Abstract
The structural and electronic properties of a monolayer and bilayer blue phosphorene/graphene-like GaN van der Waals heterostructures are studied using first-principle calculations. The results show that the monolayer-blue phosphorene/graphene-like GaN heterostructure is an indirect bandgap semiconductor with intrinsic type II band alignment. More importantly, the external electric field tunes the bandgap of monolayer-blue phosphorene/graphene-like GaN and bilayer-blue phosphorene/graphene-like GaN, and the relationship between bandgap and external electric field indicates a Stark effect. The semiconductor-to-metal transition is observed in the presence of a strong electric field.
Avoid common mistakes on your manuscript.
Introduction
Two-dimensional (2D) materials such as graphene [1], transition metal dichalcogenides (TMDs) [2], black phosphorene (BP) [3], and graphene-like GaN (g-GaN) [4] have been in the spotlight, owing to their fascinating physical properties and potential applications in devices. As a fast-emerging research area, the way in which the heterostructures are assembled from the isolated atoms remains to be an exciting research filed. It is considered as a novel way to construct devices, which integrates the properties of each isolated component with ideal properties applied in nanoelectronics [5, 6]. Due to atomic layers’ interaction [7], these heterostructures possess outstanding properties comparing with the pure 2D materials, and their properties are preserved without degradation when they are bonded together in the layer-by-layer way. To date, many efforts have been made to obtain van der Waals (vdW) heterostructures. It is worth noting that the blue phosphorene (blue-P)-based vdW heterostructures such as blue-P/TMDs [8,9,10] and blue-P/graphene [11] have attracted increasing attention due to their excellent electronic and optical characteristics.
Among the above-mentioned 2D semiconductor materials, blue-P monolayer has been prepared by epitaxial growth on Au (111) substrates for the first time in 2016 [7]. Z. Zhang et. al. predicted the epitaxial growth of blue-P monolayers on GaN (001) substrates, and proposed an unconventional “half-layer” growth mechanism. It is also pointed out that blue-P is more stable on the surface of GaN (001) due to the chemical affinity between phosphorus and gallium and the good lattice matching [12]. Blue-P, consisting of a vertically corrugated yet single layer of phosphorus atoms, attracts intense research interest due to its superb properties such as sizable bandgap and high mobility [13, 14]. In addition, g-GaN, as a novel 2D material, can be synthesized experimentally by means of a migration-enhanced encapsulated growth (MEEG) technique [15]. Theoretical simulation has shown that g-GaN is a semiconductor with an indirect bandgap, which can be efficiently manipulated by an external electric field [16]. Like other 2D materials, g-GaN can also be hydrogenated and halogenated conveniently. All these studies have shown that g-GaN is an alternative 2D semiconductor for applications in many important fields in the future. The lattice parameter of g-GaN could match well with blue-P, which indicates that blue-P/g-GaN is an ideal material system for the construction of heterostructures, as well as an excellent inserting layer for tuning of their electronic properties by the interlayer interaction. In this regard, it matters to investigate the electronic and optical properties of the blue-P/g-GaN vdW heterostructures. However, few researches have been investigated to study the properties of blue-P/g-GaN vdW heterostructures [17, 18].
In this work, the electronic structural properties and the variation tendency of the bandgap energy (Eg) with the vertical external electric field (Eext) in the blue-P/g-GaN vdW heterostructures are evaluated and conducted by using the first-principles calculations with vdW-corrected exchange-correlation functional.
