Abstract
It is well-known that in neutral and acidic aqueous electrolytes, MoS2 monolayers can store charges by adsorption of cations on to the electrode-electrolyte interface as its analog of graphene. Restricted by its low conductivity and the charge storage mechanism, the electrochemical performance of MoS2 monolayer supercapacitor electrode is not satisfactory. It is reported here that water bilayers absorbed on MoS2 monolayers can be involved in charge storage. One proton of each absorbed water molecule can intercalate/de-intercalate the water bilayers during charging/discharging in the alkaline aqueous electrolyte. For two water molecules are present for every Mo atom, the water bilayers can endow MoS2 monolayers an ultrahigh specific capacitance. In this paper, 1T phase MoS2 nanosheets with three monolayers were synthesized by hydrothermal reaction. It presents a specific capacitance of 1120 F g−1 at a current density of 0.5 A g−1 in KOH. As it is assembled with active carbon into a hybrid supercapacitor, the device has an energy density of 31.64 Wh kg−1 at a power density of 425 W kg−1, and gets a specific capacitance retention of 95.4% after 10,000 cycles at 2 A g−1.
Similar content being viewed by others
Introduction
The development of renewable energy storage devices is one of the most promising ways to address the current energy crisis along with the global environmental concern and pushes scientific communities to search for sustainable energy storage technologies1,2. Among the various realistic solutions, energy can in particular be stored electrochemically in batteries and supercapacitors. Batteries present a high energy density, which can keep our devices working throughout the day3. Supercapacitors, owning to their high power density and long cycle life, have wild applications in regenerative braking and loading leveling system of cars and electric mass transit vehicles that would otherwise lose their braking energy as heat4. During the past several years, many researchers have engaged to find ideal electrode materials which might combine the high energy density of batteries and the short charging time of supercapacitors, as shown in Fig. 15,6. Obviously, electric vehicles (EV) equipped with such devices would have short charging time, excellent acceleration performance and grade ability, and long cruising mileage, which may be as efficient and convenient as traditional internal-combustion engine vehicles but more eco-friendly. While some researchers tend to approach these goals by increasing the power density of batteries (for instance, many nanostructured lithium-ion battery electrode materials show improved rate performance for the diffusion paths in the solid electrode materials are shortened7), the other researchers tend to approach these goals by increasing the energy density of supercapacitors (lots of nanoscaled Ni(OH)2 analogous materials which are generally cathode materials of Ni-MH batteries have been applied in C//Ni(OH)2-based hybrid supercapacitors and achieved very high energy density comparable to lithium-ion batteries8,9). Supercapacitors, also known as electrochemical double layer capacitors (EDLCs), store charge by adsorption of electrolyte ions on to the electrode–electrolyte interface6. In order to achieve full utilization of electrode materials, many methods have been applied on carbon materials (enhancing the specific surface area, optimizing the porous structure and morphology10,11) to enhance the proportion of the accessible surface atoms in electrode materials. Thus, single wall carbon nanotubes and graphene, of which all atoms are on the surface, have been considered as promising electrodes for supercapacitors, and capacitances around 100 to 200 F g−1 have been achieved on such materials12,13,14,15. Besides the accessible surface atoms, near-surface atoms of pseudocapacitance materials are also involved in energy storage process. They display much higher specific capacitance than EDLCs for more proportion atoms in such materials contribute to charge storage. A new type of charge storage mechanism for supercapacitors, intercalation pseudocapacitance, was reported recently16,17,18. Cations intercalate/de-intercalate the bulk of the active materials, but doesn’t cause phase transition and is not limited by the bulk diffusion of cations18. Compared to EDLCs and pseudocapacitance, bulk atoms, besides surface atoms and/or near-surface atoms, in electrode materials can be used to store charge. Thus the highest utilization of electrode materials endows intercalative pseudocapacitance with the highest specific capacitance. Generally speaking, the utilization and efficiency of each atom in electrode materials determine the unit of capacity (mAh g−1). Theoretically, each atom of battery electrode materials can be used, although in a low rate mode, so that they present the highest unite of capacity. That is to say, the ideal electrode materials which can fast charge/discharge a huge amount of charges as shown in Fig. 1 may also combine the charge storage mechanisms of both battery and capacitor. It needs battery reaction (intercalation/de-intercalation of ions into/from the matrix) to enhance the capacity, meanwhile it also needs the capacitor reaction close to surface in order to enhance charging/discharging rate.
Two-dimensional transition–metal dichalcogenides have emerged as a fascinating new class of materials for wild applications19,20,21. Among them, the ultrathin MoS2 nanosheets (a new inorganic graphene analog) have recently evoked enormous research enthusiasm as electronics/optoelectronics22,23, sensors24, energy-storage and conversion devices25,26,27. However, the very low conductivity of the trigonal prismatic (labeled as 2H) phase MoS2 monolayers, which is thermodynamically stable, put sands in the wheels of their application as supercapacitors19. 2H-MoS2 monolayers can also store charges by interfacial adsorption as the analog of graphene. But the capacitance is much inferior to graphene28,29,30 for the conductivity (10–6–10–5 S cm−1) is much lower than that of graphene (~100 S cm−1)26. In order to improve the electrochemical performance, the 2H-MoS2 monolayers was even composited with graphene or CNTs to ameliorate the conductivity, and with pseudocapacitive materials such as polypyrrole to enhance the capacitance31,32,33,34. The octahedral (labeled as 1T) phase MoS2 monolayers, which is a thermodynamically metastable isomer of 2H phase, is 107 times more conductive than the semiconducting 2H phase19,35,36. Thus, the capacitor electrode composed of 1T-MoS2 monolayers presented impressive electrochemical performance and very high capacitance26. It has been reported and evidenced by X-ray diffraction for decades that as MoS2 monolayers are in aqueous solution, a new phase is obtained where two water monolayers are present and sandwich the MoS2 monolayers37,38. However, according to the recent reports on MoS2 monolayer supercapacitors using neutral and acidic aqueous electrolytes, they don’t contribute to, or even affect, the charge storage mechanism and performance26. It is reported in this paper that as tested in alkaline aqueous solution, the water bilayers can endow the MoS2 nanosheets, both metallic 1T phase and semiconducting 2H phase, a superior electrochemical energy storage performance. The charge storage mode also changes from low-energy EDLC mode to high-energy battery-type mode. The electrode materials composed of self-assembled rose-like metallic 1T phase MoS2 nanosheets present a very high specific capacitance (1120 F g−1) at 0.5 A g−1. This is the highest value for pure MoS2 as far as we know. The MoS2 nanosheets as a cathode were assembled with active carbon to form a MoS2//AC hybrid supercapacitor. Owning to the high capacitance of the 1T-MoS2 and the wide voltage window, the hybrid capacitor shows an impressive energy density of 31.64 Wh kg−1 in KOH aqueous electrolyte, which is even comparable to traditional lithium-ion batteries. The phenomenon reported in this paper is sure to expand the application of MoS2 nanosheets in electrochemical energy storage.
