An investigation into the simultaneous influence of withdrawal speed and number of coated layers on photocatalytic activity of ZnO thin films

  • Original Paper: Functional coatings, thin films and membranes (including deposition techniques)
  • Published:
Journal of Sol-Gel Science and Technology Aims and scope Submit manuscript

Abstract

In this context, an investigation into the influence of withdrawal speed and number of coated layers of ZnO thin films on their photocatalytic activity has been performed, to study simultaneous effect of the two parameters. Zinc acetate dehydrate, isopropanol and monoethanol amine were used as starting materials and the films were deposited on soda lime glass substrates from a sol prepared through sol–gel route. Three levels of speeds (withdrawal speed = 3, 6, and 12 cm/min) and four levels of number of layers (number of coated layers = 10, 20, 30, and 40) have been applied, using a dip-coating technique, in deposition process. The structural properties of the samples have been studied using an X-ray diffractometer, field emission scanning electron microscope, and scanning probe microscopy. Estimation of coatings porosity has also been made using image analysis of large-scale field emission scanning electron microscope images. Photocatalytic dye degradation experiments revealed that, both parameters are of great significance. It was observed that, at constant number of coated layers of 10, the films prepared by withdrawal speed = 3 cm/min revealed a noticeably better removal of 39 % than the ones prepared by withdrawal speed = 12 cm/min. However, as the number of coated layers grew to 40, the significance of the withdrawal speed decreased. Therefore, at number of coated layers = 40 the difference of performance for thin films prepared by the highest and lowest withdrawal speed was found to be only 2 %, which indicates the dominant role of number of coated layers at higher withdrawal speeds. Since higher speeds are more convenient to be achieved, by improving the number of coated layers, thin films with better photocatalytic performance could be obtained more easily.

Graphical Abstract

This is a preview of subscription content, log in via an institution to check access.

Access this article

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7

Similar content being viewed by others

References

  1. Jalali N, Briscoe J, Tan YZ, Woolliams P, Stewart M, Weaver PM, Cain MG, Dunn S (2015) ZnO nanorod surface modification with PDDA/PSS Bi-layer assembly for performance improvement of ZnO piezoelectric energy harvesting devices. J Sol-Gel Sci Technol 73(3):544–549

    Article  Google Scholar 

  2. Senthil T, Kim A-Y, Muthukumarasamy N, Kang M (2013) Improved performance of dye sensitized ZnO nanorod solar cells prepared using TiO2 seed layer. J Sol-Gel Sci Technol 67(2):420–427

    Article  Google Scholar 

  3. Hendi A, Alorainy R, Yakuphanoglu F (2014) Humidity sensing characteristics of Sn doped Zinc oxide based quartz crystal microbalance sensors. J Sol-Gel Sci Technol 72(3):559–564

    Article  Google Scholar 

  4. Khodadadi B, Bordbar M, Yeganeh-Faal A (2016) Optical, structural, and photocatalytic properties of Cd-doped ZnO powders prepared via sol–gel method. J Sol-Gel Sci Technol 77(3):521–527

  5. Talebian N, Nilforoushan MR, Memarnezhad P (2013) Photocatalytic activities of multilayered ZnO-based thin films prepared by sol–gel route: effect of SnO2 heterojunction layer. J Sol-Gel Sci Technol 65(2):178–188

    Article  Google Scholar 

  6. Chan Y-L, Pung S-Y, Sreekantan S (2013) Degradation of organic dye using ZnO nanorods based continuous flow water purifier. J Sol-Gel Sci Technol 66(3):399–405

    Article  Google Scholar 

  7. Sudha M, Senthilkumar S, Hariharan R, Suganthi A, Rajarajan M (2013) Synthesis, characterization and study of photocatalytic activity of surface modified ZnO nanoparticles by PEG capping. J Sol-Gel Sci Technol 65(3):301–310

    Article  Google Scholar 

  8. Hernández A, Maya L, Sánchez-Mora E, Sánchez EM (2007) Sol-gel synthesis, characterization and photocatalytic activity of mixed oxide ZnO-Fe2O3. J Sol-Gel Sci Technol 42(1):71–78

    Article  Google Scholar 

  9. Spanhel L (2006) Colloidal ZnO nanostructures and functional coatings: a survey. J Sol-Gel Sci Technol 39(1):7–24

    Article  Google Scholar 

  10. Dong B, Li Z, Li Z, Xu X, Song M, Zheng W, Wang C, Al-Deyab SS, El-Newehy M (2010) Highly efficient LaCoO3 nanofibers catalysts for photocatalytic degradation of Rhodamine B. J Am Ceram Soc 93(11):3587–3590. doi:10.1111/j.1551-2916.2010.04124.x

    Article  Google Scholar 

  11. Gao B, Fu J, Huo K, Zhang W, Xie Y, Chu PK (2011) Quasi-aligned Ag–Nb2O5 nanobelt arrays with enhanced photocatalytic and antibacterial activities. J Am Ceram Soc 94(8):2330–2338. doi:10.1111/j.1551-2916.2010.04370.x