Computational Methods
The band structures and electrical properties of the monolayer and bilayer blue-P/g-GaN vdW heterostructures have been investigated using the Cambridge Serial Total Energy Package (CASTEP) [19], which is based on the density functional theory (DFT) [20, 21] in a plane-wave basis set with the projector augmented wave (PAW) method potential [22, 23]. The generalized gradient approximation (GGA) with the Perdew-Burke-Ernzerhof (PBE) [24] function is adopted to describe the electrons exchange-correlation energy. Since the GGA-PAW approximation usually underestimates the Eg of semiconductors, the hybridization functional HSE06 is carried out to correct them. The effect of vdW interaction [25] is described by the Grimme’s DFT-D2 method. Here, a 500 eV cut-off energy for the plane wave basis was set to ensure the convergence of total energy. A vacuum thickness of 20 Å along the Z direction of the blue-P/g-GaN heterostructures is added to eliminate the interaction with the spurious replica images. The atomic positions are optimized until the convergence tolerance of the force on each atom is smaller than 0.001 eV/Å. The first Brillouin-zone integration is used by a fine grid of 7 × 7 × 1 for the structure optimization and 21 × 21 × 1 for electronic state calculation.
Results and Discussion
Several structures shown in our previous work have been studied as a benchmark to obtain the most stable structure of the bilayer heterostructures [18]. The optimized lattice constants are 3.25 Å and 3.20 Å for bilayer-blue-P and g-GaN, respectively, whose values are in agreement with the reported studies [9, 26]. The lattice mismatch is about of 2% only [18]. In order to obtain the minimum energy configuration and evaluate the thermal stability of the structures, the blue-P layer is moved relating to the g-GaN layer and the lowest energy configuration is found by finite amounts δx/y. The evolution of the total energy difference as a function of δx and δy is shown in our previous studies [18]. Figure 1a shows the atomic structures of side and top view of bilayer-blue-P on g-GaN. The optimum stacking mode of blue-P bilayers is consistent with the previous paper [27]. Figure 1b demonstrates the relation between the binding energy (Eb) at the interface and the interlayer distance of blue-P and g-GaN (dblue-P/g-GaN). Its definition has been described in detail in our previous studies [18]. The Eb is about 49 meV for the single-layer blue-P with an equilibrium distance of 3.57 Å. For the bilayer, the binding energy is almost the same as that of the single layer, whereas the equilibrium distance is 3.52 Å. Those binding energies have the same magnitude order as other vdW crystals, such as BP/graphene [Eb = 60 meV] [11], blue-P/graphene [Eb = 70 meV] [6], and bilayer blue-P [Eb = 25 meV] [27].
Figure 2a-b displays the band structures of monolayer- blue-P/g-GaN heterostructure and bilayer- blue-P/g-GaN heterostructure, with Eg of 1.26 eV and 1.075 eV calculated by using GGA, respectively. For the HSE06 method, the Eg is 2.2 eV and 1.91 eV, respectively. For both heterostructures, the minimal-energy states in the conduction band are near M point and the maximal-energy states in the valence band are at K point, the two points are not at the same crystal momentum in the Brillouin zone. Thus, the bandgap is an indirect band gap for both semiconductor heterostructures. The Eg of monolayer-blue-P/g-GaN heterostructure decreases 0.63 eV compared with the monolayer-blue-P (1.89 eV), while the Eg of bilayer-blue-P (1.118 eV) shrinks 0.043 eV in contrast to bilayer-blue-P/g-GaN heterostructure. The band bending can be achieved from the difference between the Fermi levels of the blue-P with the g-GaN system and the free-standing blue-P [28]: ΔEF = W − WP, where W is the work function of the composed system (blue-P/g-GaN), and WP is the work function of the pristine blue-P. The ΔEF of − 1.17 eV and − 0.81 eV for the monolayer-blue-P/g-GaN heterojunctions and the bilayer-blue-P/g-GaN heterojunctions are obtained respectively, as shown in Fig. 2c, d. As one can see, the type of the energy band alignment is the staggered gap (type II) at the interfaces for all the monolayer-blue-P/g-GaN heterostructures and the bilayer-blue-P/g-GaN heterostructures.