Results and Discussion
Characterizations
The morphology of the as-prepared MoS2 nanosheets was carefully observed by FESEM and TEM, and the corresponding images are shown in Fig. 2. The nanosheets are wrinkled, and have a diameter of 100 nm and a thickness of 6 nm, as shown in Fig. 2b,c. The wrinkled sheets are self-assembled into rose-like spherical particles with a diameter of about 800 nm, leaving millions of nanopores between them. The interference fringes of the nanosheets were clearly shown in the HRTEM image of Fig. 2e. The spacing between each fringe is 0.63 nm, corresponding to the spacing of MoS2 (002) crystal plane. For the spacing of (002) crystal plane is half of (001) crystal plane and each sheet contains 4–8 interference fringes of (002) crystal plane, each sheet has 2 to 4 MoS2 monolayers. The ultrathin structure of the nanosheets results in a low crystallinity indicated by the Debye-Scherrer ring in the inset of Fig. 2d. However, the ultrathin and wrinkled nanosheets endow the rose-like nanoparticles a high BET specific surface area (54.7 m2 g−1), as shown in Fig. S4. According to the BJH pore-size distribution results in the inset of Fig. S4, the nanopores between the nanosheets in the rose-like particles have a very wide size distribution from 20 to 80 nm.
The phase structure of the MoS2 nanosheets was further investigated by Raman spectroscopy, because Raman spectrum is very sensitive to the symmetry of the sulfur in the matrix and effective to differentiate 1T-MoS2 and 2H-MoS239,40. As shown in Fig. 2f, besides the depressed typical Raman shifts at 378.3 and 401.1 cm−1 for \({{\rm{E}}}_{2{\rm{g}}}^{1}\) and A1g of MoS2, obvious Raman shifts appear at 146, 219 and 333 cm−1 in the spectrum of the as-prepared sample, which is associated with the phonon modes in 1T-MoS241,42. It implies that the as-prepared nanosheets contain lots of 1T phase. However, only \({{\rm{E}}}_{2{\rm{g}}}^{1}\) and A1g appear in the spectrum of the annealed MoS2, indicating the total transition of the 1T-MoS2 to 2H-MoS2 after annealing26. The number of the monolayers in MoS2 film can be calculated by the Raman frequency difference between A1g and \({{\rm{E}}}_{2{\rm{g}}}^{1}\) modes43. It is about 22.8 cm−1, indicating that the sheet has three monolayers according the ref.43. This result is consistent with the HRTEM observation. The 1T and 2H phase compositions in the MoS2 nanosheets were further identified by XPS. Two predominant peaks Mo and S appear in the survey spectrum of Fig. 2g. The S to Mo atomic ratio of the as-prepared MoS2 nanosheets is ~2.1 according to the XPS element detection. It has been reported that 1T phase can cause ~1 eV chemical shifts to lower binding energy on both Mo 3d peaks and S 2p peaks44. So the high-resolution XPS of Mo 3d peaks and S 2p peaks were investigated and the corresponding spectra are shown in Fig. 2h and S5, respectively. As shown in the high-resolution XPS spectrum of Mo 3d peaks in Fig. 2h, the Mo 3d spectra consist of two peaks located at 228.0 and 231.1 eV corresponding to Mo4+ 3d5/2 and 3d3/2 components of 1T-MoS2, respectively26. Both peaks are accompanied by weak shoulders at higher binding energies of 229.0 and 232.1 eV, which are the typical sites for Mo4+ 3d5/2 and Mo4+ 3d3/2 of 2H-MoS2. The high-resolution XPS spectrum of S 2p peaks in Fig. S5 also implies a plenty of 1T-MoS2 in the rose-like particles. The relative content of 1T phase components in the as-prepared MoS2 nanosheets was calculated to be about ~78.0% according to the relative peak height of Mo 3d peaks in Fig. 2h.
