Abstract
Phase equilibria in the isothermal section of the Al-Fe-Si-V quaternary system with Al being fixed at 85 wt.% and the Al-rich corner of Al-Fe-Si ternary system at 620 °C have been determined experimentally using scanning electron microscopy coupled with energy dispersive x-ray spectroscopy, and x-ray diffractometry. Five four-phase regions are identified in the isothermal section of Al-Fe-Si-V quaternary system. Five three-phase regions are found in Al-rich corner of Al-Fe-Si ternary system. No new ternary and quaternary compounds are detected in the present study.
Similar content being viewed by others
References
J. Sun and M.P. Wan, Compartion of Corrosion Resisting Properties of Hot Dip Galvanizing and Aluminum Coating of Steel Parts and Their Application, Mod. Mach., 2010, 2, p 75-77, in Chinese
G.H. Awan and F.U. Hasan, The Morphology of Coating/Substrate Interface in Hot-Dip-Aluminized Steels, Mater. Sci. Eng. A, 2008, 472(1-2), p 157-165
S.H. Hwang, J.H. Song, and Y.S. Kim, Effects of Carbon Content of Carbon Steel on Its Dissolution into a Molten Aluminum Alloy, Mater. Sci. Eng. A, 2005, 390(1-2), p 437-443
S. Kobayashi and T. Yakou, Control of Intermetallic Compound Layers at Interface Between Steel and Aluminum by Diffusion-Treatment, Mater. Sci. Eng. A, 2002, 338(1-2), p 44-53
N.A. El-Mahallawy, M.A. Taha, M.A. Shady, A.R. El-Sissi, A.N. Attia, and W. Reif, Analysis of Coating Layer Formed on Steel Strips During Aluminising by Hot Dipping in Al-Si Baths, Mater. Sci. Technol., 1997, 13, p 832-840
R.W. Richards, R.D. Jones, P.D. Clements, and H. Clarke, Metallurgy of Continuous Hot Dip Aluminizing, Int. Mater. Rev., 1994, 39, p 191-212
G. Eggeler, W. Auer, and H. Kaesche, On the Influence of Silicon on the Growth of the Alloy Layer During Hot Dip Aluminizing, J. Mater. Sci., 1986, 21, p 3348-3350
W.J. Cheng and C.J. Wang, High-Temperature Oxidation Behavior of Hot-Dipped Aluminide Mild Steel with Various Silicon Contents, Appl. Surf. Sci., 2013, 274, p 258-265
X.P. Su, C.J. Wu, D. Liu, F.C. Yin, Z.X. Zhu, and S. Yang, Effect of Vanadium on Galvanizing Si-Containing Steels, Surf. Coat. Technol., 2010, 205(1), p 213-218
T.B. Massalski, H. Okamoto, P.R. Subramanian, and L. Kacprzak, Binary Alloy Phase Diagrams, 2nd ed., ASM, Materials Park, 1990
G.V. Raynor and V.G. Rivlin, Al-Fe-Si, Phase Equilibria in Iron Ternary Alloys, Institute of Metals, 1988, p 122-139
Z.K. Liu and Y.A. Chang, Thermodynamic Assessment of the Al-Fe-Si System, Metall. Mater. Trans. A, 1999, 30, p 1081-1095
V. Raghavan, Aluminum-Iron-Silicon, J. Phase Equilib., 2002, 23(4), p 362-366
T. Maitra and S.P. Gupta, Intermetallic Compound Formation in Fe-Al-Si Ternary System: Part II, Mater. Charact., 2002, 49(4), p 293-311
H.W.L. Phillips, Annotated Equilibrium Diagrams of Some Al Alloy Systems, Inst. Met., 1959, 25, p 57-65
V. Raghavan, Al-Fe-Si (Aluminum-Iron-Silicon), J. Phase Equilib. Diffus., 2009, 30(2), p 184-188
Y. Du, J.C. Schuster, Z.K. Liu, R. Hu, P. Nash, W. Sun, W. Zhang, J. Wang, L. Zhang, C. Tang, Z. Zhu, S. Liu, Y. Ouyang, W. Zhang, and N. Krendelsberger, A Thermodynamic Description of the Al-Fe-Si System over the Whole Coposition and Temperature Ranges via a Hybrid Approach of CALPHAD and Key Experiments, Intermetallics, 2008, 16, p 554-570
Z. Li, X. Li, F. Yin, Y. Wu, and M. Zhao, Phase Equilibria of the Al-Rich Corner in the Al-Cu-Fe-Si System at 650 °C, J. Phase Equilib. Diffus., 2014, 35(3), p 248-255
R. Schmid-Fetzer, Aluminum-Cobalt-Silicon, G. Petzow, G. Effenberg, Ed., VCH, Weinheim, 1991
E. Gebhardt and G. Joseph, The Aluminum-Silicon-Vanadium Ternary System, Z. Metallkd., 1961, 52, p 310-317, [in German]
A. Müller, The A15 Superconductor Phase in the Systems V-Ga-Al, V-Si-Al, V-Ge-Al, and V-Sb-Al, Z. Naturforsch. Astrophys. Phys. Phys. Chem., 1969, 24A, p 1134-1145, [in German]
P. Villars, A. Prince, and H. Okamoto, Al-Si-V Handbook of Ternary Alloy, Phase Diagrams, 1995, 4, p 4320-4331
B. Huber, H.S. Effenberger, and K.W. Richter, Phase Equilibria in the Al-Si-V System, Intermetallics, 2010, 18, p 606-615
E.M. Sokolovskaya, L.M. Badalova, and E.F. Kazakova, Phase Composition of Rapidly Quenched Alloys of the System Al-Fe-V, Izv. Akad. Nauk SSSR Met., 1987, 1987(5), p 212-215
E.M. Sokolovskaya, L.M. Badalova, E.F. Kazakova, and N.V. Stroeva, Interactions of Intermetallic Compounds in the Ternary System Aluminum-Iron-Vanadium, Vestn. Mosk. Univ. Ser. 2: Khim., 1988, 29(3), p 303-306, [in Russian]
V. Raghavan, The Al-Fe-V (Aliminium-Iron-Vanadium) System, J. Phase Equilib., 1992, p 204-207
V. Raghavan, The Al-Fe-V (Aliminium-Iron-Vanadium) System, J. Phase Equilib., 2002, 23, p 439-440
Materials Science International Team MSIT®, Al-Fe-V (Aluminium-Iron-Vanadium), Light Metal Systems. Part 3, Vol. 11A3, G. Effenberg, and S. llyenko, Ed., 2005, p 1-10
Acknowledgments
This investigation was supported by National Natural Science Foundation of China (No. 51471141), Scientific Research Fund of Hunan Provincial Science and Technology Department (No. 2014FJ2010), and doctoral start-up fund of Xiangtan University (No. 13QDZ02).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Zou, Q., Zhao, M., Yin, F. et al. Phase Equilibria in the Al-Rich Corner of the Al-Fe-Si-V Quaternary System at 620 °C. J. Phase Equilib. Diffus. 36, 274–282 (2015). https://doi.org/10.1007/s11669-015-0382-6
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11669-015-0382-6