The heterostructure is often subjected to an external electric field to tune its electronic properties while applied to nanoelectronic devices. In order to study the influence of the Eext on the electronic structure, the band structures are calculated with different Eext for the blue-P/g-GaN heterostructures. As reported in previous work, the geometrical structure of the heterostructure can be neglected, but the band structure changes greatly under different Eext [29]. Figure 3a shows the evolution of the Eg as a function of the Eext from − 1.0 eV/Å to 1.0 eV/Å. The direction of Eext from top (g-GaN layer) to bottom (blue-P layer) is taken as the forward direction. It is clearly shown that monolayer-blue-P/g-GaN and bilayer-blue-P/g-GaN heterostructures exhibit a bandgap modulation with the Eext. For monolayer-blue-P/g-GaN, in the case of the forward Eext, the Eg increases linearly with the increasing Eext ≤ 0.4 eV/Å (L-increase range). The monolayer-blue-P/g-GaN obtains its maximum Eg when Eext = 0.5 eV/Å and shows little change when Eext is in the range 0.4 < Eext < 0.6 eV/Å (saturation range), which enhances the band offsets so as to promote the separation of electron-hole pairs. The initial enlargement in Eg is attributed to the counterbalance of Eext to some extent by the built-in electric field (Eint). The Eg comes to a linear decrease range with increasing Eext > 0.6 eV/Å (L-decrease range). Thus, the heterostructure shows a metal behavior when it is subjected to a stronger electric field. This is originated from the dielectric breakdown as well as charge tunneling. In contrast, the Eg declines linearly with increasing Eext (L-decrease range) under a reverse Eext, caused by the conduction band minimum (CBM) band edge shifting toward to the valence band maximum (VBM). However, when Eext = − 0.7 eV/Å, the bandgap begins to decrease sharply, which may be due to the breakdown. When Eext < − 0.8 eV/Å, the blue-P/g-GaN heterojunction experiences a transition from semiconductor to metal (metal range). These results reveal that both Eg and semiconductor to metal transition of the blue-P/g-GaN heterostructure is dependent on electrostatic gating, which could be used in high-performance electronic and optoelectronic devices. In addition, the effect of Eext on the Eg between the bilayers of blue-P and g-GaN heterostructure is the same as the single layer but with a smaller electronic field for transition from semiconductor to metal.
To explore the effect of electric field on the band structure, the relation between the energy band structures and the external electric field are calculated. The band structures of the monolayer-blue-P/g-GaN heterostructures with Eext of 0.3 eV/Å, 0.5 eV/Å, − 0.3 eV/Å, and 0.7 eV/Å are shown in Fig. 3b–e. In Fig. 3b-c, under the 0.3 eV/Å and 0.5 eV/Å of Eext, the Eg increases to 1.651 eV and 1.757 eV. This indicates the quasi-Fermi level of the g-GaN monolayer is shifted downward, and the quasi-Fermi level of blue-P monolayer is lifted upward. However, in Fig. 3d-e, for the − 0.3 eV/Å and − 0.7 eV/Å of Eext, the Eg decrease to 0.888 eV and 0.49 eV. The quasi-Fermi level of g-GaN moves upward, and the quasi-Fermi level of blue-P moves downward. The results show that the bandgap varies linearly with the applied vertical Eext, indicating a giant Stark effect [30]. Upon applying a vertical Eext, the subband states of the valence and conduction valence would undergo a mixing, leading to a field-induced splitting of the electronic levels. The electrostatic potential difference induced by the external field considerably changed the electronic structures near the Fermi level [31].
Figure 4a–d shows the isosurface of charge accumulation (with color in orange) and depletion (light green), which exhibits the change of charge density of the blue-P/g-GaN heterojunction with the Eext value of 0.3 eV/Å, 0.5 eV/Å, − 0.3 eV/Å, and − 0.7 eV/Å, respectively. Upon applying a forward Eext, as exhibited in Fig. 4a-b, positive charges (holes) tend to transfer from blue-P layer to g-GaN layer, and negative charges (electrons) transfer from g-GaN to blue-P layer. At the same time concurrently, one can see that the charge-transfer amount is more than 0.3 eV/Å when the electric field is 0.5 eV/Å. Essentially, a positive external electric field orients the charge along the direction of the stress field, restricting the charge to the atomic plane, but leaving the charge in these planes, thereby facilitating the transfer of the charge from blue-P to g-GaN. In contrast, the negative Eext induces electrons to accumulate/deplete at the opposite side, as visualized in Fig. 4c-d. Mainly negative external electric fields position the charge back towards the stress field and thus transfer the charge from g-GaN to blue-P. Accordingly, the quasi-Fermi level of g-GaN monolayer and EVBM rise, while the quasi-Fermi level of blue-P monolayer and ECBM decrease, resulting in a linear reduction on bandgap. Simultaneously, electrons are transferred from blue-P to g-GaN under a reverse Eext. It is found that the amount of the transferred charge increases with the increase of electric field intensity.