Electrochemical analysis
The capacitive behavior of the 1T-MoS2 electrode was firstly investigated in 3 M KCl electrolyte in a potential window of −1.05 to −0.3 V using CV measurement in a three-electrode configuration where SCE and Pt plate served as the reference and counter electrodes, respectively. As shown in Fig. 3a, the resulting CV curve in KCl presents a horizontal straight line without any redox peaks. We substituted Cl− with SO42− in electrolyte and further investigated the capacitive behavior in 0.5 M K2SO4 aqueous solution. The CV curve remains the same and is overlapped with the one in KCl. It implies that anion substitute in electrolyte has no effect on the capacitive behavior of the 1T-MoS2 electrode. The capacitive behavior of the 1T-MoS2 electrode is totally determined by cation adsorption (here is K+ in both electrolytes) on the electrode-electrolyte interface. However, as the anion is further substituted by OH− and the CV method is carried out in 3 M KOH, the resulting CV curve is changed to battery-type: a typical anodic peak occurred at 0.53 V and a typical cathodic reduction peak occurred at 0.33 V are detected in the potential window of 0 to 0.75 V, respectively. The area encircled by the CV curve is dramatically enlarged compared to that in K2SO4 and KCl, which indicates a higher specific capacitance. A straight substitution of K+ for Na+ doesn’t cause any further change on the CV curve. As shown in Fig. 3a, the CV curve tested in KOH overlaps the one tested in NaOH. It implies that the capacitive behavior tested in alkaline aqueous electrolyte is determined by OH− and has no relationship with the kind of cation. The CV curves at various scan rates in KOH (Fig. 3b) also indicate that a battery-type charge storage behavior happens in the 1T-MoS2 electrode. The potential difference between the anodic peaks and the cathodic peaks on the CV curves becomes larger and larger with scan rates. What’s more, it is very obvious in the inset of Fig. 3b that the relationship between the current density (i) at a fixed potential and the scan rate (v) is presented by i = avb, and b is close to 0.545. The GCD measurements also support this point of view. As the electrodes are tested in KCl, the obtained curves show quasi-triangular shapes, which reflect the charge accumulation process with voltage as an EDLC (Fig. 3c). As the electrodes are tested in KOH, the obtained curves always show a plateau at a certain voltage, which is a general phenomenon in batteries and reflects the phase-transformation reactions in batteries (Fig. 3d). The transition of charge storage mechanism in alkaline electrolyte is not the unique phenomenon belonging to 1T-MoS2 nanosheets. After 4 hours annealing at 800 °C, 1T-MoS2 nanosheets can transform into 2H-MoS2 nanosheets26, as proved by the Raman spectrum in Fig. 2f 41. The transition of charge storage mechanism is also found on 2H-MoS2 electrode, as shown in Fig. S7. As the scan rate increases up to 400 mV s−1, the shape of the CV curves tested in KCl (Fig. S6b) and K2SO4 (Fig. S6c) retain their quasi-rectangular shape, but the potential difference between the anodic peaks and the cathodic peaks on the CV curves tested in KOH (Fig. 3b) and NaOH (Fig. S6a) become larger and larger. The specific capacitance was calculated based on the CV measurement and the trends of the specific capacitance with scan rate are summaries in Fig. S6d. It is very clear in this plot that the curves tested in OH− electrolytes (KOH and NaOH) overlap with each other very well and the curves tested in neutral K+ electrolytes (KCl and K2SO4) also overlap with each other very well. However, the curves tested OH− electrolytes are dramatically larger than that in neutral K+ electrolytes. And similar phenomenon is also found in 2H-MoS2 electrode (Fig. S7f). Those phenomena further testify OH− can take change on charge storage ability and behavior of MoS2 in aqueous electrolyte. The plots in Fig. S6d imply that OH− electrolytes can endow the MoS2 a much higher specific capacitance in a wide range of scan rates, although it will descend more dramatically than that in neutral K+ electrolytes.
The capacitance of the 1T-MoS2 electrode was further verified by GCD measurement in KCl (Fig. 3c) and KOH (Fig. 3d) electrolytes within a current density ranging from 0.5 to 20 A g−1, respectively. The discharging time of the electrodes in both electrolytes decline as the current density increases from 0.5 to 20 A g−1. But at a certain current density, the discharging time of the electrode in KOH is always longer than that in KCl. The specific capacitance of the MoS2 electrode in both KOH and KCl electrolytes at different current density was calculated based on the GCD measurements, and the results are summarized in Fig. 3e. Benefiting from the good conductivity of 1T phase, the MoS2 electrode in KCl presents a very high specific capacitance of 483 F g−1 at 0.5 A g−1. It is higher than most of the pure MoS2 nanosheets electrodes, as shown in Fig. 4 28,34,46,47,48,49,50,51,52, including the 1T phase MoS2 monolayer electrode which is 130 F g−1 in H2SO426. But the specific capacitance in KOH is even higher. It reaches as high as 1120 F g−1 at 0.5 A g−1, which is the highest value for pure MoS2 so far. As the current density increases 40 times to 20 A g−1, 57.9% of the specific capacitance in KOH (648 F g−1) is retained, compared to 62.3% in KCl (300 F g−1). Although the specific capacitance in KOH declines more dramatically than that in KCl, it is always higher than that in KCl at each current density. In the end, it is still more than twice as much as that in KCl. In fact, the specific capacitance in KOH is higher than any reported specific capacitance of MoS2 related electrodes, even as MoS2 was composited with some pseudocapacitive materials with high specific capacitance or with some EDLC materials with high conductivity such as graphene, CNTs and so on, as shown in Fig. 4 28,34,46,47,48,49,50,51,52. The cyclability of the 1T-MoS2 electrodes in both in KOH and KCl electrolytes was tested at a current density of 10 A g−1 over 2,000 cycles. The electrodes retained a capacitance of 96% in KOH and of 94% in KCl after 2,000 cycles, as shown in Fig. 3f. The charge transfer characteristics of the MoS2 electrodes in both KCl and KOH electrolytes were studied by EIS within the frequency range of 106 and 10−2 Hz. And the corresponding Nyquist plots are shown in Fig. S8. The intersecting point of a small semicircle with real axis represents internal resistance (Rs) and its diameter represents interfacial charge transfer resistance (Rct)53,54. The Rs of MoS2 electrodes in both electrolytes are very close, about 0.3 Ω in KOH and 0.4 Ω in KCl. But the Rct in KCl (0.6 Ω) is twice the one in KOH (0.3 Ω).
