Abstract
Magnetic TS-1 was synthesized with nanosized nickelferrite particles as nuclei via the hydrothermal synthesis and solvent vaporation method. The prepared samples were characterized with N2 adsorption-desorption isotherms, FTIR spectrometry, Raman spectrometry, X-ray diffraction, Ultraviolet-visible spectroscopy and Vibrating sample magnetometry. The results show that the composite obtained was composed of TS-1 with MFI structure and NiFe2O4 with spinel structure, its specific surface area was about 316 m2/g, pore volume was 0.12 cm3/g and pore size distribution was in the range of 0.5–0.7 nm. The catalytic activity of the composite was also investigated by its catalyzing the decomposition of rhodamine B oxidized by H2O2 in aqueous solution. In this case Rhodamine B pollutant could be completely degraded within 150 min. Magnetic TS-1 exhibited high photocatalytic efficiency and super paramagnetic nature for cleaning polluted water with the help of magnetic separation.
Similar content being viewed by others
References
Taramasso M., Perego G., Notari B., Preparation of Porous Crystalline Synthetic Material Comprised of Silicon and Titanium Oxides, US 4410501, 1983
Xu Y. M., Wang R. S., Chem. J. Chinese Universities, 1999, 20(7), 1002
Vasile A., Busuioc-Tomoiaga A. M., Materials Research Bulletin, 2012, 47, 35
Wang R. W., Hu L., Chu B., Zhu G. S., Qiu S. L., Chem. J. Chinese Universities, 2004, 25(8), 1485
Wang D. Q., Li Y., Liu L. S., Li J. P., Zhang R., Chem. J. Chinese Universities, 2012, 33(12), 2722
Zhu G. W., Chen X. B., Jiang H., Huang J., Wang R. W., Qiu S. L., Chem. Res. Chinese Universities, 2013, 29(6), 1036
Kim J. H., Do Y. J., Park J. H., Park S. S., Hong S. S., Lee G. D., Kinet. Catal. Lett., 2004, 83(2), 377
Cojocariu A. M., Mutin P. H., Dumitriu E., Vioux A., Fajula F., Hulea V., Chemosphere, 2009, 77, 1065
Lee G. D., Jung S. K., Jeong Y. J., Park J. H., Lim K. T., Ahn B. H., Hong S. S., Appl. Catal. A: Gen., 2003, 239, 197
Zhang J., Zhao D. S., Yang L.Y., Li Y. B., Chemical Engineering Journal, 2010, 156, 528
Hourdin G., Germain A., Moreau C., Fajula F., Catalysis Letters, 2000, 69, 241
Beydoun D., Amal R., Low G. K. C., Setphen M., J. Phys. Chem. B, 2000, 104(18), 4387
Kurinobu S., Tsurusaki K., Natuic Y., Kimata M., Hasegawa M., Journal of Magnetism and Magnetic Materials, 2007, (310), 1025
Li Y., Dong X. F., Li J. P., Particuology, 2011, 9(5), 475
Yuan J., Lü Y. K., Li Y., Li J. P., Chem. Res. Chinese Universities, 2010, 26(2), 278
Li C., Xiong G., Liu J. K., Ying P. L., Xin Q., Feng Z. C., J. Phys. Chem. B, 2001, 105(15), 2993
Author information
Authors and Affiliations
Corresponding author
Additional information
Supported by the Major Program of Science and Technology of Shanxi Province, China(No.20111101013).
Rights and permissions
About this article
Cite this article
Li, Y., Xue, Z., Zhang, Q. et al. Preparation of magnetic TS-1 and its catalytic activity. Chem. Res. Chin. Univ. 31, 430–433 (2015). https://doi.org/10.1007/s40242-015-4434-6
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40242-015-4434-6