Abstract
Metal–oxide–semiconductor (MOS) capacitors and MOS field-effect transistors (MOSFETs) fabricated on the carbon face of 4H-SiC were characterized following different postoxidation annealing methods used to passivate the oxide–semiconductor (O–S) interface. Of the various processes studied, sequential postoxidation annealing in NO followed by atomic hydrogen gave the lowest interface trap density (D it). Direct oxidation/passivation in NO yielded somewhat better I–V characteristics, though all passivation ambients produced approximately the same breakdown field strength. n-Channel MOSFETs showed high channel mobility at low field, which is likely caused by the presence of mobile ions at the O–S interface. Comparisons with the silicon face are presented for interface trap density, oxide breakdown field, and channel mobility. These comparisons suggest that the carbon face does not offer significant performance advantages.
Similar content being viewed by others
References
J.B. Casady and R.W. Johnson, Solid State Electron. 39, 1409 (1996).
J.C. Zolper, Solid State Electron. 42, 2153 (1998).
S. Dhar, S. Wang, J.R. Williams, S.T. Pantelides, and L.C. Feldman, Mater. Res. Bull. 30, 288 (2005).
J.A. Cooper Jr. and A. Agarwal, Proc. IEEE 90, 956 (2002).
G.Y. Chung, C.C. Tin, J.R. Williams, K. McDonald, M.D. Ventra, S.T. Pantelides, L.C. Feldman, and R.A. Weller, Appl. Phys. Lett. 76, 1713 (2000).
P. Jamet and S. Dimitrijev, Appl. Phys. Lett. 79, 323 (2001).
K. Fukuda, M. Kato, S. Harada, and K. Kojima, Mater. Sci. Forum 527, 1043 (2006).
S. Dhar, L.C. Feldman, S. Wang, T. Isaacs-Smith, and J.R. Williams, J. Appl. Phys. 98, 014902 (2005).
G.Y. Chung, C.C. Tin, J.R. Williams, K. McDonald, R.K. Chanana, R.A. Weller, S.T. Pantelides, L.C. Feldman, O.W. Holland, M.K. Das, and J.W. Palmour, IEEE Electron. Dev. Lett. 22, 176 (2001).
S.W. Wang, S. Dhar, S.R. Wang, A.C. Ahyi, A. Franceschetti, J.R. Williams, L.C. Feldman, and S.T. Pantelides, Phys. Rev. Lett. 98, 026101 (2007).
T.L. Biggerstaff, C.L. Reynolds, T. Zheleva, A. Lelis, D. Habersat, S. Haney, S.–H. Ryu, A. Agarwal, and G. Duscher, Appl. Phys. Lett. 95, 032108 (2009).
Y. Song, S. Dhar, L.C. Feldman, G. Chung, and J.R. Williams, J. Appl. Phys. 95, 4953 (2004).
Y.Q. Wu, P.D. Ye, M.A. Capano, Y. Xuan, Y. Sui, M. Qi, J.A. Cooper, T. Shen, D. Pandey, G. Prakash, and R. Reifenberger, Appl. Phys. Lett. 92, 092102 (2008).
J. Pernot, S. Contreras, J. Camassel, J.L. Robert, W. Zawadzki, E. Neyret, and L. Di Cioccio, Appl. Phys. Lett. 77, 4359 (2000).
G. Gudjonsson, H.O. Olafsson, F. Allerstam, P.A. Nilsson, E.O. Sveinbjornsson, H. Zirath, T. Rodle, and R. Jos, IEEE Electron. Dev. Lett. 26, 96 (2005).
Acknowledgements
This work was supported by ARL under Contract ARMY-W911NF-07-2-0046 (Aivars Lelis, Technical Program Manager), by TARDEC under Contract W56H2V-06-C-0228 (Terrence Burke, Technical Program Manager), by the Auburn University Space Research Institute, and by the Auburn University Natural Resources Management and Development Institute.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Chen, Z., Ahyi, A., Zhu, X. et al. MOS Characteristics of C-Face 4H-SiC. J. Electron. Mater. 39, 526–529 (2010). https://doi.org/10.1007/s11664-010-1096-5
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-010-1096-5