Abstract
Fine BaZrO3 and BaHfO3 powders have been prepared by a microwave-assisted hydrothermal (MWHT) process. The powders have been characterized by x-ray diffraction and scanning electron microscopy, and their particle size distribution has been assessed from dynamic light scattering data. The results indicate that microwave processing during hydrothermal synthesis notably reduces the average particle size of the resulting powder and ensures a narrower particle size distribution. BaHfO3 particles prepared under the optimal MWHT synthesis conditions are predominantly spherical in shape and uniform in size, with an average size (1.2 μm) a factor of 2.5 smaller in comparison with particles prepared by a conventional hydrothermal process (2.9 μm).
Similar content being viewed by others
References
Zhang, J.L. and Evetts, J.E., BaZrO3 and BaHfO3: Preparation, Properties, and Compatibility with YBa2Cu3O7−x , J. Mater. Sci., 1994, vol. 29, no. 3, pp. 778–785.
Erb, A., Walker, E., and Flükiger, R., The Use of BaZrO3 Crucibles in Crystal Growth of the High-Tc Superconductors: Progress in Crystal Growth As Well As in Sample Quality, Phys. C (Amsterdam, Neth.), 1996, vol. 258, pp. 9–20.
Liang, R., Bonn, D.A., and Hardy, W.N., Growth of High Quality YBCO Single Crystals Using BaZrO3 Crucibles, Phys. C (Amsterdam, Neth.), 1998, vol. 304, pp. 105–111.
Byrappa, K. and Yoshimura, M., Handbook of Hydrothermal Technology, New York: William Andrew, 2001.
Kolen’ko, Yu.V., Burukhin, A.A., Churagulov, B.R., et al., Hydrothermal Synthesis of Different Nanocyrstalline ZrO2 and TiO2 Polymorphs, Zh. Neorg. Khim., 2002, vol. 47, no. 11, pp. 1755–1762.
Cheng, H.-M., Wu, L.-J., Ma, J.-M., et al., The Effects of pH and Alkaline Earth Ions on the Formation of Nanosized Zirconia Phases under Hydrothermal Conditions, J. Eur. Ceram. Soc., 1999, vol. 19, no. 8, pp. 1675–1681.
Burukhin, A.A., Churagulov, B.R., Oleinikov, N.N., et al., Synthesis of Nanocrystalline Ferrite Powders in Hydrothermal and Supercritical Solutions, Zh. Neorg. Khim., 2001, vol. 46, no. 5, pp. 735–741.
Katsuki, H. and Komarneni, S., Microwave-Hydrothermal Synthesis of Monodispersed Nanophase α-Fe2O3, J. Am. Ceram. Soc., 2001, vol. 84, no. 10, pp. 2313–2317.
Komarneni, S., Roy, R., and Li, Q., Microwave-Hydrothermal Synthesis of Ceramic Powders, Mater. Res. Bull., 1992, vol. 27, no. 12, pp. 1393–1405.
Komarneni, S., Li, Q., Steffansson, K.M., and Roy, R., Microwave-Hydrothermal Processing for Synthesis of Electroceramic Powders, J. Mater. Res., 1993, vol. 8, no. 12, pp. 3176–3183.
Liu, F., Abothu, I.R., and Komarneni, S., Barium Titanate Ceramics Prepared from Conventional and Microwave Hydrothermal Powders, Mater. Lett., 1999, vol. 38, pp. 344–350.
Komarneni, S., D’Arrigo, M.C., Leonelli, C., et al., Microwave-Hydrothermal Synthesis of Nanophase Ferrites, J. Am. Ceram. Soc., 1998, vol. 81, no. 11, pp. 3041–3043.
Komarneni, S., Menon, V.C., Li, Q.H., et al., Microwave-Hydrothermal Processing of BiFeO3 and CsAl2PO6, J. Am. Ceram. Soc., 1996, vol. 79, no. 5, pp. 1409–1412.
Kumada, N., Kinomura, N., and Komarneni, S., Microwave-Hydrothermal Synthesis of ABi2O6 (A = Mg, Zn), Mater. Res. Bull., 1998, vol. 9, pp. 1411–1414.
Vivekanandan, R., Philip, S., and Kutty, T.R.N., Hydrothermal Preparation of Ba(Ti,Zr)O3 Fine Powders, Mater. Res. Bull., 1987, vol. 22, no. 1, pp. 99–108.
Zheng, W., Liu, C., Yue, Y., and Pang, W., Hydrothermal Synthesis and Characterization of BaZr1−x MxO3−a (M = Al, Ga, In, x ≤ 0.20) Series Oxides, Mater. Lett., 1997, vol. 30, no. 1, pp. 93–97.
Phule, P.P. and Grundy, D.C., Pathways for the Low Temperature Synthesis of Nano-sized Crystalline Barium Zirconate, Mater. Sci. Eng., B, 1994, vol. 23, pp. 29–35.
Kolen’ko, Yu.V., Burukhin, A.A., Churagulov, B.R., et al., On the Possibility of Preparing Fine-Particle Barium Zirconate by Hydrothermal Synthesis, Neorg. Mater., 2002, vol. 38, no. 3, pp. 320–324 [Inorg. Mater. (Engl. Transl.), vol. 38, no. 3, pp. 252–255].
Dias, A. and Ciminelli, V.S.T., Electroceramic Materials of Tailored Phase and Morphology by Hydrothermal Technology, Chem. Mater., 2003, vol. 15, no. 6, pp. 1344–1352.
Kolen’ko, Yu.V., Meskin, P.E., Mukhanov, V.A., et al., Effect of the Nature of the Cation on the Phase Composition of Nanocrystalline Titania-like Dioxides Prepared by Hydrothermal Processing of Amorphous Hydroxide Gels, Zh. Neorg. Khim., 2005, vol. 50, no. 12, pp. 1941–1946.
Vukalovich, M.P. and Rivkin, S.L., Teplofizicheskie svoistva vody i vodyanogo para (Thermophysical Properties of Water and Water Vapor), Moscow: Energiya, 1971.
Microwave-Enhanced Chemistry, Kingston, H.M. and Haswell, S.J., Eds., Washington, DC: American Chemical Society, 1997.
Bondioli, F., Ferrari, A.M., Leonelli, C., et al., Microwave-Hydrothermal Synthesis of Nanocrystalline Zirconia Powders, J. Am. Ceram. Soc., 2001, vol. 84, no. 11, pp. 2728–2730.
Author information
Authors and Affiliations
Corresponding author
Additional information
Original Russian Text © V.D. Maksimov, P.E. Meskin, B.R. Churagulov, 2007, published in Neorganicheskie Materialy, 2007, Vol. 43, No. 9, pp. 1102–1108.
Rights and permissions
About this article
Cite this article
Maksimov, V.D., Meskin, P.E. & Churagulov, B.R. Microwave-assisted hydrothermal synthesis of fine BaZrO3 and BaHfO3 powders. Inorg Mater 43, 988–993 (2007). https://doi.org/10.1134/S0020168507090142
Received:
Issue Date:
DOI: https://doi.org/10.1134/S0020168507090142