Abstract
The bone formation around titanium implants with varied surface properties was investigated after 1 year in rabbits. Machined and electropolished samples with and without thick, anodically formed surface oxides were prepared, surface characterized and inserted in the cortical bone of rabbits. Scanning electron microscopy, scanning Auger electron spectroscopy and atomic force microscopy revealed marked differences in oxide thickness, surface topography and roughness, but no significant differences in surface chemical composition between the different groups of implants. Light microscopic morphology and morphometry showed that all implants were in contact with bone and had a large proportion of bone within the threads. There were no significant differences between the differently prepared implant groups. Our study shows that a high degree of bone contact and bone formation is achieved after 1 year with titanium implants which are modified with respect to oxide thickness and surface topography. There is no indication that a reduction of surface roughness, which in the initial phase decreases the rate of bone formation, had any influence on the amount of bone after 1 year in rabbit cortical bone.
Similar content being viewed by others
References
J. C. KELLER, W. M. J. DOUGHERTY, G. R. GROTENDORST and P. J. WIGHTMAN, J. Adhesion 28 (1989) 115.
J. C. KELLER, R. A. DRAUGHN, J. P. WIGHTMAN, W. J. DOUGHERTY and S. D. MELETIOU, Int. J. Oral Maxillofac. 5 (1990) 360.
M. C. SUNNY and P. C. SHARMA, J. Biomed. Mater. Res. 24 (1990) 455.
K. T. BOWERS, J. C. KELLER, B. A. RANDOLPH, D. G. WICK and C. M. MICHAELS, Int. J. Oral Maxillofacial Impl. 7 (1992) 302.
D. R. COOLEY, A. F. VAN DELLEN, J. O. BURGESS and A. S. WINDELER, J. Prosth. Dent. 67 (1992) 93.
P. DUCHEYNE, S. RADIN and L. KING, J. Biomed. Mater. Res. 27 (1993) 25.
J. HAMBLETON, Z. SCHWARTZ, A. KHARE, S. W. WINDELER, M. LUNA, B. P. BROOKS, D. D. DEAN and B. D. BOYAN, J. Orthop. Res. 12 (1994) 542.
J. Y. MARTIN, Z. SCHWARTZ, T. W. HUMMERT, D. M. SCHRAUB, J. SIMPSON, J. J. LANKFORD, D. D. DEAN, D. L. COCHRAN and B. D. BOYAN, J. Biomed. Mater. Res. 29 (1995) 389.
Z. SCHWARTZ, J. Y. MARTIN, D. D. DEAN, J. SIMPSON, D. L. COCHRAN and B. D. BOYAN, ibid. 30(2) (1996) 145.
C. LARSSON, P. THOMSEN, B. O. ARONSSON, M. RODAHL, J. LAUSMAA, B. KASEMO and L. E. ERICSON, Biomaterials 15 (1994) 1062.
B. KASEMO and J. LAUSMAA, Swed. Dent. J. Suppl. 28 (1985) 19.
T. ALBREKTSSON, P.-I. BRÅNEMARK, H.-A. HANSSON, B. KASEMO, K. LARSSON, I. LUNDSTRÖM, D. MCQUEEN and R. SKALAK, Ann. Biomed. Engng 11 (1983) 1.
R. HAZAN, R. BRENER and U. ORON, Biomaterials 14 (1993) 570.
J. C. KELLER, C. M. STANFORD, J. P. WIGHTMAN, R. A. DRAUGN and R. ZAHARIAS, J. Biomed. Mater. Res. 28 (1994) 939.
K. M. SWART, J. C. KELLER, J. P. WIGHTMAN, R. A. DRAUGN, C. M. STANFORD and C. M. MICHAELS, J. Oral Implant. 18 (1992) 130.
B. CHEHROUDI, T. R. L. GOULD and D. M. BRUNETTE, J. Biomed. Mater. Res. 23 (1989) 1067.
Idem, ibid. 24 (1990) 1202.
D. BUSER, R. K. SEHENK, S. STEINEMANN, J. P. FIORELLINI, C. H. FOX and H. STITCH, ibid. 25 (1991) 889.
M. KÖNÖNEN, M. HORMIA, J. KIVILAHTI, J. HAUTANIEMI and I. THESLEFF, J. Biomed. Mater. Sci. 26 (1992) 1325.
M. THERIN, A. MEUNIER and P. CHRISTEL, J. Mater. Sci. Mater. Med. 2 (1991) 1.
J. L. RICCI, J. M. SPIVAK, N. C. BLUMENTHAL and H. ALEXANDER, in “The bone-biomaterial interface”, edited by J. E. Davies (Toronto University Press, Toronto, 1991, pp. 334–49.
J.-E. SUNDGREN, P. BODÖ and I. LUNDSTRÖM, J. Coll. Interface Sci. 110 (1986) 9.
J. LAUSMAA, J. Electron Spectrosc. Rel. Phenom. 81 (1996) 343.
C. LARSSON, P. THOMSEN, B.-O. ARONSSON, M. RODAHL, J. LAUSMAA, B. KASEMO and L.E. ERICSON, Biomaterials 17 (1996) 605.
J. LAUSMAA, B. KASEMO, H. MATTSSON and H. ODELIUS, Appl. Surface Sci. 45 (1990) 189.
J. LAUSMAA, B. KASEMO, U. ROLANDER, L. M. BJURSTEN, L. E. ERICSON, L. ROSANDER and P. THOMSEN, in “Surface Characterization of Biomaterials”, edited by B. D. Ratner (Elsevier, New York, 1988) pp. 161–74.
