Electrochemical Evaluation of Pt-Based Binary Catalysts on Various Supports for the Direct Methanol Fuel Cell

  • Review Article
  • Published:
Electrocatalysis Aims and scope Submit manuscript

Abstract

Multi-walled carbon nanotubes (MWCNTs), TiO2, MoO2, and carbon black Vulcan XC-72 were investigated as supports for PtRu and PtSn catalysts. X-ray diffraction (XRD) confirmed that all electrocatalysts examined display characteristic patterns similar to that of the Pt/C electrocatalyst, an indication that the catalysts have predominantly the Pt face-centered cubic (fcc) crystal structure. High-resolution transmission electron microscopy (HRTEM) images showed spherical PtRu and PtSn nanoparticles with a narrow particle size distribution, dispersed on the support materials. The metal loading for the prepared electrocatalyst was estimated using energy-dispersive X-ray spectroscopy (EDS), and it was observed to be closest to that of the catalysts supported on Vulcan XC-72. Cyclic voltammograms showed PtSn/C to be the most active, as it possessed a higher electroactive surface area than that of the other catalysts, followed by Pt/C > PtRu/MWCNT > PtRu/C > PtSn/MWCNT > PtSn/MoO2 > PtRu/MoO2 > PtSn/TiO2 > PtRu/TiO2. It was also observed that catalysts supported on MWCNTs were more active than those supported on metal oxides. Furthermore, catalysts supported on MWCNTs proved to be more stable than all the other supported catalysts examined. Therefore, MWCNTs have been proven in this study to be the best material for supporting electrocatalysts for direct methanol fuel cells.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4

Similar content being viewed by others

References

  1. H.Y. Yana, J. Inukai, H. Uchida, M. Watanabe, P.K. Babu, T. Kobayashi, J.H. Chung, E. Oldfield, A. Wieckowski, Phys. Chem. Chem. Phys. 8, 4932 (2006)

    Article  CAS  Google Scholar 

  2. S.S. Kocha, Electrochemical degradation: electrocatalyst and support durability, in Polymer Electrolyte Fuel Cell Degradation, ed. by M.M. Mench, E.C. Kumbur, T.N. Veziroglu (Academic, Boston, 2012), p. 89

    Chapter  Google Scholar 

  3. G.Q. Lu, C.Y. Wang, J. Power Sources 134, 33 (2004)

    Article  CAS  Google Scholar 

  4. K. Sundmarcher, T. Schultz, S. Zhou, K. Scott, M. Ginkel, E.D. Giles, Chem. Eng. Sci. 56, 333 (2001)

    Article  Google Scholar 

  5. T.S. Zhao, W.W. Yang, R. Chen, Q.X. Wu, J. Power Sources 195, 3451 (2010)

    Article  CAS  Google Scholar 

  6. H. Liu, C. Song, L. Zhang, J. Zhang, H. Wang, D.P. Wilkinson, J. Power Sources 155, 95 (2006)

    Article  CAS  Google Scholar 

  7. Garche J, Encyclopedia of electrochemical power sources, ed. by T.S. Zhao, C. Xu (Elsevier, ISBN-13: 978-0-444-52093-7, 2009), p. 381

  8. S.K. Kamarudin, F. Achmad, W.R.W. Daud, Int. J. Hydrogen Energy 34, 6902 (2009)

    Article  CAS  Google Scholar 

  9. D.H. Lim, D.H. Choi, W.D. Lee, H.I. Lee, Appl. Catal. B Environ. 89, 484 (2009)

    Article  CAS  Google Scholar 

  10. T. Toda, H. Igarashi, M. Watanabe, J. Electroanal. Chem. 460, 258 (1999)

    Article  CAS  Google Scholar 

  11. Garche J, Encyclopedia of electrochemical power sources, ed. by SH Bergens, MEP Markiewicz, (Elsevier, ISBN-13: 978-0-444-52093-7, 2009), p. 616