In order to uncover the charge storage mechanism, the crystallographic structure of the 1T-MoS2 nanosheets at four different states (dried, wetted, wetted after charging in KOH and wetted after charging in KCl) were characterized by XRD, and the corresponding XRD spectra are shown in Fig. 5a. The dried MoS2 nanosheets present a typical powder diffraction pattern which matches very well with the standard powder diffraction file JCPDS card #37-1492. After it is wetted by aqueous solution, two dramatic diffraction peaks at 2θ of 9.77° and 19.17° appeared instead of (002) peak of MoS2 in the spectrum. These two peaks have been reported for decades. They belong to the water bilayers sandwiching MoS2 layers37, as denoted by the labels in the spectrum. The number of water molecules in the water bilayers was carefully investigated by weighing measurment in the ref.37, and it is found that two water molecules are present for every Mo atom. After charging in KOH, both water peaks slightly shift to high 2θ, at 2θ of 10.25° and 19.65°, respectively. This shift indicates constriction of water bilayers. The spacing of water bilayer (001) plane decreases by 0.43 Å from 9.05 Å to 8.62 Å. However, the water peaks are totally disappeared in the spectrum of wetted MoS2 nanosheets charged in KCl. Based on the electrochemical measurements and XRD characterization, we speculate that in the alkaline aqueous electrolyte, the water bilayers in wetted MoS2 nanosheets are involved in the charge storage process following the below equation:
And the corresponding charge storage process is schematically illustrated by Fig. 5b. A water monolayer should be absorbed on each side of MoS2 monolayer as it is wetted by an aqueous solution. And each S atom in the MoS2 monolayer should absorb one H2O molecule. During charging, a proton would be pulled away from each H2O molecule, which of course leads to the constriction of water bilayers. The proton could also return during the discharging process, as shown in Fig. 5b. That is to say, MoS2 can store charge analogous to aqueous Ni-MH battery electrode materials such as Ni(OH)2 and Co(OH)255. The charge storage of MoS2 in alkaline aqueous solution mainly depends on the intercalation/de-intercalation of proton within the water bilayers. However, the MoS2 monolayer may be the fastest battery for proton needn’t diffuse within the crystalline framework during charging/discharging process. We also calculated the theoretical specific capacitance according to equation (1) assuming a potential window of 0.75 V, which is 1607 F g−1. The measured value of GCD measurement in KOH at 0.5 A g−1 is very close to, but still below, the theoretical value. The absorption may be very weak. The vanishment of water peaks in the XRD pattern after charging in KCl, as shown in Fig. 5a, implies that cation absorption on the MoS2 monolayer can effectively destroy the water bilayers.
Electrochemical performance of the MoS2//AC hybrid supercapacitor device
To further evaluate the MoS2 electrode for practical applications, a hybrid supercapacitor device was fabricated using the MoS2 as positive electrode and AC as negative electrode in 3M KOH aqueous electrolyte (denoted as MoS2//AC), as schematically illustrated by Fig. 6a. The CV curves of the device in Fig. 6b exhibit close EDLC properties, indicating a capacitor behavior. And the CV curves didn’t show obvious distortion at the scan rate up to 400 mV s−1, demonstrating a good rate character. The GCD curves of the device at a current density ranging from 0.5 to 20 A g−1 in a potential window of 1.7 V in Fig. 6c also present analogous triangular shape. The specific capacitance based on GCD measurements is summarized in Fig. 6d. The specific capacitance presents a very high value of 78.82 F g−1 at a current density of 0.5 A g−1, corresponding to an energy density of 31.64 Wh kg−1 at a power density of 425 W kg−1, which is comparable to the Nickel hydroxide related composite electrodes in reports (Table S1)8,56,57,58,59,60,61,62,63,64,65,66,67,68,69,70,71,72,73,74,75. The GCD measurements at 2 A g−1 were also performed on this device up to 10,000 cycles, and the corresponding evolution of the capacitance and coulombic efficiency is shown in Fig. 6e. And a section of the GCD curve close to the end is also shown in the inset. After initial hundreds of cycles, both the capacitance and coulombic efficiency enters into a relatively stable stage. After 10,000 cycles, the GCD curves still remain their quasi-triangular shape, and the device still possesses a great specific capacitance retention of 95.4%.
Conclusion
In conclusion, three-layer 1T phase MoS2 nanosheets were fabricated via a one-pot facial hydrothermal reaction in this paper. These nanosheets were self-assembled into rose-like nanoparticles. It is demonstrated that in alkaline aqueous electrolyte the water bilayers absorbed on MoS2 layers can contribute to energy storage by proton intercalation/de-intercalation. During charging, a proton will break away from every water molecule in the water bilayers. During discharging, the proton will come back to form water molecules and water bilayers again. The proton intercalation/de-intercalation process endows MoS2 a very high capacity. The theoretical unit of capacity for MoS2 was calculated to be 334 mAh g−1. For a potential window of 0.75 V, it is corresponding to a capacitance of 1607 F g−1. Thus, in alkaline electrolyte, the as-prepared 1T phase MoS2 nanosheets can present an ultrahigh special capacitance of 1120 F g−1 at a discharge current density of 0.5 A g−1. As the pure 1T phase MoS2 nanosheets were assembled into MoS2//AC hybrid supercapacitor device, it presented a high energy density of 31.64 Wh kg−1 at a power density of 425 W kg−1, which is comparable to the Nickel hydroxide related composite electrodes in reports. The research in this paper is sure to expand the application of MoS2 nanosheets in electrochemical energy storage.
Experimental Section
Chemicals
Molybdenum (VI) oxide powder (MoO3), thioacetamide, urea and sodium chloride (NaCl) were purchased from Sinopharm Chemical Reagent Co., Ltd. All solvents and chemicals regents in the present work were of analytical grade and used without further purification.
Method
First, 12 mg of MoO3 was dissolved in 10 ml of deionized water and stirred intensively for 10 min. Then 14 mg of thioacetamide, 0.12 g of urea and 0.68 g of NaCl were added to the above solution successively and stirred vigorously for another 2 h to form a homogeneous solution. Then the solution was transferred to a 50 ml Teflon lined stainless steel autoclave and loaded into an electric oven at 200 °C for 12 h. Finally, the black precipitate was collected by centrifuging, thoroughly washing with deionized water several times and freeze-drying. A part of the hydrothermal product was annealed in a tube furnace at 800 °C for 4 h in a nitrogen atmosphere for comparison.