J. LAUSMAA, “Surface oxides on titanium: Preparation, characterization and biomaterial properties”, PhD Thesis, University of Gothenburg (1991).
D. LANDOLT, Electrochim. Acta 32 (1987) 1.
S. D. ROSS, “Anodic oxidation”, Organic Chemistry, Vol. 32, (Academic Press, New York, 1975).
L. E. DAVIS, N. C. MacDONALD, P. W. PALMBERG, G. E. RIACH and R. E. WEBER, “Handbook of Auger electron spectroscopy”, (Physical Electronics, Eden Prairie, 1978).
D. SARID and V. ELINGS, J. Vac. Sci. Technol. B 9 (1991) 431.
J. E. GRIFFITH, D. A. GRIGG, M. J. VASILE, P. E. RUSSELL and E. A. FITZGERALD, J. Vac. Sci. Technol. A 10 (1992) 674.
K. DONATH and G. A. BREUNER, J. Oral Pathol. 11 (1982) 318.
J. LAUSMAA, B. KASEMO and H. MATTSSON, Appl. Surf. Sci. 44 (1990) 133.
G. D. DAVIS, M. NATAN and K. A. ANDERSON, ibid. 15(1983) 321.
A. M. BARO, N. GARCIA, R. MIRANDA, L. VAZQUES, C. APARICIO, J. OLIVÉ and J. LAUSMAA, Biomaterials 7 (1986) 463.
H. OLIN, B.-O. ARONSSON, B. KASEMO, J. LAUSMMA and M. RODAHL, Ultramicroscopy 42–44 (1992) 567.
M. JOBIN, R. EMCH, F. ZENHAUSERN, S. STEINEMANN and P. DESCOUTS, J. Vac. Sci. Technol. B 9 (1991) 1263.
L. SENNERBY, P. THOMSEN and L. E. ERICSON, Int. J. Oral Maxillofac. Impl. 7 (1992) 62.
Idem, J. Mater. Sci. Mater. Med. 4 (1993) 493.
Idem, ibid. 4 (1993) 240.
A. WENNERBERG, A. EKTESSABI, T. ALBREKTSSON, C. JOHANSSON and B. ANDERSSON, (1996) to be published.
M. QUIRYNEN, C. M. L. BOLLEN, G. WILLEMS and D. VAN STEENBERGHE, Int. J. Oral Maxillofac. Impl. 9 (1994) 71.
A. WENNERBERG, T. ALBREKTSSON,and B. ANDERSSON, ibid. 8 (1993) 622.
N. C. BLUMENTHAL and V. COSMA, J. Biomed. Mater. Res. 23 (1989) 13.
K. E. HEALEY and P. DUCHEYNE, ibid. 26 (1992) 319.
Idem, J. Coll. Interface Sci. 150 (1992) 404.
A. RICH and K. A. HARRIS, J. Cell Sci. 50 (1981) 1.
T. N. SALTHOUSE, J. Biomed. Mater. Res. 18 (1984) 395.
P. VAN DER VALK, A. W. J. VAN PELT, H. J. BUSSCHER, H. P. D. JONG, C. R. H. WILDEVAR and J. ARENOS, ibid. 17 (1983) 807.
D. COCHRAN, J. SIMPSON, H. WEBER and D. BUSER, Int. J. Oral Maxillofac. Impl. 9 (1994) 289.
B. D. BOYAN, T. W. HUMMERT, K. KIESWETTER, D. SCHRAUB, D. D. DEAN and Z. SCHWARTZ, Cells Mater. 5 (1995) 323.
P.-I. BRÅNEMARK, U. BREINE, R. ADELL, B. O. HANSSON, J. LINDSTRÖM and A. OHLSSON, Scand. J. Plast. Reconstr. Surg. 3 (1969) 81.
T. ALBREKTSSON, P.-I. BRÅNEMARK, H.-A. HANSSON and J. LINDSTRÖM, Acta Orthop. Scand. 52 (1981) 155.
T. ALBREKTSSON, CRC Crit. Rev. Biocomp. 1 (1985) 53.
S. G. STEINEMANN, J. EULENBERG, P. A. MAEUSLI and A. SCHROEDER, in “Biological and biomechanical performance of biomaterials”, edited by M. A. P. Christel and A. J. C. Lee (Elsevier, Amsterdam, 1989) pp. 409–14.
G. A. ZARB and T. ALBREKTSSON, J. Periodont. Res. Dent. 11 (1991) 88.
R. BRÅNEMARK, PhD thesis, Göteborg University (1996).
L. SENNERBY, L. E. ERICSON, P. THOMSEN, U. LEKHOLM and P. ÅSTRAND, J. Clin. Oral Impl. Res. 2 (1991) 103.
M. ESPOSITO, P. THOMSEN, J. MÖLNE, C. GRETZER, L. E. ERICSON and U. LEKHOLM, ibid. (1997) in press.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
LARSSON, C., EMANUELSSON, L., THOMSEN, P. et al. Bone response to surface modified titanium implants – studies on the tissue response after 1 year to machined and electropolished implants with different oxide thicknesses. Journal of Materials Science: Materials in Medicine 8, 721–729 (1997). https://doi.org/10.1023/A:1018548225899
Issue Date:
DOI: https://doi.org/10.1023/A:1018548225899