Abstract
A processing technique for applying plastic deformation to a solid wood has been developed. In the present study, the effects of repetitive flow forming on the fluidity of solid wood materials impregnated with thermoplastic binder and on the mechanical properties of the products were investigated. The results showed that the increase in the number of extrusions decreased the load of the starting point of the extrusion especially in the lower polymer content of the wood materials. The bending strengths of the products were decreased with the repetitive extrusion using the lower polymer content (less than approximately 50 %) of the materials. On the other hand, the strength with higher polymer content (more than approximately 50 %) increased with the repetitive extrusion. The wood particles were found to become smaller in size with the repetitive extrusion. The tangles of the wood particles were also observed in higher polymer content of the materials. It was speculated that these configuration changes during reprocessing strongly affect both the fluidity during the extrusion and the mechanical properties of the products.
Similar content being viewed by others
References
Sandberg D, Haller P, Navi P (2012) Thermo-hydro and thermos-hydro-mechanical wood processing: An opportunity for future environmentally friendly wood products. Wood Mater Sci Eng 8:64–88. doi:10.1080/17480272.2012.751935
Yamashita O, Yokochi H, Imahishi H, Miki T, Kanayama K (2006) Flow phenomenon of bulk wood. Trans of the Japan Society Of Mechanical Engineering A 72:2074–2078
Yamashita O, Yokochi H, Miki T, Kanayama K (2007) Producing cups from wood by extrusion using flow phenomenon of bulk wood. Trans. of the Japan Society Of Mechanical Engineering A 73:583–588
Yamashita O, Yokochi H, Miki T, Kanayama K (2009) The pliability of wood and its application to molding. J Mater Proc Tech 209:5239–5244
Miki T, Seki M, Sugimoto H, Shigematsu I, Kanayama K (2012) Mechanical properties of wood plastic composites prepared by wood flow forming using low molecular phenol resin. Proc. of 11th pacific rim Bio-comp 154–161
Miki T, Seki M, Shigematsu I, Kanayama K (2013) Preparation of three dimensional products using flow deformability of wood treated by small molecular resins. Adv Mater Res 856:79–86
Miki T, Sugimoto H, Shigematsu I, Kanayama K (2014) Superplastic deformation of solid wood by slipping cells at sub-micrometer intercellular layers. Inter J Nanotech 11:678. doi:10.1504/IJNT.2014.060572
Furuno T, Goto T (1978) The role of polymer in the cell wall on the dimensional stability of wood-polymer composite (WPC). Journal of the Japan Wood Research Society 24:287–293
Stamm AJ (1964) Wood and cellulose science. The Ronald press co, New York, pp. 476–477
Okumura M, Shiraishi N, Sadoh K, Yokota T (1977) Temperature dependence of viscoelastic behavior of wood-PMMA composites. The Society of Mater Sci 26:465–471
Stamm AJ (1964) Wood and cellulose science. The Ronald press co, New York, pp. 58–59
Wunderlich W (1989) Physical Constants of Poly (methyl methacrylate). In: Brandrup J, Immergut EH (eds) Polymer handbook, 3rd edn. Willy, New York, p. V/77
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Seki, M., Miki, T., Tanaka, S. et al. Repetitive flow forming of wood impregnated with thermoplastic binder. Int J Mater Form 10, 435–441 (2017). https://doi.org/10.1007/s12289-016-1291-x
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12289-016-1291-x