Characterization
The crystallography was investigated by X-ray diffractometer (XRD, Rigaku D/max 2500 pc, Cu Kα radiation: λ = 1.5406 Å). The morphology was characterized by field emission scanning electron microscopy (FESEM, JEOL JSM-6700F) and transmission electron microscopy (TEM, JEOL 2100F, 200 KV). The Micromeritics ASAP 2020 analyzer was used to determine the Brunauer-Emmett-Teller (BET) surface area and Barrett-Joyner-Halenda (BJH) porosities. The Raman spectra were obtained on WITec CRM200 confocal Raman microscopy system (WITec, Germany) with a laser wavelength of 488 nm. X-ray photoelectron spectroscopy (XPS) spectra were obtained on an ESCALAB Mk II (Vacuum Generators) spectrometer with monochromatized Al Kα X-rays (240 W).
Electrochemical measurements
All the electrochemical measurements were performed with an electrochemical workstation (Princeton Applied Research). The working electrode was prepared by mixing the prepared active material, acetylene black and polyvinylidene fluoride (PVDF) binder in a weight ratio of 80:15:5 with N-methyl-2-pyrrolidinone (NMP) as a solvent. The resulting slurry was cautiously pasted onto a clean nickel foam (1 cm × 1 cm) substrate with a mass loading of 2.0 mg cm−2, and dried at 80 °C for 12 h in a vacuum. For three-electrode measurements, a platinum plate (Pt) was used as the counter electrode, and a saturated calomel electrode (SCE) was used as the reference electrode. Four electrolytes including 3 M KOH, 3 M NaOH, 3 M KCl, 0.5 M K2SO4 were used for comparison. Electrochemical impedance spectroscopy (EIS) measurements were performed in a frequency range from 0.01 to 100 kHz with 5 mV amplitude.
The hybrid supercapacitor was assembled into a device using the as-synthesized MoS2 electrode as the positive electrode, a commercial activated carbon (AC) electrode as the negative electrode and one piece of cellulose paper as a separator in 3 M KOH electrolyte. The preparation of the negative electrode was similar to that of the positive electrode. The mass ratio of MoS2 on the positive electrode to AC on the negative electrode was decided according to the well-known charge balance theory (q+ = q−). The charge stored (q) by each electrode depends on the following equation9:
where C (F g−1) is the specific capacitance of the electrode, ∆V (V) is the potential window and m (g) is the mass loading. In order to get q+ = q−, the mass balancing will follow the equation9.
Based on analysis of the potential windows and the specific capacitances of the MoS2 and AC electrodes from cyclic voltammograms (CVs) in Fig. S1 and galvanostatic charge-discharge curves (GCD) in Fig. S2, the optimal mass ratio of the positive electrode to the negative electrode was about 0.24 (the mass loading of the positive electrode is 2.0 mg cm−2 and that of the negative electrode is 8.3 mg cm−2). The electrochemical performance of the AC electrode in a three-electrode system in 3 M KOH is shown in Fig. S3. The calculation methodology on special capacitance, coulombic efficiency, energy density and power density were also shown in the supporting information.
References
Chu, S. & Majumdar, A. Opportunities and challenges for a sustainable energy future. Nature 488, 294–303, https://doi.org/10.1038/nature11475 (2012).
Dunn, B., Kamath, H. & Tarascon, J.-M. Electrical Energy Storage for the Grid: A Battery of Choices. Science 334, 928–935, https://doi.org/10.1126/science.1212741 (2011).
Wang, X., Weng, Q., Yang, Y., Bando, Y. & Gotberg, D. Hybrid two-dimensional materials in rechargeable battery applications and their microscopic mechanisms. Chem. Soc. Rev. 45, 4042–4073, https://doi.org/10.1039/c5cs00937e (2016).
Miller, J. R. & Simon, P. Materials science-Electrochemical capacitors for energy management. Science 321, 651–652, https://doi.org/10.1126/science.1158736 (2008).
Service, R. F. Materials science-New ‘supercapacitor’ promises to pack more electrical punch. Science 313, 902–902, https://doi.org/10.1126/science.313.5789.902 (2006).
Wei, W., Cui, X., Chen, W. & Ivey, D. G. Manganese oxide-based materials as electrochemical supercapacitor electrodes. Chem. Soc. Rev. 40, 1697–1721, https://doi.org/10.1039/c0cs00127a (2011).
Taberna, L., Mitra, S., Poizot, P., Simon, P. & Tarascon, J. M. High rate capabilities Fe3O4-based Cu nano-architectured electrodes for lithium-ion battery applications. Nat. Mater. 5, 567–573, https://doi.org/10.1038/nmat1672 (2006).
Tang, Z., Tang, C.-h & Gong, H. A High Energy Density Asymmetric Supercapacitor from Nano-architectured Ni(OH)2/Carbon Nanotube Electrodes. Adv. Funct. Mater. 22, 1272–1278, https://doi.org/10.1002/adfm.201102796 (2012).
Yan, J. et al. Advanced Asymmetric Supercapacitors Based on Ni(OH)2/Graphene and Porous Graphene Electrodes with High Energy Density. Adv. Funct. Mater. 22, 2632–2641, https://doi.org/10.1002/adfm.201102839 (2012).
Liu, S. et al. Leaf-inspired interwoven carbon nanosheet/nanotube homostructures for supercapacitors with high energy and power densities. J. Mater. Chem. A 5, 19997–20004, https://doi.org/10.1039/c7ta04952h (2017).
Zhang, L. L. & Zhao, X. S. Carbon-based materials as supercapacitor electrodes. Chem. Soc. Rev. 38, 2520–2531, https://doi.org/10.1039/b813846j (2009).
Banda, H. et al. One-step synthesis of highly reduced graphene hydrogels for high power supercapacitor applications. J. Power Sources 360, 538–547, https://doi.org/10.1016/j.jpowsour.2017.06.033 (2017).
Izadi-Najafabadi, A. et al. Extracting the Full Potential of Single-Walled Carbon Nanotubes as Durable Supercapacitor Electrodes Operable at 4 V with High Power and Energy Density. Adv. Mater. 22, E235, https://doi.org/10.1002/adma.200904349 (2010).
Kimizuka, O. et al. Electrochemical doping of pure single-walled carbon nanotubes used as supercapacitor electrodes. Carbon 46, 1999–2001, https://doi.org/10.1016/j.carbon.2008.08.026 (2008).