To make it clear that how Eext modulates the electronic property, the integrated charge density difference of the monolayer-blue-P/g-GaN heterostructure as a function of the perpendicular distance is calculated, displayed in Fig. 4e. The positive values in Fig. 4e indicate charge accumulation, and the negative values represent charge depletion. For Eext = 0, the charge density difference of the heterostructure is obtained by ∆ρ = ρheterostructure−ρg-GaN−ρblue-P. The change of the plane-average charge density difference at interfaces indicates that the electrons were transferred from the g-GaN layer to blue-P layer across the interface, whereas the holes remained in the g-GaN side. The surface averaged differential charge with an electric field is calculated for 0.3 eV/Å and − 0.3 eV/Å. The Eext can exert influence on transferring charges in the heterostructure. It can be described as [29]
where \( \int {\rho}_{E_{\mathrm{ext}}}\left(x,y,z\right) dxdy\ \mathrm{and}\int {\rho}_{E_0}\left(x,y,z\right) dxdy \) are the charge density at (x, y, z) point in the supercell of the monolayer-BP/g-GaN heterostructure with and without Eext, respectively. The direction of charge transfer induced by the negative (blue line) Eext is opposite to that of the positive (red line) Eext. The integrated charge density quantitatively illustrates that the amount of transferred charges increases with the strength of the Eext. The value of the charges transfers for the blue-P/g-GaN heterostructure with 0.3 eV/Å of Eext is larger than that of 0 eV/Å and − 0.3 eV/Å, because the positive external electric field localizes the charges along the direction of the applied field, confining the charges to g-GaN planes.
In order to distinguish the contributions of blue-P and g-GaN in the band structure, the projected state density of the heterostructures is calculated and shown in Fig. 5a. It can be seen that the contribution of VBM mainly comes from the g-GaN, and the entrainment contribution is mainly from the blue-P. Figure 5b displays the isosurface of charge accumulation and depletion of the monolayer- blue-P/g-GaN and bilayer-blue-P/g-GaN under 0.5 eV/Å and 0.7 eV/Å external field, respectively. Due to the dielectric breakdown of the bilayer-blue-P/g-GaN at 0.7 eV/Å external field, the current relathed the charge transfer would have saturated under the increasing external field, which is in accordance with that in Fig. 3a.
Conclusion
In summary, the structural and electronic properties of the monolayer-blue-P/g-GaN and bilayer-blue-P/g-GaN vdW heterostructures are investigated by using first-principle calculations. The results show that the monolayer-blue-P/g- GaN heterostructure is an indirect band gap semiconductor with intrinsic type II band alignment. The band offset and Eg of monolayer-blue-P/g-GaN and bilayer-blue-P/g-GaN can be continuously tuned by Eext, and the relation between Eg and Eext indicates a Stark effect. The Eg becomes zero at − 0.8 and 0.9 eV/Å for monolayer-blue-P/g-GaN, and − 0.5 and 0.7 eV/Å for bilayer-blue-P/g-GaN, indicating a transition from semiconductor to metal.
