Room Temperature NO2 Gas Sensor Based on SnO2-WO3 Thin Films

  • Published:
Plasmonics Aims and scope Submit manuscript

Abstract

Metal oxide semiconductors (MOS) are important and promising materials in optoelectronics, and it has been widely used in various catalytic applications such as gas sensing due to its high reactivity with many gases. In current work, mixtures of SnO2-WO3 (1:1) were prepared to synthesize nanostructured thin films by pulsed laser deposition as gas sensors. The sensitivity of sensors was measured for a relatively low concentration (200 ppm) of NO2 gas at room temperature; sensors prepared with target exposed to (200) laser shots have higher sensitivity with a maximum value of 96.49 % at time 65 s as compared with the sensors prepared with (150) laser shots where the sensitivity has a maximum value 71.82 % at time 110 s; XRD pattern shows a better crystalline and high intensity with increasing laser shots up to 200; scanning electron microscopy (SEM) micrographs show approximate homogeneity of grains that cover the substrate without cracks and pinholes with nanoparticles fall in micro and nanometer range 50–200 nm. The values of the direct band gap were found to be 2.07143 eV for films prepared with 150 laser shots and 2.02899 eV for films prepared with 200 laser shots which have higher absorbance than the former films due to the increment in thickness and particle size. Empirical equations between sensitivity and gas exposure time have been formulated with great coincidence with the experimental data.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7

Similar content being viewed by others

References

  1. Potje-Kamloth K (2008) Semiconductor junction gas sensors. Chem Rev 108(2):367–399

    Article  CAS  Google Scholar 

  2. Williams DE (1999) Semiconducting oxides as gas-sensitive resistors. Sensors Actuators B Chem 57(1–3):1–16

    Article  CAS  Google Scholar 

  3. Liu L, Zhang T, Wang L, Li S (2009) Improved ethanol sensing properties of Cu-doped SnO2 nanofibers. Mater Lett 63(23):2041–2043

    Article  CAS  Google Scholar 

  4. Wang Y, Jia W, Strout T, et al. (2009) Ammonia gas sensor using polypyrrole-coated TiO2/ZnO nanofibers. Electroanalysis 21(12):1432–1438

    Article  CAS  Google Scholar 

  5. Sharma A, Tomar M, Gupta V (2011) SnO2 thin film sensor with enhanced response for NO2 gas at lower temperatures. Sensors Actuators B Chem 156.2(743–752)

  6. Chaudhari GN, Bende AM, Bodade AB, Patil SS, Sapkal VS (2006) Sensors Actuators B 115:297–302

    Article  CAS  Google Scholar 

  7. Deepa M, Srivastava A K, Sharma S N, Govind, Shivaprasad S M (2008) Appl Surf Sci 254:2342–2352

    Article  CAS  Google Scholar 

  8. Xie G, Yu J, Chen X, Jiang Y (2007) Sensors Actuators B 123:909–914

    Article  CAS  Google Scholar 

  9. Li PG, Guo X, Wang XF, Tang WH (2009) Facile route to straight SnO2 nanowires and their optical properties. J Alloys Compd 479:74–77

    Article  CAS  Google Scholar 

  10. Zhao J, Wu S, Liu J, Liu H, Gong S, Zhou D (2010) Tin oxide thin films prepared by aerosol-assisted chemical vapor deposition and the characteristics on gas detection. Sensors Actuators B 145:788–793

    Article  CAS  Google Scholar 

  11. Du HY, Wang J, Su MY, Yao PJ, Zheng YG, Yu NS (2012) Formaldehyde gas sensor based on SnO2/In2O3 hetero-nanofibers by a modified double jets electrospinning process. Sens. Actuators B Chem. 166:746–752

    Article  Google Scholar 

  12. Aksoy S, Caglar Y (2012) Effect of ambient temperature on electrical properties of nanostructure n-ZnO/p-Si heterojunction diode. Superlattice Microst 51:613–625

    Article  CAS  Google Scholar 

  13. Lv PW, Zheng WF, Lin LM, Peng FC, Huang ZG, Lai FC (2011) I-V characteristics of ZnO/Cu2O thin film n-i-p heterojunction. Phys B Condens Matter 406:1253–1257

    Article  CAS  Google Scholar 

  14. Chowdhuri A, Singh SK, Sreenivas K, Gupta V (2010) Contribution of adsorbed oxygen and interfacial space charge for enhanced response of SnO2 sensors having CuO catalyst for H2S gas. Sens. Actuators B Chem. 145:155–166

    Article  CAS  Google Scholar 

  15. Jain GH, Patil LA (2007) CuO-doped BSST thick film resistors for ppb level H2S gas sensing at room temperature. Sens. Actuators B Chem. 123:246–253

    Article  CAS  Google Scholar 

  16. Licznerski BW, Nitsch K, Teterycz H, Szecowka PM, Wisniewski K (1999) Humidity insensitive thick film methane sensor based on SnO2/Pt. Sens Actuators B Chem 57:192–196

    Article  CAS  Google Scholar 

  17. Cui GL, Gao L, Yao BB, Wang SM, Zhang PH, Zhang MZ (2013) Electrochemistry of CuO/In2O3 p-n heterojunction nano/microstructure array with sensitivity to H2 at and below room-temperature. Electrochem Commun 30:42–45

    Article  CAS  Google Scholar 

  18. Nayak AK, Ghosh R, Santra S, Guha PK, Pradhan D (2015) Hierarchical nanostructured WO3–SnO2 for selective sensing of volatile organic compounds. Nanoscale 7:12460

    Article  CAS  Google Scholar 

  19. Sahay PP, Tewari S, Nath RK (2007) Optical and electrical studies on spray deposited ZnO thin films. J Cryst Res Technol 42(7):723–729

    Article  CAS  Google Scholar 

  20. Haider AJ, Najim AA, Muhi MAH (2016) TiO2/Ni composite as antireflection coating for solar cell application. Opt Commun 370:263–266

    Article  CAS  Google Scholar 

  21. Sharma A, Tomar M, Gupta V (2012) Low temperature operating SnO2 thin film sensor loaded with WO3 micro-discs with enhanced response for NO2 gas. Sensors Actuators B 161:1114–1118

    Article  CAS  Google Scholar 

Download references

Acknowledgments

The authors gratefully acknowledge the Nanotechnology and Advanced Materials Research Centre, University of Technology, Baghdad, Iraq, for conducting all tests.

Author information

Authors and Affiliations

Authors

Corresponding author

Correspondence to Aus A. Najim.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Najim, A.A., Shaker, S.S. & Muhi, M.A.H. Room Temperature NO2 Gas Sensor Based on SnO2-WO3 Thin Films. Plasmonics 12, 1051–1055 (2017). https://doi.org/10.1007/s11468-016-0358-3

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s11468-016-0358-3

Keywords

Navigation