Liu, C., Yu, Z., Neff, D., Zhamu, A. & Jang, B. Z. Graphene-Based Supercapacitor with an Ultrahigh Energy Density. Nano Lett. 10, 4863–4868, https://doi.org/10.1021/nl102661q (2010).
Brezesinski, T., Wang, J., Tolbert, S. H. & Dunn, B. Ordered mesoporous alpha-MoO3 with iso-oriented nanocrystalline walls for thin-film pseudocapacitors. Nat. Mater. 9, 146–151, https://doi.org/10.1038/nmat2612 (2010).
Brezesinski, K. et al. Pseudocapacitive Contributions to Charge Storage in Highly Ordered Mesoporous Group V Transition Metal Oxides with Iso-Oriented Layered Nanocrystalline Domains. J. Am. Chem. Soc. 132, 6982–6990, https://doi.org/10.1021/ja9106385 (2010).
Augustyn, V. et al. High-rate electrochemical energy storage through Li+ intercalation pseudocapacitance. Nat. Mater. 12, 518–522, https://doi.org/10.1038/nmat3601 (2013).
Subbaiah, Y. P. V., Saji, K. J. & Tiwari, A. Atomically Thin MoS2: A Versatile Nongraphene 2D Material. Adv. Funct. Mater. 26, 2046–2069, https://doi.org/10.1002/adfm.201504202 (2016).
Zhang, X., Lai, Z., Tan, C. & Zhang, H. Solution-Processed Two-Dimensional MoS2 Nanosheets: Preparation, Hybridization, and Applications. Angew. Chem., Int. Ed. 55, 8816–8838, https://doi.org/10.1002/anie.201509933 (2016).
Wang, H., Feng, H. & Li, J. Graphene and Graphene-like Layered Transition Metal Dichalcogenides in Energy Conversion and Storage. Small 10, 2165–2181, https://doi.org/10.1002/smll.201303711 (2014).
Kappera, R. et al. Phase-engineered low-resistance contacts for ultrathin MoS2 transistors. Nat. Mater. 13, 1128–1134, https://doi.org/10.1038/nmat4080 (2014).
Lopez-Sanchez, O., Lembke, D., Kayci, M., Radenovic, A. & Kis, A. Ultrasensitive photodetectors based on monolayer MoS2. Nat. Nanotechnol. 8, 497–501, https://doi.org/10.1038/nnano.2013.100 (2013).
Wu, S. et al. Electrochemically Reduced Single-Layer MoS2 Nanosheets: Characterization, Properties, and Sensing Applications. Small 8, 2264–2270, https://doi.org/10.1002/smll.201200044 (2012).
Stephenson, T., Li, Z., Olsen, B. & Mitlin, D. Lithium ion battery applications of molybdenum disulfide (MoS2) nanocomposites. Energy Environ. Sci. 7, 209–231, https://doi.org/10.1039/c3ee42591f (2014).
Acerce, M., Voiry, D. & Chhowalla, M. Metallic 1T phase MoS2 nanosheets as supercapacitor electrode materials. Nat. Nanotechnol. 10, 313–318, https://doi.org/10.1038/nnano.2015.40 (2015).
Kibsgaard, J., Chen, Z., Reinecke, B. N. & Jaramillo, T. F. Engineering the surface structure of MoS2 to preferentially expose active edge sites for electrocatalysis. Nat. Mater. 11, 963–969, https://doi.org/10.1038/nmat3439 (2012).
Huang, K.-J., Zhang, J.-Z., Shi, G.-W. & Liu, Y.-M. Hydrothermal synthesis of molybdenum disulfide nanosheets as supercapacitors electrode material. Electrochim. Acta 132, 397–403, https://doi.org/10.1016/j.electacta.2014.04.007 (2014).
Wang, L., Ma, Y., Yang, M. & Qi, Y. Hierarchical hollow MoS2 nanospheres with enhanced electrochemical properties used as an Electrode in Supercapacitor. Electrochim. Acta 186, 391–396, https://doi.org/10.1016/j.electacta.2015.10.130 (2015).
Pandey, K., Yadav, P. & Mukhopadhyay, I. Electrochemical and electronic properties of flower-like MoS2 nanostructures in aqueous and ionic liquid media. RSC Adv. 5, 57943–57949, https://doi.org/10.1039/c5ra09282e (2015).
Da Silveira Firmiano, E. G. et al. Supercapacitor Electrodes Obtained by Directly Bonding 2D MoS2 on Reduced Graphene Oxide. Adv. Energy Mater. 4, https://doi.org/10.1002/aenm.201301380 (2014).
Huang, K.-J., Wang, L., Zhang, J.-Z., Wang, L.-L. & Mo, Y.-P. One-step preparation of layered molybdenum disulfide/multi-walled carbon nanotube composites for enhanced performance supercapacitor. Energy 67, 234–240, https://doi.org/10.1016/j.energy.2013.12.051 (2014).
Tang, H. et al. Growth of Polypyrrole Ultrathin Films on MoS2 Monolayers as High-Performance Supercapacitor Electrodes. Adv. Mater. 27, 1117–1123, https://doi.org/10.1002/adma.201404622 (2015).
Huang, K.-J. et al. Synthesis of polyaniline/2-dimensional graphene analog MoS2 composites for high-performance supercapacitor. Electrochim. Acta 109, 587–594, https://doi.org/10.1016/j.electacta.2013.07.168 (2013).
Chhowalla, M. et al. The chemistry of two-dimensional layered transition metal dichalcogenide nanosheets. Nat. Chem. 5, 263–275, https://doi.org/10.1038/nchem.1589 (2013).
Cao, X., Tan, C., Zhang, X., Zhao, W. & Zhang, H. Solution-Processed Two-Dimensional Metal Dichalcogenide-Based Nanomaterials for Energy Storage and Conversion. Adv. Mater. 28, 6167–6196, https://doi.org/10.1002/adma.201504833 (2016).