  12. R. Balgis, G.M. Anilkumar, S. Sago, T. Ogi, K. Okuyama, J. Power Sources 203, 26 (2012)

    Article  CAS  Google Scholar 

  13. C.M. Chen, M. Chen, Y.W. Peng, H.W. Yu, C.F. Chen, Thin Solid Films 498, 202 (2006)

    Article  CAS  Google Scholar 

  14. H.A. Gasteiger, S.S. Kocha, B. Sompappli, F.T. Wagner, Appl. Catal. B Environ. 56, 9 (2005)

    Article  CAS  Google Scholar 

  15. J.B. Fernandas, in Catalysis, selected applications, ed. by B. Viswanathan (Narosa Publishing House, 2007), p 9

  16. K.T. Jeng, C.C. Chien, N.Y. Hsu, S.C. Yern, S.D. Chiou, S.H. Lin, W.M. Huang, J. Power Sources 160, 97 (2006)

    Article  CAS  Google Scholar 

  17. S. Rojas, F.J. Garcia, S. Jaras, M.V. Huerta, J.L.F. Fierro, M. Boutonnet, Appl. Catal. A Gen. 285, 24 (2005)

    Article  CAS  Google Scholar 

  18. R.P. Raffaelle, B.J. Landi, J.D. Harris, S.G. Bailey, A.F. Hepp, Mater. Sci. Eng. B 116, 233 (2005)

    Article  CAS  Google Scholar 

  19. E. Antolini, E.R. Gonzalez, Solid State Ionics 180, 746 (2009)

    Article  CAS  Google Scholar 

  20. S. Maass, F. Finsterwalder, G. Frank, R. Hartmann, C. Merten, J. Power Sources 176, 444 (2008)

    Article  CAS  Google Scholar 

  21. F. Rodrìguez-Reinosa, Carbon 36, 159 (1998)

    Article  Google Scholar 

  22. B.L. Dutrow, C.M. Clark, Geochemical instrumentation and analysis. serc.carleton.edu/research_education/geochemsheet/techniques/XRD.html

  23. Y.-H. Cho, O.-H. Kim, D.Y. Chung, H. Choe, Y.-H. Cho, Y.-E. Sun, Appl. Catal. B Environ. 154-155, 309 (2014)

    Article  CAS  Google Scholar 

  24. L. Chen, J. Zang, Y. Wang, L. Bian, Electrochim. Acta 53, 3442 (2008)

    Article  CAS  Google Scholar 

  25. Y. Wang, J. Zang, L. Dong, H. Pan, Y. Yuan, Y. Wang, Electrochim. Acta 113, 583 (2013)

    Article  CAS  Google Scholar 

  26. N.Y. Hsu, C.C. Chien, K.T. Jeng, Appl. Catal. B Environ. 84, 196 (2008)

    Article  CAS  Google Scholar 

  27. S.M.S. Kumar, N. Hdyatai, J.S. Herrero, S. Irusta, K. Scott, Int. J. Hydrogen Energy 36, 5453 (2011)

    Article  CAS  Google Scholar 

  28. E. Antolini, Appl. Catal. B Environ. 88, 1 (2009)

    Article  CAS  Google Scholar 

  29. J. Prabhuram, T.S. Zhao, C.W. Wong, J.W. Guo, J. Power Sources 134, 1 (2004)

    Article  CAS  Google Scholar 

  30. H. Lipson, H. Steeple, Interpretation of X-Ray Powder Diffraction Patterns (Macmillan and Company, Ltd, London, 1970), pp. 93–94