Abbreviations
- 2D:
-
Two-dimensional
- Blue-P:
-
Blue phosphorene
- BP:
-
Black phosphorene
- CASTEP:
-
Cambridge Serial Total Energy Package
- CBM:
-
Conduction band minimum
- DFT:
-
Density functional theory
- GGA:
-
Generalized gradient approximation
- G-GaN:
-
Graphene-like GaN
- MEEG:
-
Migration-enhanced encapsulated growth
- PAW:
-
Projector augmented wave
- PBE:
-
Perdew-Burke-Ernzerhof
- TMDs:
-
Transition metal dichalcogenides
- VBM:
-
Valence band maximum
- vdW:
-
van der Waals
References
Novoselov KS, Geim AK, Morozov SV, Jiang D, Zhang Y, Dubonos SV, Grigorieva IV, Firsov AA (2004) Electric field effect in atomically thin carbon films. Science. 306:666–669
Ramasubramaniam A, Naveh D, Towe E (2011) Tunable band gaps in bilayer transition-metal dichalcogenides. Phys Rev B 84:205325
Rodin AS, Carvalho A, Castro Neto AH (2014) Strain-induced gap modification in black phosphorus. Phys Rev Lett 112:176801
Al Balushi ZY, Wang K, Ghosh RK, Vila RA, Eichfeld SM, Caldwell JD, Qin X, Lin YC, DeSario PA, Stone G, Subramanian S, Paul DF, Wallace RM, Datta S, Redwing JM, Robinson JA (2016) Two-dimensional gallium nitride realized via graphene encapsulation. Nat Mater. 15:1166–1171
Roy T, Tosun M, Kang JS, Sachid AB, Desai SB, Hettick M, Hu CC, Javey A (2014) Field-effect transistors built from all two-dimensional material components. ACS Nano. 8:6259–6264
Sun M, Chou JP, Ren Q, Zhao Y, Yu J, Tang W (2017a) Tunable Schottky barrier in van der Waals heterostructures of graphene and g-GaN. Appl. Phys. Lett. 110:192
Deng D, Novoselov KS, Fu Q, Zheng N, Tian Z, Bao X (2016) Catalysis with two-dimensional materials and their heterostructures. Nat Nanotechnol. 11:218–230
Peng Q, Wang Z, Sa B, Wu B, Sun Z (2016a) Electronic structures and enhanced optical properties of blue phosphorene/transition metal dichalcogenides van der Waals heterostructures. Sci Rep. 6:31994
Peng Q, Wang Z, Sa B, Wu B, Sun Z (2016b) Blue phosphorene/MS2 (M = Nb, Ta) heterostructures as promising flexible anodes for lithium-ion batteries. ACS Appl Mater Interfaces. 8:13449–13457
Zhang ZY, Si MS, Peng SL, Zhang F, Wang YH, Xue DS (2015) Bandgap engineering in van der Waals heterostructures of blue phosphorene and MoS2 : a first principles calculation. J Solid State Chem 231:64–69
Padilha JE, Fazzio A, da Silva AJ (2015) Van der Waals heterostructure of phosphorene and graphene: tuning the Schottky barrier and doping by electrostatic gating. Phys Rev Lett. 114:066803
Zeng J, Cui P, Zhang Z (2017) Half Layer By Half Layer Growth of a Blue Phosphorene Monolayer on a GaN(001) Substrate. Phys Rev Lett. 118:046101
Zhu Z, Tomanek D (2014) Semiconducting layered blue phosphorus: a computational study. Phys. Rev. Lett. 112:176802
Xiao J, Long M, Zhang X, Ouyang J, Xu H, Gao Y (2015) Theoretical predictions on the electronic structure and charge carrier mobility in 2D phosphorus sheets. Sci Rep. 5:9961
Balushi ZYA, Wang K, Ghosh RK, Vilá RA, Eichfeld SM, Caldwell JD, Qin X, Lin YC, Desario PA, Stone G (2016) Two-dimensional gallium nitride realized via graphene encapsulation. Nature Materials. 15:1166
Chen Q, Hu H, Chen X, Wang J (2011) Tailoring band gap in GaN sheet by chemical modification and electric field: Ab initio calculations. Appl Phys Lett. 98:1687
Sun M, Chou JP, Yu J, Tang W (2017b) Electronic properties of blue phosphorene/graphene and blue phosphorene/graphene-like gallium nitride heterostructures. Phys Chem Chem Phys. 19:17324–17330
