Effects of {10–12} Twins on Dynamic Torsional Properties of Extruded AZ31 Magnesium Alloy

  • Published:
Metals and Materials International Aims and scope Submit manuscript

Abstract

Effects of initial twins on dynamic torsional properties of extruded AZ31 alloy were investigated by introducing {10–12} twins into it through precompression to 3 and 6% strains along the extrusion direction and performing torsional testing at a strain rate of 1.4 × 103 s−1 using a torsional Kolsky bar system. The as-extruded sample without twins showed higher dynamic torsional properties than the precompressed samples with many initial twins; the maximum shear strength and fracture shear strain decreased with increasing amount of initial twins. In the as-extruded sample, twinning occurred vigorously throughout the gage section of the tubular specimen during high-strain-rate torsional tests, resulting in heavily deformed morphology, many macrocracks, and rough fractured surfaces. The increased amount of initial twins suppressed the twinning behavior and localized the applied torsional deformation; this resulted in an almost unchanged sample shape, no secondary cracks, and a flat fracture plane, thereby deteriorating the dynamic torsional properties of the extruded alloy.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6

Similar content being viewed by others

References

  1. G.S. Rao, Y.V.R.K. Prasad, Mater. Sci. Eng. A 13, 2219 (1982)

    Google Scholar 

  2. S. Kleiner, P.J. Uggowitzer, Mater. Sci. Eng. A 379, 258 (2004)

    Article  Google Scholar 

  3. L. Tang, C. Liu, Z. Chen, D. Ji, H. Xiao, Mater. Des. 50, 587 (2013)

    Article  Google Scholar 

  4. J. Koike, T. Kobayashi, T. Mukai, H. Watanabe, M. Suzuki, K. Maruyama, K. Higashi, Acta Mater. 51, 2055 (2003)

    Article  Google Scholar 

  5. S. Sandlöbes, S. Zaefferer, I. Schestakow, S. Yi, R.G. Martinez, Acta Mater. 59, 429 (2011)

    Article  Google Scholar 

  6. A. Jain, S.R. Agnew, Mater. Sci. Eng. A 462, 29 (2007)

    Article  Google Scholar 

  7. Y.N. Wang, J.C. Huang, Acta Mater. 55, 897 (2007)

    Article  Google Scholar 

  8. M.R. Barnett, Mater. Sci. Eng. A 464, 1 (2007)

    Article  Google Scholar 

  9. L. Wu, S.R. Agnew, Y. Ren, D.W. Brown, B. Clausen, G.M. Stoica, H.R. Wenk, P.K. Liaw, Mater. Sci. Eng. A 527, 7057 (2010)

    Article  Google Scholar 

  10. X.Y. Lou, M. Li, R.K. Boger, S.R. Agnew, R.H. Wagoner, Int. J. Plast. 23, 44 (2007)

    Article  Google Scholar 

  11. L. Wu, A. Jain, D.W. Brown, G.M. Stoica, S.R. Agnew, B. Clausen, D.E. Fielden, P.K. Liaw, Acta Mater. 56, 688 (2008)

    Article  Google Scholar 

  12. G. Proust, C.N. Tomé, A. Jain, S.R. Agnew, Int. J. Plast. 25, 861 (2009)

    Article  Google Scholar 

  13. R.E.R. Hill, R. Abbaschian, Physical Metallurgy Principles, 3rd edn. (PWS-Kent, Boston, 1994)

    Google Scholar 

  14. H.E. Kadiri, J. Kapil, A.L. Oppedal, L.G. Hector Jr., S.R. Agnew, M. Cherkaoui, S.C. Vogel, Acta Mater. 61, 3549 (2013)