    Google Scholar 

  31. D.M. Han, Z.P. Gao, R. Zeng, C.J. Kim, Y.Z. Meng, H.K. Liu, Int. J. Hydrogen Energy 34, 2426 (2009)

    Article  CAS  Google Scholar 

  32. M. Zhu, G. Sun, Q. Xin, Electrochim. Acta 54, 1511 (2009)

    Article  CAS  Google Scholar 

  33. J.H. Han, J.H. Han, H.T. Liu, J. Power Sources 164, 166 (2007)

    Article  CAS  Google Scholar 

  34. E. Antolini, T. Lopez, E.R. Gonzalez, J. Alloys Compd. 461, 253 (2008)

    Article  CAS  Google Scholar 

  35. C.T. Hsieh, J.Y. Lin, S.Y. Yang, Phys. E. 41, 373 (2009)

    Article  CAS  Google Scholar 

  36. E. Yoo, T. Okada, T. Kizuka, J. Nakamura, J. Power Sources 180, 221 (2008)

    Article  CAS  Google Scholar 

  37. E. Antolini, J.R.C. Salgado, E.R. Gonzalez, J. Electroanal. Chem. 580, 145 (2006)

    Article  CAS  Google Scholar 

  38. S.Y. Huang, P. Ganesan, B.N. Popov, Appl. Catal. B Environ. 102, 71 (2011)

    Article  CAS  Google Scholar 

  39. M. Carmo, A.R. dos Santos, J.G.R. Poco, M. Linardi, J. Power Sources 173, 860 (2007)

    Article  CAS  Google Scholar 

  40. C.M. Chen, M. Chen, Y.W. Peng, H.W. Yu, C.F. Chen, Thin Solid Films 498, 202 (2006)

    Article  CAS  Google Scholar 

  41. J. Chen, Q. Chen, Q. Ma, J. Colloid Interface Sci. 370, 32 (2012)

    Article  CAS  Google Scholar 

  42. N.Y. Hsu, C.C. Chien, K.T. Jeng, Appl. Catal. B Environ. 84, 196 (2008)

    Article  CAS  Google Scholar 

  43. G. An, P. Yu, L. Mao, Z. Liu, S. Miao, Z. Miao, K. Ding, Carbon 45, 536 (2002)

    Article  CAS  Google Scholar 

  44. W.Z. Li, C.H. Liang, W.J. Zhou, J.S. Qiu, Z.H. Zhou, G.Q. Sun, J. Phys. Chem. B 107, 6292 (2003)

    Article  CAS  Google Scholar 

  45. S. Kim, H.J. Sohn, S. Park, Curr. Appl. Phys. 10, 1142 (2010)

    Article  Google Scholar 

  46. M. Williams, L. Khotseng, Q. Naidoo, L. Petric, A. Nachaev, V. Linkov, S. Afr. J. Sci. 105, 285 (2009)

    CAS  Google Scholar 

  47. M. Carmo, A.R. dos Santos, J.G.R. Poco, M. Linardi, J. Power Sources 173, 860 (2007)

    Article  CAS  Google Scholar 

  48. A.L. Ocampo, M. Miranda-Hernández, J. Morgado, J.A. Montaya, P.J. Sebastian, J. Power Sources 160, 915 (2006)

    Article  CAS  Google Scholar 

  49. J. Prabhuram, T.S. Zhao, Z.X. Liang, R. Chen, Electrochim. Acta 52, 2649 (2007)

    Article  CAS  Google Scholar 

  50. A.O. Neto, T.P.R. Vasconcelos, R.W.R.V. Da Silva, M. Linardi, E.V. Spinace, J. Appl. Electrochem. 35, 193 (2005)

    Article  CAS  Google Scholar 

  51. M. Zhu, G. Sun, Q. Xin, Electrochim. Acta 54, 1511 (2009)

    Article  CAS  Google Scholar 

  52. F. Colmati, E. Antolini, E.R. Gonzalez, Electrochim. Acta 50, 5496 (2005)

    Article  CAS  Google Scholar 

  53. Y. Shao, G. Yin, Y. Gao, J. Power Sources 171, 558 (2007)

    Article  CAS  Google Scholar 

  54. E. Antolini, T. Lopez, E.R. Gonzalez, J. Alloys Compd. 461, 253 (2008)

    Article  CAS  Google Scholar 

  55. C. Jehabharathi, P. Venkateshkumar, J. Mathiyarasu, K.L.N. Phani, Electrochim. Acta 54(2), 448 (2008)

    Article  CAS  Google Scholar 

  56. C.J. Tseng, S.T. Lo, S.C. Lo, P.P. Chu, Mater. Chem. Phys. 100, 385 (2006)

    Article  CAS  Google Scholar 

  57. H. Li, G. Sun, L. Cao, L. Jiang, Q. Xin, Electrochim. Acta 52, 6622 (2007)

    Article  CAS  Google Scholar 

  58. S.Y. Huang, P. Ganesan, B.N. Popov, Appl. Catal. B Environ. 102, 71 (2011)

    Article  CAS  Google Scholar 

  59. V.A. Paganin, E. Sitta, T. Iwasita, W. Vielstich, J. Appl. Electrochem. 35, 1239 (2005)

    Article  CAS  Google Scholar 

Download references

Acknowledgments

The generous financial support of Eskom and kind contribution from Physics Department, SAIAMC (UWC), and iThemba Laboratories are gratefully acknowledged.

Author information

Authors and Affiliations

Authors

Corresponding author

Correspondence to L. Khotseng.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Khotseng, L., Bangisa, A., Modibedi, R.M. et al. Electrochemical Evaluation of Pt-Based Binary Catalysts on Various Supports for the Direct Methanol Fuel Cell. Electrocatalysis 7, 1–12 (2016). https://doi.org/10.1007/s12678-015-0282-x

Download citation

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s12678-015-0282-x

Keywords

Navigation