Joensen, P., Crozier, E., Alberding, N. & Frindt, R. A study of single-layer and restacked MoS2 by X-ray diffraction and X-ray absorption spectroscopy. J. Phys. C: Solid State Phys. 20, 4043 (1987).
Geng, X. et al. Two-Dimensional Water-Coupled Metallic MoS2 with Nanochannels for Ultrafast Supercapacitors. Nano Lett. 17, 1825–1832, https://doi.org/10.1021/acs.nanolett.6b05134 (2017).
Lukowski, M. A. et al. Enhanced Hydrogen Evolution Catalysis from Chemically Exfoliated Metallic MoS2 Nanosheets. J. Am. Chem. Soc.y 135, 10274–10277, https://doi.org/10.1021/ja404523s (2013).
Kang, Y. et al. Plasmonic Hot Electron Induced Structural Phase Transition in a MoS2 Monolayer. Adv. Mater. 26, 6467–6471, https://doi.org/10.1002/adma.201401802 (2014).
Jiménez Sandoval, S., Yang, D., Frindt, R. F. & Irwin, J. C. Raman study and lattice dynamics of single molecular layers of MoS2. Phys. Rev. B 44, 3955–3962 (1991).
Calandra, M. Chemically exfoliated single-laye MoS2: Stability, lattice dynamics, and catalytic adsorption from first principles. Phys. Rev. B 88, 245428 (2013).
Ho, Y.-T. et al. Layered MoS2 grown on c-sapphire by pulsed laser deposition. Phys. Status Solidi-Rapid Res. Lett. 9, 187–191, https://doi.org/10.1002/pssr.201409561 (2015).
Geng, X. et al. Pure and stable metallic phase molybdenum disulfide nanosheets for hydrogen evolution reaction. Nat. Commun. 7, https://doi.org/10.1038/ncomms10672 (2016).
Simon, P., Gogotsi, Y. & Dunn, B. Where Do Batteries End and Supercapacitors Begin? Science 343, 1210–1211, https://doi.org/10.1126/science.1249625 (2014).
Wang, J. et al. Ni3S2@MoS2 core/shell nanorod arrays on Ni foam for high-performance electrochemical energy storage. Nano Energy 7, 151–160, https://doi.org/10.1016/j.nanoen.2014.04.019 (2014).
Yang, C., Chen, Z., Shakir, I., Xu, Y. & Lu, H. Rational synthesis of carbon shell coated polyaniline/MoS2 monolayer composites for high-performance supercapacitors. Nano Res. 9, 951–962, https://doi.org/10.1007/s12274-016-0983-3 (2016).
Ma, G. et al. In situ intercalative polymerization of pyrrole in graphene analogue of MoS2 as advanced electrode material in supercapacitor. J. Power Sources 229, 72–78, https://doi.org/10.1016/j.jpowsour.2012.11.088 (2013).
Ren, L. et al. Three-Dimensional Tubular MoS2/PANI Hybrid Electrode for High Rate Performance Supercapacitor. ACS Appl. Mater. Interfaces 7, 28294–28302, https://doi.org/10.1021/acsami.5b08474 (2015).
Ji, H. et al. Porous Hybrid Composites of Few-Layer MoS2 Nanosheets Embedded in a Carbon Matrix with an Excellent Supercapacitor Electrode Performance. Small 11, 6480–6490, https://doi.org/10.1002/smll.201502355 (2015).
Xie, B. et al. Hydrothermal synthesis of layered molybdenum sulfide/N-doped graphene hybrid with enhanced supercapacitor performance. Carbon 99, 35–42, https://doi.org/10.1016/j.carbon.2015.11.077 (2016).
Weng, Q. et al. Supercapacitive energy storage performance of molybdenum disulfide nanosheets wrapped with microporous carbons. J. Mater. Chem. A 3, 3097–3102, https://doi.org/10.1039/c4ta06303a (2015).
Liu, L., Lang, J., Zhang, P., Hu, B. & Yan, X. Facile Synthesis of Fe2O3 Nano-Dots@Nitrogen-Doped Graphene for Supercapacitor Electrode with Ultralong Cycle Life in KOH Electrolyte. ACS Appl. Mater. Interfaces 8, 9335–9344, https://doi.org/10.1021/acsami.6b00225 (2016).
Zhou, C., Zhang, Y., Li, Y. & Liu, J. Construction of High-Capacitance 3D CoO@Polypyrrole Nanowire Array Electrode for Aqueous Asymmetric Supercapacitor. Nano Lett. 13, 2078–2085, https://doi.org/10.1021/nl400378j (2013).
Deng, T. et al. Atomic-level energy storage mechanism of cobalt hydroxide electrode for pseudocapacitors. Nat. Commun. 8, https://doi.org/10.1038/ncomms15194 (2017).
Wu, P. et al. A Low-Cost, Self-Standing NiCo2O4@CNT/CNT Multilayer Electrode for Flexible Asymmetric Solid-State Supercapacitors. Adv. Funct. Mater. 27, https://doi.org/10.1002/adfm.201702160 (2017).
Li, S. et al. A superhydrophilic “nanoglue” for stabilizing metal hydroxides onto carbon materials for high-energy and ultralong-life asymmetric supercapacitors. Energy Environ. Sci. 10, 1958–1965, https://doi.org/10.1039/c7ee01040k (2017).
Owusu, K. A. et al. Low-crystalline iron oxide hydroxide nanoparticle anode for high-performance supercapacitors. Nat. Commun. 8, https://doi.org/10.1038/ncomms14264 (2017).
Nagaraju, G., Cha, S. M., Sekhar, S. C. & Yu, J. S. Metallic Layered Polyester Fabric Enabled Nickel Selenide Nanostructures as Highly Conductive and Binderless Electrode with Superior Energy Storage Performance. Adv. Energy Mater. 7, https://doi.org/10.1002/aenm.201601362 (2017).
He, W. et al. Ultrathin and Porous Ni3S2/CoNi2S4 3D-Network Structure for Superhigh Energy Density Asymmetric Supercapacitors. Adv. Energy Mater. 7, https://doi.org/10.1002/aenm.201700983 (2017).
