Abstract
The effect of commercial nano-sized MgO particles on the heterogeneous nucleation of iron-rich intermetallic compounds in Al–5Mg–2Si–0.7Mn–1.1Fe (wt%) was investigated. The experimental results showed that, when solidified under non-equilibrium conditions, the formation of Al6(Fe, Mn) phase was enhanced by a decreased cooling rate. The MgO addition resulted in a suppression of Al15(Fe, Mn)3Si2 phase. However, it promoted the heterogeneous nucleation of the Al6(Fe, Mn) phase. Besides, a peritectic reaction commenced at the liquid/Al6(Fe, Mn) interface, resulting in the formation of Al15(Fe, Mn)3Si2 and (Al) at the interface in the alloy solidified at 0.1 K/s. The investigation of the effect of MgO on phase selection included analysis of the crystallographic matching at the interface.
Similar content being viewed by others
References
Mbuya T O, and Odera B O, IJCMR 16 (2003) 451.
Zhang L, Gao J, Damoah L N W, and Roberston D G, Miner Process Extr Metall Rev 33 (2012) 99.
Mondolfo L F, Aluminum Alloys: Structure and Properties, Butterworths, London (1976).
Munson D, J Inst Met 95 (1967) 217.
Kral M V, McIntyre H R, and Smillie M J, Scr Mater 51 (2004) 215.
Carpenter G J C, and Le Page Y, Scr Metall Mater 28 (1993) 733.
Shabestari S G, Mater Sci Eng A 383 (2004) 289.
Cooper M, Acta Crystallogr 23 (1967) 1106.
Aluminium Association, Standard Test Procedure for Aluminium Alloy Grain Refiners: TP - 1, Aluminium Association, Washington, DC (1987).
Que Z P, Wang Y, Zhou Y P, Liu L, and Fan Z, Mater Sci Forum 828–829 (2015) 53.
Barlock J G, and Mondolfo L F, Z Metallkunde 66 (1975) 605.
Acknowledgments
The authors wish to acknowledge the financial support from the EPSRC under the Grant for the EPSRC Centre: LiME.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Que, Z.P., Zhou, Y.P., Wang, Y. et al. Effect of MgO on Phase Selection in Al–Mg–Si–Fe–Mn Alloys. Trans Indian Inst Met 68, 1167–1172 (2015). https://doi.org/10.1007/s12666-015-0664-z
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12666-015-0664-z