Abstract
Hydrogen storage properties of pure Mg were studied at 593 K under 12 bar H2. In order to increase the hydriding and dehydriding rates, pure Mg was ground under hydrogen atmosphere (reactive mechanical grinding, RMG) and its hydrogen storage properties were subsequently investigated. Pure Mg absorbed hydrogen very slowly. At the number of cycles (n) of 1, pure Mg absorbed 0.05 wt% H for 5 min, 0.08 wt% H for 10 min and 0.29 wt% H for 60 min at 593 K under 12 bar H2. Activation was completed at the fifth cycle. At n = 6, pure Mg absorbed 1.76 wt% H for 5 min, 2.17 wt% H for 10 min and 3.40 wt% H for 60 min. The activation of pure Mg after RMG was completed at the sixth cycle. At n = 7, pure Mg after RMG absorbed 2.57 wt% H for 5 min, 3.21 wt% H for 10 min and 4.15 wt% H for 60 min.
Similar content being viewed by others
References
Akiba E, Nomura K, Ono S and Suda S 1982 Int. J. Hydrogen Energy 17 787
Aminorroaya S, Ranjbar A, Cho Y H, Liu H K and Dahle A K 2011 Int. J. Hydrogen Energy 36 571
Boulet J M and Gerard N 1983 J. Less-Common Met. 89 151
Cho Y H, Aminorroaya S, Liu H K and Dahle A K 2011 Int. J. Hydrogen Energy 36 4984
Eisenberg F G, Zagnoli D A and Sheridan III J J 1980 J. Less-Common Met. 74 323
Hong S H and Song M Y 2013a Met. Mater. Int. 19 895
Hong S H and Song M Y 2013b Met. Mater. Int. 19 1145
Kwak Y J, Park H R and Song M Y 2013 Met. Mater. Int. 19 543
Li Z, Liu X, Huang Z, Jiang L and Wang S 2006 Rare Metals 25 247
Li Z, Liu X, Jiang L and Wang S 2007 Int. J. Hydrogen Energy 32 1869
Lucaci M, Biris A R, Orban R L, Sbarcea G B and Tsakiris V 2009 J. Alloys Compd. 488 163
Milanese C, Girella A, Bruni G, Cofrancesco P, Berbenni V, Matteazzi P and Marini A 2010 Intermetallics 18 203
Mintz M H, Gavra Z and Hadari Z 1978 J. Inorg. Nucl. Chem. 40 765
Pei P, Song X, Liu J, Song A, Zhang P and Chen G 2012 Int. J. Hydrogen Energy 37 984
Reilly J J and Wiswall R H 1967 Inorg. Chem. 6 2220
Reilly J J and Wiswall Jr R H 1968 Inorg. Chem. 7 2254
Song M Y, Baek S H, Bobet J-L and Hong S H 2010 Int. J. Hydrogen Energy 35 10366
Song M Y, Baek S H, Bobet J-L, Park H R and Kim B G 2013a Met. Mater. Int. 19 237
Song M Y, Kwak Y J, Lee S H, Park H R and Kim B G 2013b Met. Mater. Int. 19 879
Song M Y, Kwon S N, Mumm D R and Park H R 2013c Met. Mater. Int. 19 309
Song M Y, Kwon S N, Park H R and Mumm D R 2013d Met. Mater. Int. 19 1139
Tanguy B, Soubeyroux J L, Pezat M, Portier J and Hagenmuller P 1976 Mater. Res. Bull. 11 1441
Zhong H C, Wang H, Ouyang L Z and Zhu M 2011 J. Alloys Compd. 509 4268
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Song, M.Y., Kwak, Y.J., Lee, S.H. et al. Comparison of hydrogen storage properties of pure Mg and milled pure Mg. Bull Mater Sci 37, 831–835 (2014). https://doi.org/10.1007/s12034-014-0013-6
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12034-014-0013-6