    Article  Google Scholar 

  12. Talebian N, Nilforoushan MR, Ghasem RR (2012) Enhanced photocatalytic activities of ZnO thin films: a comparative study of hybrid semiconductor nanomaterials. J Sol-Gel Sci Technol 64(1):36–46

    Article  Google Scholar 

  13. Fortunato E, Barquinha P, Martins R (2012) Oxide Semiconductor thin-film transistors: a review of recent advances. Adv Mater 24(22):2945–2986. doi:10.1002/adma.201103228

    Article  Google Scholar 

  14. Benhaliliba M, Benouis C, Aida M, Yakuphanoglu F, Juarez AS (2010) Indium and aluminium-doped ZnO thin films deposited onto FTO substrates: nanostructure, optical, photoluminescence and electrical properties. J Sol-Gel Sci Technol 55(3):335–342

    Article  Google Scholar 

  15. Bouznit Y, Beggah Y, Djessas K (2012) RF magnetron sputtering of ZnO and Al-doped ZnO films from ceramic and nanopowder targets: a comparative study. J Sol-Gel Sci Technol 61(2):449–454

    Article  Google Scholar 

  16. Kamata K, Nishino J, Ohshio S, Maruyama K, Ohtuki M (1994) Rapid formation of zinc oxide films by an atmospheric-pressure chemical vapor deposition method. J Am Ceram Soc 77(2):505–508. doi:10.1111/j.1151-2916.1994.tb07021.x

    Article  Google Scholar 

  17. Huang M-C, Wang T, Wu B-J, Lin J-C, Wu C-C (2016) Anodized ZnO nanostructures for photoelectrochemical water splitting. Appl Surf Sci 360(Part B):442–450. doi:10.1016/j.apsusc.2015.09.174

    Article  Google Scholar 

  18. Torres Delgado G, Zúñiga Romero CI, Mayén Hernández SA, Castanedo Pérez R, Zelaya Angel O (2009) Optical and structural properties of the sol–gel-prepared ZnO thin films and their effect on the photocatalytic activity. Sol Energ Mat Sol Cells 93(1):55–59. doi:10.1016/j.solmat.2008.03.020

    Article  Google Scholar 

  19. Cruz MA, Hernandez-Como N, Mejia I, Ortega-Zarzosa G, Martínez-Castañón G-A, Quevedo-Lopez MA (2016) Impact of the annealing atmosphere in the electrical and optical properties of ZnO thin films. J Sol-Gel Sci Technol 79(1):184–189

  20. Thein MT, Pung S-Y, Aziz A, Itoh M (2015) Stacked ZnO nanorods synthesized by solution precipitation method and their photocatalytic activity study. J Sol-Gel Sci Technol 74(1):260–271

    Article  Google Scholar 

  21. Kayani ZN, Kiran F, Riaz S, Zia R, Naseem S (2015) Dip coated nickel zinc oxide thin films: structural, optical and magnetic investigations. Superlattice Microst 77:171–180

    Article  Google Scholar 

  22. Aydemir S, Karakaya S (2015) Effects of withdrawal speed on the structural and optical properties of sol–gel derived ZnO thin films. J Magn Magn Mater 373:33–39

    Article  Google Scholar 

  23. Aydemir S (2015) Effects of withdrawal speed on the microstructural and optical properties of sol–gel grown ZnO: Al thin films. Vacuum 120:51–58

    Article  Google Scholar 

  24. Rosas-Barrera K, Ropero-Vega J, Pedraza-Avella J, Nino-Gomez M, Pedraza-Rosas J, Laverde-Catano D (2011) Photocatalytic degradation of methyl orange using Bi2MNbO7 (M= Al, Fe, Ga, In) semiconductor films on stainless steel. Catal Today 166(1):135–139

    Article  Google Scholar 

  25. Jongnavakit P, Amornpitoksuk P, Suwanboon S, Ratana T (2012) Surface and photocatalytic properties of ZnO thin film prepared by sol–gel method. Thin Solid Films 520(17):5561–5567

    Article  Google Scholar 

  26. Zhang Y, Gao F, Gao L, Hou L, Jia Y (2012) Study of tri-layer antireflection coatings prepared by sol–gel method. J Sol-Gel Sci Technol 62(2):134–139

    Article  Google Scholar 

  27. Stathatos E, Petrova T, Lianos P (2001) Study of the efficiency of visible-light photocatalytic degradation of basic blue adsorbed on pure and doped mesoporous titania films. Langmuir 17(16):5025–5030

    Article  Google Scholar 

  28. Addamo M, Augugliaro V, Di Paola A, Garcia-Lopez E, Loddo V, Marci G, Palmisano L (2008) Photocatalytic thin films of TiO2 formed by a sol–gel process using titanium tetraisopropoxide as the precursor. Thin Solid Films 516(12):3802–3807

