Abstract
Ru-Ta-C films deposited on silicon substrates were evaluated as barriers for copper metalization. The films were prepared by magnetron cosputtering using a Ru target and a Ta-C target. Compositions and structure of resultant films were optimally tuned by the respective deposition power of each target. The fabricated Ru-Ta-C films were characterized via four-point probe measurement, x-ray diffractometry, field-emission electron probe microanalysis, and transmission electron microscopy. Failure temperature was evaluated by the sudden rise in electrical resistivity after annealing the Cu/Ru-Ta-C/Si sandwich films, and a reference bilayer Cu/(5 nm Ru)/(5 nm Ta-C)/Si scheme. The optimal compositions were 10 nm Ru77Ta15C7 and (5 nm Ru)/(5 nm Ta-C), both of which showed failure temperature of 650°C for 30 min and electrical resistivity less than 150 μΩ cm. Because of their high thermal stability and low electrical resistivity, both Ru-Ta-C and Ru/Ta-C films are promising barriers for Cu metalization.
Similar content being viewed by others
References
H. Okamoto and T.B. Massalski, eds., Binary Alloy Phase Diagrams, 2nd ed. (Materials Park, OH: American Society of Metals, 1990), pp. 527, 877, and 1467.
D. Josell, D. Wheeler, C. Witt, and T.P. Moffat, Electrochem. Solid-State Lett. 6, C143 (2003).
M.W. Lane, C.E. Murray, F.R. McFeely, P.M. Vereecken, and R. Rosenberg, Appl. Phys. Lett. 83, 2330 (2003).
R. Chan, T.N. Arunagiri, Y. Zhang, O. Chyan, R.M. Wallace, M.J. Kim, and T.Q. Hurd, Electrochem. Solid-State Lett. 7, G154 (2004).
T.N. Arunagiri, Y. Zhang, O. Chyan, M. El-Bouanani, M.J. Kim, K.H. Chen, C.T. Wu, and L.C. Chen, Appl. Phys. Lett. 86, 083104 (2005).
M. Damayanti, T. Sritharan, S.G. Mhaisalkar, and Z.H. Gan, Appl. Phys. Lett. 88, 044101 (2006).
C.W. Chen, J.S. Chen, and J.S. Jeng, J. Electrochem. Soc. 155, H438 (2008).
C.W. Chen, J.S. Chen, and J.S. Jeng, J. Electrochem. Soc. 155, H1003 (2008).
N. Tarazawa, T. Hinomura, K. Mori, Y. Koyama, S. Hirao, E. Kobori, H. Korogi, K. Maekawa, K. Tomita, H. Chibahara, N. Suzumura, K. Asai, H. Miyatake, and S. Matsumoto, International Interconnect Technology Conference, IEEE (2009), p. 113.
J.S. Fang, J.H. Lin, B.Y. Chen, and T.S. Chin, J. Electrochem. Soc. 158, H97 (2011).
T.Y. Lin, H.Y. Cheng, T.S. Chin, C.F. Chiu, and J.S. Fang, Appl. Phys. Lett. 91, 152908 (2007).
J.S. Fang, C.F. Chiu, J.H. Lin, and T.S. Chin, J. Electrochem. Soc. 156, H147 (2009).
T. Laurila, K. Zeng, J.K. Kivilahti, J. Molarius, and I. Suni, J. Appl. Phys. 91, 5391 (2002).
S.H. Kwon, O.K. Kwon, J.S. Min, and S.W. Kang, J. Electrochem. Soc. 153, G578 (2006).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Fang, J., Lin, J., Chen, B. et al. Low-Resistivity Ru-Ta-C Barriers for Cu Interconnects. J. Electron. Mater. 41, 138–143 (2012). https://doi.org/10.1007/s11664-011-1797-4
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-011-1797-4