Calcium sulfo aluminate cement (\( {\text{C}}\overline{\text{S}} {\rm{A}} \)) is a promising low CO2 footprint alternative to Portland cement. The phase assemblage of a commercial \( {\text{C}}\overline{\text{S}} {\rm{A}} \) cement was investigated by a combination of XRD, SEM-EDX and selective extraction techniques. This study focused on the composition of perovsite phases present in the cement.
You have full access to this open access chapter, Download conference paper PDF
Similar content being viewed by others
Keywords
1 Introduction
Calcium sulfo aluminate cements (\( {\text{C}}\overline{\text{S}} {\rm{A}} \))Footnote 1 were developed by the China Building Material Academy in the seventies. \( {\text{C}}\overline{\text{S}} {\rm{A}} \) have many specific properties compared to Portland cement as fast setting, rapid hardening, shrinkage reduction. This special cement used alone or in combination with calcium sulphates and Portland cement has found applications such as airport runways and roads patching, selfleveling mortars, tile adhesives grouts… (Zhang et al. 1999). This is also a promising low CO2 footprint alternative to Portland cement due to the difference in the amount of energy used to produce \( {\text{C}}\overline{\text{S}} {\rm{A}} \) cements (lower kiln temperatures and energy at the mill to grind). The main raw materials used for making \( {\text{C}}\overline{\text{S}} {\rm{A}} \) cements are bauxite, limestone, clay, and gypsum and this leads to a mineralogical composition very different than Portland cement. While many studies have been carried out on the characterization of Portland cement, few are available concerning \( {\text{C}}\overline{\text{S}} {\rm{A}} \). In this study, we report a characterization of a commercial \( {\text{C}}\overline{\text{S}} {\rm{A}} \) using Rietveld quantitative analysis and scanning electron microscopy.
2 Methods and Approaches
The \( {\text{C}}\overline{\text{S}} {\rm{A}} \) cement was from a commercial supplier and the chemical characteristics of the cement are given in Table 1.
In order to analyze mineralogical composition, X-ray diffraction was performed on cement with a diffractometer BRUKER D8 Advance. Powder samples were analyzed using an incident beam angle (Cu Kα, λ = 1.54 Å) varying between 5 and 70°. Software X’Pert High Score was used to process diffraction patterns and crystals were identified using the Powder Diffraction File database. Rietveld analysis allowed obtaining mass fractions of crystalline phases in the cement.
For the microscopical investigations, powder samples were impregnated using a low viscosity epoxy and polished down to 0.25 μm using diamond pastes. The samples were further coated with carbon (~15 nm) and examined using a Quanta 200 FEG scanning electron microscope (SEM) from FEI coupled to an Oxford Xmax N 80 mm2 energy dispersive X-ray spectroscopy (EDX) analyser.
In order to improve the characterization of the cement, two different selective dissolution methods were used. In the first method, the silicate phases were removed in a solution of acid salicylic in methanol (Hjorth and Lauren 1971). In addition, a second selective dissolution method was used to get mainly perovskite phases in \( {\text{C}}\overline{\text{S}} {\rm{A}} \) by removing ye’elimite, anhydrite, gypsum with 5% Na2CO3 solution (Wang 2010). The method was modified to prevent precipitation of CaCO3 by washing the filtered suspension with 6% acetic acid. The filter paper and contents were placed in an oven at 105 °C until a constant weight was reached.
3 Results and Discussion
The main phases observed in the experimental diffraction pattern (Fig. 1a) are the orthorhombic ye’elimite C4A3\( \overline{\text{S}} \) with small amount of the pseudo cubic form, belite β and α’H- C2S and perovskites from the \( {\text{C}}\overline{\text{S}} {\rm{A}} \) clinker. Anhydrite II \( {\text{C}}\overline{\text{S}} \) is also present as mineral addition. Perovskite family has crystal structures related to the mineral perovskite CT. Ferrite phase Ca2(AlxFe1-x)2O5 is usually present in \( {\text{C}}\overline{\text{S}} {\rm{A}} \) and its structure is derived from that of perovskite by the substitution of Al and Fe for Ti, together with ordered omission of oxygen atoms, which causes onehalf of the sheets of octahedral in perovskite to be replaced by chains of tetrahedral (Taylor 1997). To obtain a good Rietveld refinement, it is also necessary to add a perovskite phase CT (Alvarez- Pinazo et al. 2012). The titanium dioxide is present by the use of bauxite, which usually contains some TiO2, as raw materials in the manufacturing process of \( {\text{C}}\overline{\text{S}} {\rm{A}} \) clinker. The peaks associated with this cubic phase are confirmed in the XRD pattern of the \( {\text{C}}\overline{\text{S}} {\rm{A}} \) after the extraction of the main phases (Fig. 1b).