    Article  Google Scholar 

  29. Chen D, Li F, Ray AK (2000) Effect of mass transfer and catalyst layer thickness on photocatalytic reaction. AIChE J 46(5):1034–1045

    Article  Google Scholar 

  30. Bel Hadj Tahar N, Bel Hadj Tahar R, Ben Salah A, Savall A (2008) Effects of individual layer thickness on the microstructure and optoelectronic properties of sol–gel-derived zinc oxide thin films. J Am Ceram Soc 91(3):846–851. doi:10.1111/j.1551-2916.2007.02221.x

    Article  Google Scholar 

  31. Chen Y, Stathatos E, Dionysiou DD (2008) Microstructure characterization and photocatalytic activity of mesoporous TiO2 films with ultrafine anatase nanocrystallites. Surf Coat Technol 202(10):1944–1950

    Article  Google Scholar 

  32. Musat V, Rego A, Monteiro R, Fortunato E (2008) Microstructure and gas-sensing properties of sol–gel ZnO thin films. Thin Solid Films 516(7):1512–1515

    Article  Google Scholar 

  33. Negishi N, Matsuzawa S, Takeuchi K, Pichat P (2007) Transparent micrometer-thick TiO2 films on SiO2-coated glass prepared by repeated dip-coating/calcination: characteristics and photocatalytic activities for removing acetaldehyde or toluene in air. Chem Mater 19(15):3808–3814

    Article  Google Scholar 

  34. Mehrotra K, Yablonsky GS, Ray AK (2005) Macro kinetic studies for photocatalytic degradation of benzoic acid in immobilized systems. Chemosphere 60(10):1427–1436

    Article  Google Scholar 

  35. Kaneva N, Bojinova A, Papazova K, Dimitrov D, Svinyarov I, Bogdanov M (2015) Effect of thickness on the photocatalytic properties of ZnO thin films. Bulg ChemCommun 47(1):395–401

    Google Scholar 

  36. Lv J, Gong W, Huang K, Zhu J, Meng F, Song X, Sun Z (2011) Effect of annealing temperature on photocatalytic activity of ZnO thin films prepared by sol–gel method. Superlattice Microst 50(2):98–106

    Article  Google Scholar 

  37. Jongnavakit P, Amornpitoksuk P, Suwanboon S, Ndiege N (2012) Preparation and photocatalytic activity of Cu-doped ZnO thin films prepared by the sol–gel method. Appl Surf Sci 258(20):8192–8198

    Article  Google Scholar 

  38. Moongraksathum B, Chen Y-W (2016) Preparation and characterization of SiO2–TiO2 neutral sol by peroxo sol–gel method and its application on photocatalytic degradation. J Sol-Gel Sci Technol 77(2):288–297

  39. Neogi SK, Ghosh R, Paul GK, Bera SK, Bandyopadhyay S (2009) Effects of Co doping on structural, morphological and transport properties of sol–gel AZO thin films. J Alloy Compd 487(1–2):269–273. doi:10.1016/j.jallcom.2009.07.118

    Article  Google Scholar 

  40. Javadi S, Masoudpanah SM, Zakeri A (2016) Conventional versus microwave combustion synthesis of CoFe2O4 nanoparticles. J Sol-Gel Sci Technol 79(1):176–183

  41. Hwang J, Shoji N, Endo A, Daiguji H (2014) Effect of withdrawal speed on film thickness and hexagonal pore-array dimensions of SBA-15 mesoporous silica thin film. Langmuir 30(51):15550–15559

    Article  Google Scholar 

  42. Faustini M, Louis B, Albouy PA, Kuemmel M, Grosso D (2010) Preparation of sol−gel films by dip-coating in extreme conditions. J Phys Chem C 114(17):7637–7645. doi:10.1021/jp9114755

    Article  Google Scholar 

  43. Thongsuriwong K, Amornpitoksuk P, Suwanboon S (2013) Structure, morphology, photocatalytic and antibacterial activities of ZnO thin films prepared by sol–gel dip-coating method. Adv Powder Technol 24(1):275–280. doi:10.1016/j.apt.2012.07.002

    Article  Google Scholar 

Download references

Acknowledgments

The authors would like to express special thanks to Mr. Sajjad Alavi for his technical assistance and 90iha group for their moral support.

Author information

Authors and Affiliations

Authors

Corresponding author

Correspondence to Hamed Bazrafshan.

Ethics declarations

Conflict of interest

The authors declare that they have no competing interests.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Alavi, S., Bazrafshan, H. & Nikazar, M. An investigation into the simultaneous influence of withdrawal speed and number of coated layers on photocatalytic activity of ZnO thin films. J Sol-Gel Sci Technol 81, 652–661 (2017). https://doi.org/10.1007/s10971-016-4230-x

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s10971-016-4230-x

Keywords

Navigation