    Article  Google Scholar 

  15. L. Jiang, J.J. Jonas, A.A. Luo, A.K. Sachdev, S. Godet, Scr. Mater. 54, 771 (2006)

    Article  Google Scholar 

  16. L. Jiang, J.J. Jonas, R.K. Mishra, A.A. Luo, A.K. Sachdev, S. Godet, Acta Mater. 55, 3899 (2007)

    Article  Google Scholar 

  17. S.-G. Hong, S.H. Park, C.S. Lee, Acta Mater. 58, 5873 (2010)

    Article  Google Scholar 

  18. M.R. Barnett, Z. Keshavarz, A.G. Beer, D. Atwell, Acta Mater. 52, 5093 (2004)

    Article  Google Scholar 

  19. I. Karaman, H. Sehitoglu, A.J. Beaudoin, Y.I. Chumlyakov, H.J. Maier, C.N. Tome, Acta Mater. 48, 2031 (2000)

    Article  Google Scholar 

  20. B. Song, R. Xin, G. Chen, X. Zhang, Q. Liu, Scr. Mater. 66, 1061 (2012)

    Article  Google Scholar 

  21. Q. Dai, W. Lan, X. Chen, J. Eng. Mater. Technol. 136, 011005-1 (2013)

    Article  Google Scholar 

  22. L. Jiang, J.J. Jonas, A.A. Luo, A.K. Sachdev, S. Godet, Mater. Sci. Eng. A 445–446, 302 (2007)

    Article  Google Scholar 

  23. M. Knezevic, A. Levinson, R. Harris, R.K. Mishra, R.D. Doherty, S.R. Kalidindi, Acta Mater. 58, 6230 (2010)

    Article  Google Scholar 

  24. S.H. Park, S.-G. Hong, C.S. Lee, Mater. Sci. Eng. A 578, 271 (2013)

    Article  Google Scholar 

  25. S.-G. Hong, S.H. Park, C.S. Lee, J. Mater. Res. 25, 784 (2010)

    Article  Google Scholar 

  26. S.H. Park, Mater. Sci. Eng. A 680, 214 (2017)

    Article  Google Scholar 

  27. S.H. Park, S.-G. Hong, C.S. Lee, Mater. Sci. Eng. A 570, 149 (2013)

    Article  Google Scholar 

  28. S.-H. Kim, S.-G. Hong, J.-H. Lee, C.S. Lee, J. Yoon, H. Yu, S.H. Park, Mater. Sci. Eng. A 700, 191 (2017)

    Article  Google Scholar 

  29. S.H. Park, H.S. Kim, J.H. Bae, C.D. Yim, B.S. You, Scr. Mater. 69, 250 (2013)

    Article  Google Scholar 

  30. C.H. Park, C.-S. Oh, S. Kim, Mater. Sci. Eng. A 542, 127 (2012)

    Article  Google Scholar 

  31. G. Wan, B.L. Wu, Y.D. Zhang, G.Y. Sha, C. Esling, Mater. Sci. Eng. A 527, 2915 (2010)

    Article  Google Scholar 

  32. F. Kabirian, A.S. Khan, T.G. Herlod, Int. J. Plast. 68, 1 (2015)

    Article  Google Scholar 

  33. N. Guo, B. Song, C. Guo, R. Xin, Q. Liu, Mater. Des. 83, 270 (2015)

    Article  Google Scholar 

  34. B. Song, C. Wang, N. Guo, H. Pan, R. Xin, Mater. 10, 280 (2017)

    Article  Google Scholar 

  35. H. Chen, T. Liu, H. Yu, B. Song, D. Hou, N. Guo, J. He, Adv. Eng. Mater. 18, 1683 (2016)

    Article  Google Scholar 

  36. B. Hwang, S. Lee, Y.C. Kim, N.J. Kim, D.H. Shin, Mater. Sci. Eng. A 441, 308 (2006)

    Article  Google Scholar 

  37. H. Kolsky, Proc. Phys. Soc. 62B, 676 (1949)

    Article  Google Scholar 

  38. A. Gilat, in ASM Handbook, vol. 8: Mechanical Testing and Evaluation, ed. by H. Kuhn, D. Medlin (ASM Int, Metals Park, 2000)