Guan, C. et al. Rational Design of Metal-Organic Framework Derived Hollow NiCo2O4 Arrays for Flexible Supercapacitor and Electrocatalysis. Adv. Energy Mater. 7, https://doi.org/10.1002/aenm.201602391 (2017).
Zhu, J. et al. Wearable High-Performance Supercapacitors Based on Silver-Sputtered Textiles with FeCo2S4-NiCo2S4 Composite Nanotube-Built Multitripod Architectures as Advanced Flexible Electrodes. Adv. Energy Mater. 7, https://doi.org/10.1002/aenm.201601234 (2017).
Wang, T. et al. 2-Methylimidazole-Derived Ni-Co Layered Double Hydroxide Nanosheets as High Rate Capability and High Energy Density Storage Material in Hybrid Supercapacitors. ACS Appl. Mater. Interfaces 9, 15510–15524, https://doi.org/10.1021/acsami.7b02987 (2017).
Zhao, Y., Hu, L., Zhao, S. & Wu, L. Preparation of MnCo2O4@Ni(OH)2 Core-Shell Flowers for Asymmetric Supercapacitor Materials with Ultrahigh Specific Capacitance. Adv. Funct. Mater. 26, 4085–4093, https://doi.org/10.1002/adfm.201600494 (2016).
Zhu, Y. et al. Porous NiCo2O4 spheres tuned through carbon quantum dots utilised as advanced materials for an asymmetric supercapacitor. J. Mater. Chem. A 3, 866–877, https://doi.org/10.1039/c4ta05507a (2015).
Su, Y.-Z., Xiao, K., Li, N., Liu, Z.-Q. & Qiao, S.-Z. Amorphous Ni(OH)2 @ three-dimensional Ni core-shell nanostructures for high capacitance pseudocapacitors and asymmetric supercapacitors. J Mater Chem A 2, 13845–13853, https://doi.org/10.1039/c4ta02486a (2014).
Zhu, J. et al. 3D Carbon/Cobalt-Nickel Mixed-Oxide Hybrid Nanostructured Arrays for Asymmetric Supercapacitors. Small 10, 2937–2945, https://doi.org/10.1002/smll.201302937 (2014).
Wang, X., Sumboja, A., Lin, M., Yan, J. & Lee, P. S. Enhancing electrochemical reaction sites in nickel-cobalt layered double hydroxides on zinc tin oxide nanowires: a hybrid material for an asymmetric supercapacitor device. Nanoscale 4, 7266–7272, https://doi.org/10.1039/c2nr31590d (2012).
Wang, X., Liu, W. S., Lu, X. & Lee, P. S. Dodecyl sulfate-induced fast faradic process in nickel cobalt oxide-reduced graphite oxide composite material and its application for asymmetric supercapacitor device. J. Mater. Chem. 22, 23114–23119, https://doi.org/10.1039/c2jm35307e (2012).
Zhu, J. et al. Hydrogenated CoOx nanowire@Ni(OH)2 nanosheet core-shell nanostructures for high-performance asymmetric supercapacitors. Nanoscale 6, 6772–6781, https://doi.org/10.1039/c4nr00771a (2014).
Kong, W., Lu, C., Zhang, W., Pu, J. & Wang, Z. Homogeneous core-shell NiCo2S4 nanostructures supported on nickel foam for supercapacitors. J Mater Chem. A 3, 12452–12460, https://doi.org/10.1039/c5ta02432c (2015).
Yang, B. et al. The growth and assembly of the multidimensional hierarchical Ni3S2 for aqueous asymmetric supercapacitors. Crystengcomm 17, 4495–4501, https://doi.org/10.1039/c4ce02558j (2015).
Hu, W. et al. CoNi2S4 Nanosheet Arrays Supported on Nickel Foams with Ultrahigh Capacitance for Aqueous Asymmetric Supercapacitor Applications. ACS Appl. Mater. Interfaces 6, 19318–19326, https://doi.org/10.1021/am5053784 (2014).
Xu, K. et al. Design and synthesis of 3D interconnected mesoporous NiCo2O4@CoxNi1-x(OH)2 core-shell nanosheet arrays with large areal capacitance and high rate performance for supercapacitors. J. Mater. Chem. A 2, 10090–10097, https://doi.org/10.1039/c4ta01489h (2014).
Wang, H., Gao, Q. & Hu, J. Asymmetric capacitor based on superior porous Ni-Zn-Co oxide/hydroxide and carbon electrodes. J. Power Sources 195, 3017–3024, https://doi.org/10.1016/j.jpowsour.2009.11.059 (2010).
Acknowledgements
This work is supported by the Key Program for International S&T Cooperation Projects of China (2016YFE0132900), Jilin Province Science and Technology Development Project (No. 20180101071JC), the Program for JLU Science and Technology Innovative Research Team (JLUSTIRT, 2017TD-09). Y. Liu is grateful for the financial support by the research grants (No. 51761135110). Q. Jiang acknowledges the financial support by the research grants (No. 51631004). N. Gao acknowledges the financial support by the research grants (No. 11604023).
Author information
Authors and Affiliations
Contributions
R.Z., S.W. and G.W. conceived and designed the study. R.Z. and S.W. performed the experiments. N.G., Y.L., J.L. and Q.J. provided helps in the experiments. R.Z. and G.W. wrote the manuscript and all authors discussed the experiments and final manuscript.
Corresponding author
Ethics declarations
Competing Interests
The authors declare no competing interests.
Additional information
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Zhou, R., Wei, S., Liu, Y. et al. Charge Storage by Electrochemical Reaction of Water Bilayers Absorbed on MoS2 Monolayers. Sci Rep 9, 3980 (2019). https://doi.org/10.1038/s41598-019-40672-w
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-019-40672-w
- Springer Nature Limited
This article is cited by
-
Highly improved supercapacitance properties of MnFe2O4 nanoparticles by MoS2 nanosheets
Scientific Reports (2021)