Abstract
Around 20% of powders are scattered as waste outside the deposition chamber during spray forming of AA7055. To recycle these valuable powders, a recovery and a hot deformation processing routes are developed. Firstly, strict screening of powder is established in which the chemical compositions and microstructure are measured. Cold isostatic pressing followed by hot extrusion and T76 or T6 heat treatment is developed to compact the powders into a solid bar shape which could be used as billets. The hyperbolic sinusoidal constitutive equation is obtained using Gleeble hot compression test of the densified material. The analysis of mechanical properties shows the samples after T76 heat treatment possess slightly lower strength but enhanced toughness than that of sprayed samples. Thus, further deformation processing like forging is needed to improve compactness and mechanical properties of these billets.
Access this chapter
Tax calculation will be finalised at checkout
Purchases are for personal use only
References
Rometsch, P.A., Zhang, Y., Knight, S.: Heat treatment of 7xxx series aluminium alloys - some recent developments. Trans. Nonferrous Met. Soc. China 24, 2003–2017 (2014)
Srivatsan, T.S., Anand, S., Sriram, S., et al.: The high-cycle fatigue and fracture behav-iour of aluminium alloy 7055. Mater. Sci. Eng., A 281, 292–304 (2000)
Singer, A.R.E.: The principles of spray rolling of metals. Met. Mater. 31, 246–252 (1970)
Singer, A.R.E.: Recent developments in the spray forming of metals. Powder Metallurgy Powder Technol. 21, 219–234 (1985)
Li, X.: Study on Microstructure and Properties of 7055 Aluminium Alloy. Shanghai Jiao Tong University, Shanghai (2008)
Zhang, X.: Effect of rolling method on microstructure and mechanical properties of 7055aluminum alloy. In: Proceedings of the 2019 China Aluminum Processing Industry Annual Conference and China (Zouping) Aluminum Processing Industry Development Summit Forum, China Nonferrous Metal Processing Industry Association (2019)
Wen, J., Yu, G., Zhang, H., et al.: Effect of hot forging on microstructure and properties of spray formed extruded 7055aluminum alloy. Trans. Nonferrous Metals Soc. China 28, 872−879
Cerri, E., Evangelista, E., Forcellese, A., et al.: Comparative hot workability of 7012 and 7075 alloys after different pretreatment. Mater. Sci. Eng. A 197, 181–198 (1995)
Tekkaya, A.E., Schikorra, M., Becker, D., Biermann, D., Hammer, N., Pantke, K.: Hot profile extrusion of AA-6060 aluminum chips. J. Mater. Process. Technol. 209(7), 3343–3350 (2009)
Mcqueen, H.J., Ryan, N.D.: Constitutive analysis in hot working. Mater. Sci. Eng., A 322, 43–63 (2002)
Zener, C., Hollomon, J.H.: Effect of strain rate upon plastic flow of steel. J. Appl. Phys. 15, 22–27 (1944)
Acknowledgment
This work is supported by the Research Council of Norway (Project nr: 309691), and the National Key R&D Program of China (Project nr: 2019YFE0105000).
Author information
Authors and Affiliations
Corresponding author
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 2024 The Author(s), under exclusive license to Springer Nature Switzerland AG
About this paper
Cite this paper
Wang, L., Tao, Z., Huang, Y., Shi, M., Tang, K., Ma, X. (2024). Recovering and Hot Deformation Processing of Recycled Spray Formed 7055 Aluminum Alloy Powders. In: Mocellin, K., Bouchard, PO., Bigot, R., Balan, T. (eds) Proceedings of the 14th International Conference on the Technology of Plasticity - Current Trends in the Technology of Plasticity. ICTP 2023. Lecture Notes in Mechanical Engineering. Springer, Cham. https://doi.org/10.1007/978-3-031-42093-1_56
Download citation
DOI: https://doi.org/10.1007/978-3-031-42093-1_56
Published:
Publisher Name: Springer, Cham
Print ISBN: 978-3-031-42092-4
Online ISBN: 978-3-031-42093-1
eBook Packages: EngineeringEngineering (R0)