    Google Scholar 

  39. Y. Shiota, Y. Tomota, A. Moriai, T. Kamiyama, Met. Mater. Int. 11, 371 (2005)

    Article  Google Scholar 

  40. H.S. Lee, B. Hwang, S. Lee, C.G. Lee, S.J. Kim, Metall. Mater. Trans. 35A, 2373 (2004)

    Google Scholar 

  41. D.G. Lee, S. Lee, C.S. Lee, Mater. Sci. Eng. A 366, 25 (2004)

    Article  Google Scholar 

  42. C.S. Roberts, Magnesium and Its Alloys (Wiley, New York, 1960)

    Google Scholar 

  43. G.E. Dieter, Mechanical Metallurgy, SI Metric edn. (McGraw-Hill Book Co., Singapore, 1988)

    Google Scholar 

  44. P. Franciosi, Acta Metall. 33, 1601 (1985)

    Article  Google Scholar 

  45. C.S. Pande, B.B. Rath, M.A. Imam, Mater. Sci. Eng. A 367, 171 (2004)

    Article  Google Scholar 

  46. J. Zhang, Q. Yu, Y. Jiang, Q. Li, Int. J. Plast. 27, 768 (2011)

    Article  Google Scholar 

  47. Y.-H. Zhao, J.F. Bingert, X.-Z. Liao, B.-Z. Cui, K. Han, A.V. Sergueeva, A.K. Mukherjee, R.Z. Valiev, T.G. Langdon, Y.T. Zhu, Adv. Mater. 18, 2949 (2006)

    Article  Google Scholar 

  48. J. Marian, W. Cai, V.V. Bulatov, Nat. Mater. 3, 158 (2004)

    Article  Google Scholar 

  49. M.A. Meyers, O. Vöhringer, V.A. Lubarda, Acta Mater. 49, 4025 (2001)

    Article  Google Scholar 

  50. M.R. Barnett, Scr. Mater. 59, 696 (2008)

    Article  Google Scholar 

  51. J.W. Christian, S. Mahajan, Prog. Mater Sci. 39, 1 (1995)

    Article  Google Scholar 

  52. A. Ghaderi, M.R. Barnett, Acta Mater. 59, 7824 (2011)

    Article  Google Scholar 

  53. N. Stanford, J. Geng, Y.B. Chun, C.H.J. Davies, J.F. Nie, M.R. Barnett, Acta Mater. 60, 218 (2012)

    Article  Google Scholar 

  54. I. Ulacia, C.P. Salisbury, I. Hurtado, M.J. Worswick, J. Mater. Process. Technol. 211, 830 (2011)

    Article  Google Scholar 

Download references

Acknowledgements

This work was supported by the National Research Foundation of Korea (NRF) grant funded by the Korean government (MSIP, South Korea) (No. 2016R1C1B2012140 and No. 2017R1A4A1015628).

Author information

Authors and Affiliations

  1. School of Materials Science and Engineering, Kyungpook National University, Daegu, 41566, Republic of Korea

    Jong Un Lee, Sang-Hoon Kim, Ye Jin Kim & Sung Hyuk Park

  2. Technical Research Laboratories, POSCO, Pohang, 37859, Republic of Korea

    Seok Weon Song

  3. Gwangyang Steel Products Research Group, Technical Research Laboratories, POSCO, Gwangyang, 57807, Republic of Korea

    Yongjin Kim

Authors
  1. Jong Un Lee
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Seok Weon Song
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Yongjin Kim
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Sang-Hoon Kim
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Ye Jin Kim
    View author publications

    You can also search for this author in PubMed Google Scholar

  6. Sung Hyuk Park
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Sung Hyuk Park.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Lee, J.U., Song, S.W., Kim, Y. et al. Effects of {10–12} Twins on Dynamic Torsional Properties of Extruded AZ31 Magnesium Alloy. Met. Mater. Int. 24, 283–289 (2018). https://doi.org/10.1007/s12540-018-0030-x

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s12540-018-0030-x

Keywords

Search

Navigation