23>) was observed to be the dominant slip mode in magnesium single crystals compressed quasi-statically along c-axis at room temperature. Transmission electron microscopy (TEM) observations revealed the <c+a> dislocation character and structure: some <c+a> dislocations are long, straight and aligned with the basal plane, while others are curved and are not contained within the basal plane.
Access this chapter
Tax calculation will be finalised at checkout
Purchases are for personal use only
References
T. Obara, H. Yoshinga, and S. Morozumi, Acta Metallurgica 21, 845 (1973).
C. M. Byer, B. Li, B. Cao, and K. Ramesh, Scripta Materialia 62, 536 (2010).
C. M. Byer and K. Ramesh, Acta Materialia 61, 3808 (2013).
B. Syed, J. Geng, R. Mishra, and K. Kumar, Scripta Materialia 67, 700 (2012).
E. Lilleodden, Scripta Materialia 62, 532 (2010).
S. Sandlöbes, S. Zaefferer, I. Schestakow, S. Yi, and R. Gonzalez-Martinez, Acta Mater. 59, 429 (2011).
N. Dixit, K. Y. Xie, K. J. Hemker, and K. Ramesh, Acta Materialia 87, 56 (2015).
H. Fan and J. A. El-Awady, Materials Science and Engineering: A 644, 318 (2015).
K. Y. Xie, Z. Alam, A. Caffee, and K. J. Hemker, Scripta Materialia (accepted) (2015).
T. Nogaret, W. A. Curtin, J. A. Yasi, L. G. Hector, and D. R. Trinkle, Acta Mater. 58, 4332 (2010).
Y. Tang and J. A. El-Awady, Acta Mater. 71, 319 (2014).
T. J. Balk, K. J. Hemker, and L. P. Kubin, Scripta Materialia 56, 389 (2007).
H. Yoshinaga and R. Horiuchi, Trans. JIM 4, 1 (1963).
H. Yoshinaga and R. Horiuchï, Transactions of the Japan Institute of Metals 5, 14 (1963).
T. Nogaret, W. Curtin, J. Yasi, L. Hector, and D. Trinkle, Acta Materialia 58, 4332 (2010).
J. Geng, M. F. Chisholm, R. Mishra, and K. Kumar, Philosophical Magazine Letters 94, 377 (2014).
Author information
Authors and Affiliations
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 2016 TMS (The Minerals, Metals & Materials Society)
About this chapter
Cite this chapter
Xie, K.Y., Alam, Z., Caffee, A., Hemker, K.J. (2016). Deformation behavior of Mg single crystals compressed along c-axis. In: Singh, A., Solanki, K., Manuel, M.V., Neelameggham, N.R. (eds) Magnesium Technology 2016. Springer, Cham. https://doi.org/10.1007/978-3-319-48114-2_42
Download citation
DOI: https://doi.org/10.1007/978-3-319-48114-2_42
Publisher Name: Springer, Cham
Print ISBN: 978-3-319-48620-8
Online ISBN: 978-3-319-48114-2
eBook Packages: Chemistry and Materials ScienceChemistry and Material Science (R0)