Photopyroelectric spectroscopy of Sb₂O₃ - ZnO ceramics

Abstract.

Photopyroelectric spectroscopy is used to study the band-gap energy of the ceramic (ZnO + xSb₂O₃), x = 0.1 - 1.5 mol% and the ceramic (ZnO + 0.4 mol%  Bi₂O₃ + xSb₂O₃), x = 0 - 1.5 mol% sintered at isothermal temperature, 1280 °C, for 1 and 2 hours. The wavelength of incident light, modulated at 9 Hz, is kept in the visible range and the photopyroelectric spectrum with reference to doping level is discussed. The band-gap energy is reduced from 3.2 eV, for pure ZnO, to 2.86, 2.83 eV for the samples without Bi₂O₃at 0.1 mol% of Sb₂O₃ for 1 and 2 hours of sintering time, respectively. It is reduced to 2.83, 2.80 eV for the samples with Bi₂O₃ at 0 mol% of Sb₂O₃ for 1 and 2 hours of sintering time, respectively. The steepness factor σ_A which characterizes the slop of exponential optical absorption is discussed with reference to the doping level. The phase constitution is determined by XRD analysis; microstructure and compositional analysis of the selected areas are analyzed using SEM and EDX.