Abstract
By using a Gleeble 3500D thermo-mechanical simulator, the nucleation behavior of intragranular acicular ferrites (IAF) was studied in a Ti-killed C-Mn steel. During continuous cooling transformation, the allotriomorphic ferrite (AF) and ferrite side plate (FSP) microstructures grew more rapidly with the temperature decreasing from 800 to 650 °C, and the IAF microstructure was dominant within austenite grain with further cooling to 600 °C. The diffusion bonding experiment and the effect of C, Mn and Si concentrations on the Ae3 temperature by thermodynamic calculation confirm that Ti2 O3 itself absorbs neighboring Mn atoms to form Mn-depleted zone (MDZ), which promotes the nucleation of IAF microstructure effectively. High temperature holding tests indicate that the nucleation potential of IAF microstructure was lowered in the Ti-killed C-Mn steel when it was treated at high temperature (1250 °C) for a longer time, which is attributed to the saturated absorption degree of Mn atoms by titanium oxide.
Similar content being viewed by others
References
M. A. Linaza, J. L. Romero, J. M. Rodríguez-Ibabe, J. J. Urcola, Scripta Metall. 29 (1993) 1217–1222.
J. Takamura, S. Mizoguchi, in: Proc 6th Int. Iron and Steel Cong. Vol. 1, ISIJ, Tokyo, 1990, pp. 68–610.
K. He, D. V. Edmonds, Mater. Sci. Technol. 18 (2002) 289–296.
S. Zhang, N. Hatori, M. Enomoto, T. Tarui, ISIJ Int. 36 (1996) 1301–1309.
K. Yamamoto, T. Hasegawa, J. I. Takamura, ISIJ Int. 36 (1996) 80–86.
B. Ralph, Mater. Sci. Technol 6 (1990) 1139–1144.
T. K. Lee, H.J. Kim, B. Y. Kang, S. K. Hwang, ISIJ Int. 40 (2000) 1260–1268.
J. Y. Park, J. K. Park, W. Y. Choo, ISIJ Int. 40 (2000) 1253–1259.
G. Shigesato, M. Sugiyama, J. Electron Microsc. 51 (2002) 359–367.
J. S. Byun, J. H. Shim, J. Y. Suh, Y. J. Oh, Y. W. Cho, J. D. Shim, D. N. Lee, Mater. Sci. Eng. A 319-321 (2001) 326–331.
J. M. Gregg, H. K. D. H. Bhadeshia, Acta Mater. 45 (1997) 739–748.
J. H. Shim, Y. W. Cho, S. H. Chung, J. D. Shim, D. N. Lee, Acta Mater. 47 (1999) 2751–2760.
H. Mabuchi, R. Uemori, M. Fujioka, ISIJ Int. 36 (1996) 1406–1412.
F. Ishikawa, T. Takahashi, ISIJ Int. 35 (1995) 1128–1133.
T. Hanamura, H. Shibata, Y. Waseda, H. Nakajima, S. Torizuka, T. Takanashi, K. Nagai, ISIJ Int. 39 (1999) 1188–1193.
I. E. Grey, C. Li, A. F. Reid, J. Solid State Chem. 17 (1976) 343–352.
J. H. Shim, J.S. Byun, Y. W. Cho, Y. J. Oh, J. D. Shim, D. N. Lee, Scripta Mater. 44 (2001) 49–54.
J. H. Shim, Y. J. Oh, J. Y. Suh, Y. W. Cho, J. D. Shim, J. S. Byun, D. N. Lee, Acta Mater. 49 (2001) 2115–2122.
J. S. Byun, J. H. Shim, Y. W. Cho, D. N. Lee, Acta Mater 51 (2003) 1593–1606.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Chai, F., Su, H., Yang, Cf. et al. Nucleation Behavior Analysis of Intragranular Acicular Ferrite in a Ti-killed C-Mn Steel. J. Iron Steel Res. Int. 21, 369–374 (2014). https://doi.org/10.1016/S1006-706X(14)60057-1
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1016/S1006-706X(14)60057-1