However, with the assumed stoichiometry of perovskite CT, the elemental oxide composition TiO2 calculated from phase content deduced by Rietveld analysis is strongly overestimated in comparison with XRF analysis.
EDX analysis on polished section of \( {\text{C}}\overline{\text{S}} {\rm{A}} \) (Fig. 2a) and \( {\text{C}}\overline{\text{S}} {\rm{A}} \) after extraction revealed an average composition of ferrite Ca1.99Al0.39Si0.10Fe1.35Ti0.08Mg0.07O5.00 not far from the brownmillerite series Ca2(Fe2-xAlx)O5. However, the average composition of perovskite Ca2.00Al0.30Si0.22Fe1.06Ti0.40Mg0.05O5.31 is very different to the Ca2Ti2O4 composition. These compositions were similar to those observed in the ferrite/perovskite phases of a calcium aluminate cement (Gloter et al. 2000). We also observed in some grains perovskite lamellae with high amount of Ti on the scale of few micrometers (Fig. 2b).
4 Conclusions
The phase assemblage of a commercial calcium sulfo aluminate cement has been investigated with a special attention to the ferrite- perovskite phases. The ferrite composition is closed to the brownmillerite Ca2(Fe2-xAlx)O5 whereas the perovskite shows heterogeneity with important substitution of Ti by Fe, Al and Si.
Notes
- 1.
Standard cement chemistry notation is used.
As per this simplified notation: C = CaO, A = Al2O3, F = Fe2O3, S = SiO2,  = SO3 and T = TiO2.
References
Alvarez- Pinazo G, Cuesta A, Garcia-Maté M, Santacruz I, Losilla ER, De la Torre AG, Leon-Reina L, Aranda MAG (2012) Rietveld quantitative phase analysis of Yeelimitecontaining cements. Cem Concr Res 42:960–971
Gloter A, Ingrin J, Bouchet D, Scrivener K, Colliex C (2000) TEM evidence of perovskitebrownmillerite coexistence in the Ca(AlxFe1-x)O2.5 system with minor amounts of titanium and silicon. Phys. Chem. Miner 27:504–513
Hjorth L, Lauren K-G (1971) Belite in Portland cement. Cem Concr Res 1:27–40
Taylor HFW (1997) Cement Chemistry. Thomas Telford, London
Wang J (2010) Hydration mechanism of cements based on low-CO2 clinkers containing belite, ye’elimite and calcium alumino ferrite. PhD dissertation, University of Lille I, France
Zhang L, Su M, Wang Y (1999) Development of the use of sulfo- and ferroaluminate cements in China. Adv Cem Res 11:15–21
Acknowledgements
The authors acknowledge A. Diaz (C2MA, IMT Mines Ales) for sample preparation for SEM experiments
Author information
Authors and Affiliations
Corresponding author
Editor information
Editors and Affiliations
Rights and permissions
Open Access This chapter is licensed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license and indicate if changes were made.
The images or other third party material in this chapter are included in the chapter's Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the chapter's Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder.
Copyright information
© 2019 The Author(s)
About this paper
Cite this paper
Le Saout, G., Idir, R., Roux, JC. (2019). Characterisation of Perovskites in a Calcium Sulfo Aluminate Cement. In: Glagolev, S. (eds) 14th International Congress for Applied Mineralogy (ICAM2019). ICAM 2019. Springer Proceedings in Earth and Environmental Sciences. Springer, Cham. https://doi.org/10.1007/978-3-030-22974-0_82
Download citation
DOI: https://doi.org/10.1007/978-3-030-22974-0_82
Published:
Publisher Name: Springer, Cham
Print ISBN: 978-3-030-22973-3
Online ISBN: 978-3-030-22974-0
eBook Packages: Earth and Environmental ScienceEarth and Environmental Science (R0)