Guo J, Zhou Z, Wang T, Lu Z, Yang Z, Liu C (2017) Electronic structure and optical properties for blue phosphorene/graphene-like GaN van der Waals heterostructures. Curr Appl Phys. 17:1714–1720
Clark SJ, Segall M, Pickard CJ, Hasnip P, Probert M, Refson K, Payne MC (2005) First principles methods using CASTEP. 220:567–570
Klimes J, Bowler DR, Michaelides A (2010) Chemical accuracy for the van der Waals density functional. J Phys Condens Matter. 22:022201
Kresse G, Furthmüller J (1996) Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Physical Review B 54:11169–11186
Blöchl PE (1994) Projector augmented-wave method. Phys Rev B. 50:17953–17979
Kresse GJ, Joubert D (1999) From ultrasoft pseudopotentials to the projector augmented-wave method. 59:1758
Perdew JP, Burke K, Ernzerhof M (1997) Generalized gradient approximation made simple [Phys. Rev. Lett. 77, 3865 (1996)]. Phys Rev Lett 78:1396–1396
Grimme S, Antony J, Ehrlich S, Krieg H (2010) A consistent and accurate ab initio parametrization of density functional dispersion correction (DFT-D) for the 94 elements H-Pu. J Chem Phys. 132:154104
Shao Y, Xiao Z, Bi C, Yuan Y, Huang J (2014) Origin and elimination of photocurrent hysteresis by fullerene passivation in CH3NH3PbI3 planar heterojunction solar cells. Nature Communications. 5:5784
Mogulkoc Y, Modarresi M, Mogulkoc A, Ciftic YO (2016) electronic and optical properties of bilayer blue phosphorus. Computational Materials Science. 124:23–29
Khomyakov PA, Giovannetti G, Rusu PC, Brocks G, van den Brink J, Kelly PJ (2009) First-principles study of the interaction and charge transfer between graphene and metals. Physical Review B. 79
Xiong W, Xia C, Du J, Wang T, Peng Y, Wei Z, Li J (2017) Band engineering of the MoS2/stanene heterostructure: strain and electrostatic gating. Nanotechnology. 28:195702
Huang L, Li J (2016) Tunable electronic structure of black phosphorus/blue phosphorus van der Waals p-n heterostructure. Applied Physics Letters. 108:083101
Tian X-Q, Wang X-R, Wei Y-D, Liu L, Gong Z-R, Gu J, Du Y, Yakobson BI (2017) Highly tunable electronic structures of phosphorene/carbon nanotube heterostructures through external electric field and atomic intercalation. Nano Lett. 17:7995–8004
Acknowledgements
The authors are grateful to Dr. Xiaodong Yang from Nanjing University, Prof. Shengzhan Lu and Prof. Tianxing Wang from Henan Normal University for their help on the DFT calculation. This work is supported by the High-Performance Computing Center of Henan Normal University.
Funding
This work is supported by the NSFC nos. 11404100 and 11304083, the Young Scholar Foundation of Henan Normal University no. 5101029470616, and the surplus foundation for vertical scientific research projects of Henan Normal University no. 5201029120301. This work is also supported by the China Scholarship Council (nos. 201608410308 and 201608410415).
Availability of Data and Materials
The datasets generated during and/or analyzed during the current study are available from the corresponding author on request.
Author information
Authors and Affiliations
Contributions
JG and ZZ designed the simulation, analyzed the data, and wrote the paper. HL, HW, and CL checked the manuscript. All authors read and approved the final manuscript.
Corresponding author
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Guo, J., Zhou, Z., Li, H. et al. Tuning Electronic Properties of Blue Phosphorene/Graphene-Like GaN van der Waals Heterostructures by Vertical External Electric Field. Nanoscale Res Lett 14, 174 (2019). https://doi.org/10.1186/s11671-019-2999-6
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s11671-019-2999-6