Abstract
The preparation and characterization of nanoscale zero-valent iron-loaded porous sepiolite, as well as its application in the decolorization of methylene blue in aqueous solution, have been studied in this work through the measurements of field emission scanning electron microscope with energy dispersive spectrometry, x-ray photoelectron spectrometry, Fourier transform infrared spectroscopy and specific surface area. The results showed that nanoscale zero-valent iron particles were successfully loaded on the surface and interior pores of sepiolite through physical adsorption. It was revealed that the decoloration capacity of methylene blue on nanoscale zero-valent iron-loaded porous sepiolite in water was comparable to that of nanoscale zero-valent iron, and nine times higher than that of natural sepiolite. This indicates that porous sepiolite was a good supporter for the loading of nanoscale zero-valent iron and nanoscale zero-valent iron-loaded sepiolite was a good decolorant because of its high decoloration efficiency and easy separation.
Similar content being viewed by others
References
Y. Liu, S.A. Majetich, R.D. Tilton, D.S. Sholl, and G.V. Lowry, Environ. Sci. Technol. 39, 1338 (2005).
X. Zhang, Y.M. Lin, X.Q. Shan, and Z.L. Chen, Chem. Eng. J. 158, 566 (2010).
C.B. Wang and W.X. Zhang, Environ. Sci. Technol. 31, 2154 (1997).
Y.H. Huang, P.K. Peddi, C. Tang, H. Zeng, and X. Teng, Sep. Purif. Technol. 118, 690 (2013).
X. Zhang, S. Lin, X.-Q. Lu, and Z.L. Chen, Chem. Eng. J. 163, 243 (2010).
A.M. Azzam, S.T. El-Wakeel, B.B. Mostafa, and M.F. El-Shahat, J. Environ. Chem. Eng. 4, 2196 (2016).
J. Fan, Y. Guo, J. Wang, and M. Fan, J. Hazard. Mater. 166, 904 (2009).
C.D. Raman and S. Kanmani, J. Environ. Manag. 177, 341 (2016).
R.L. Frost, Y. Xi, and H. He, J. Colloid Interface Sci. 341, 153 (2010).
Y.-P. Sun, X.Q. Li, J. Cao, W. Zhang, and H.P. Wang, Adv. Colloid Interface Sci. 120, 47 (2006).
S.A. Kim, S. Kamala-Kannan, K.J. Lee, Y.J. Park, P.J. Shea, W.H. Lee, H.M. Kim, and B.T. Oh, Chem. Eng. J. 217, 54 (2013).
F. Fu, J. Ma, L. Xie, B. Tang, W. Han, and S. Lin, J. Environ. Manag. 128, 822 (2013).
L.N. Shi, Y.M. Lin, X. Zhang, and Z.L. Chen, Chem. Eng. J. 171, 612 (2011).
X. Wang, P. Wang, J. Ma, H. Liu, and P. Ning, Appl. Surf. Sci. 345, 57 (2015).
A. Akbari and F. Mohamadzadeh, J. Nanostruct. 2, 175 (2012).
H. Kim, H.J. Hong, J. Jung, S.H. Kim, and J.W. Yang, J. Hazard. Mater. 176, 1038 (2010).
E. Petala, K. Dimos, A. Douvalis, T. Bakas, J. Tucek, R. Zbořil, and M.A. Karakassides, J. Hazard. Mater. 261, 295 (2013).
G. Quan, J. Zhang, J. Guo, and Y. Lan, Water. Air. Soil Pollut. 225, 1979 (2014).
R. Fu, Y. Yang, Z. Xu, X. Zhang, X. Guo, and D. Bi, Chemosphere 138, 726 (2015).
J. Sheng, Y. Xie, and Y. Zhou, Appl. Clay Sci. 46, 422 (2009).
A. Al-Futaisi, A. Jamrah, and R. Al-Hanai, Desalination 214, 327 (2007).
G.C. Allen, M.T. Curtis, A.J. Hooper, and P.M. Tucker, J. Chem. Soc. Dalt. Trans. 14, 1525 (1974).
A.P. Grosvenor, B.A. Kobe, M.C. Biesinger, and N.S. McIntyre, Surf. Interface Anal. 36, 1564 (2004).
Acknowledgements
The financial supports to this work from the National Natural Science Foundation of China under the Projects Nos. 51474167 and 51674183 were gratefully acknowledged.
Author information
Authors and Affiliations
Corresponding authors
Electronic supplementary material
Below is the link to the electronic supplementary material.
Rights and permissions
About this article
Cite this article
Wang, Q., Ren, G., Jia, F. et al. Preparation and Characterization of Nanoscale Zero-Valent Iron-Loaded Porous Sepiolite for Decolorizing Methylene Blue in Aqueous Solutions. JOM 69, 699–703 (2017). https://doi.org/10.1007/s11837-017-2269-y
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11837-017-2269-y