Structural and optical characterization of ZnO and AZO thin films: the influence of post-annealing

  • Published:
Journal of Materials Science: Materials in Electronics Aims and scope Submit manuscript

Abstract

In the present study, ZnO and Al:ZnO (AZO) thin films were prepared by reactive RF sputtering on quartz substrates at a constant oxygen partial pressure and a typical sputtering power. Films were annealed at different temperatures in argon ambient in the oven to study their various structural and optical properties. It was understood that introducing Al into ZnO structure would affect the ZnO crystalline structure noticeably. It was observed that annealing had great influence on various properties of thin films while ZnO film showed low crystallinity, Al doping into ZnO structure pronounced significant improvement in both crystallinity and particle sizes. It was found that crystal structures, average crystalline sizes, and topology of all thin films were modified enormously by post-annealing. It was shown that films transparency fluctuated by annealing, in which the transparency of AZO thin film annealed at 500 °C was much greater than others. Annealing led to decrease optical band gap of all annealed films from 3.31 to 3.26 eV for ZnO and 4 to 3.4 eV for AZO films. Photoluminescence manifested that blue emission in as-deposited film led to two different blue and violet emissions in all AZO and ZnO films. It was identified that the emission intensity of AZO film annealed at 500 °C was 12 times more than other ZnO and AZO films.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10
Fig. 11

Similar content being viewed by others

References

  1. X.-H. Lu, D. Wang, G.-R. Li, C.-Y. Su, D.-B. Kuang, Y.-X. Tong, Controllable electrochemical synthesis of hierarchical ZnO nanostructures on FTO Glass. J. Phys. Chem. C 113, 13574–13582 (2009)

    Article  Google Scholar 

  2. L. Zhang, K. Jin, S. Li, L. Wang, Y. Zhang, X. Li, Synthesis of flower-Like ZnO films and their photovoltaic properties for dye-sensitized solar cells. J. Electr. Mater. 44, 244–251 (2015)

    Article  Google Scholar 

  3. K. Pradhan, R.M. Mundle, K. Santiago, J.R. Skuza, B. Xiao, K.D. Song, M. Bahoura, R. Cheaito, P.E. Hopkins, Extreme tunability in aluminum doped Zinc Oxide plasmonic materials for near-infrared applications, Sci. Rep. 4 (2014)

  4. T. Minami, Y. Nishi, T. Miyata, Effect of the thin Ga2O3 layer in n + -ZnO/n-Ga2O3/p-Cu2O heterojunction solar cells. Thin Solid Films 549, 65–69 (2013)

    Article  Google Scholar 

  5. H. Masui, S. Nakamura, S.P. DenBaars, U.K. Mishra, Nonpolar and semipolar iii-nitride light-emitting diodes: achievements and challenges. Electron Devices IEEE Trans. 57, 88–100 (2010)

    Article  Google Scholar 

  6. X. Jiang, F.L. Wong, M.K. Fung, S.T. Lee, Aluminum-doped zinc oxide films as transparent conductive electrode for organic light-emitting devices. Appl. Phys. Lett. 83, 1875–1877 (2003)

    Article  Google Scholar 

  7. L. Chow, O. Lupan, G. Chai, H. Khallaf, L.K. Ono, B. Roldan Cuenya, I.M. Tiginyanu, V.V. Ursaki, V. Sontea, A. Schulte, Synthesis and characterization of Cu-doped ZnO one-dimensional structures for miniaturized sensor applications with faster response. Sens. Actuators A 189, 399–408 (2013)

    Article  Google Scholar 

  8. W. Li, J. Chen, H. Cui, F. Liu, X. Hao, Inhibiting MoS2 formation by introducing a ZnO intermediate layer for Cu2ZnSnS4 solar cells. Mater. Lett. 130, 87–90 (2014)

    Article  Google Scholar 

  9. P. Yang, H. Yan, S. Mao, R. Russo, J. Johnson, R. Saykally, N. Morris, J. Pham, R. He, J.H. Choi, Controlled growth of ZnO nanowires and their optical properties. Adv. Funct. Mater. 12, 323 (2002)

    Article  Google Scholar 

  10. S. Sadjadi, M. Eskandari, Ultrasonic assisted synthesis of imidazo[1,2-a]azine catalyzed by ZnO nanorods. Ultrason. Sonochem. 20, 640–643 (2013)

    Article  Google Scholar 

  11. Z. Zang, M. Wen, W. Chen, Y. Zeng, Z. Zu, X. Zeng, X. Tang, Strong yellow emission of ZnO hollow nanospheres fabricated using polystyrene spheres as templates. Mater. Des. 84, 418–421 (2015)

    Google Scholar 

  12. Z. Zang, X. Tang, Enhanced fluorescence imaging performance of hydrophobic colloidal ZnO nanoparticles by a facile method 619, 98–101 (2015)

    Google Scholar 

  13. Y. Sun, D.J. Riley, M.N.R. Ashfold, Mechanism of ZnO nanotube growth by hydrothermal methods on ZnO film-coated Si substrates. J. Phys. Chem. B 110, 15186–15192 (2006)

    Article  Google Scholar 

  14. S. Ţălu, S. Stach, S. Solaymani, R. Moradian, A. Ghaderi, M.R. Hantehzadeh, S.M. Elahi, Ż. Garczyk, S. Izadyar, Multifractal spectra of atomic force microscope images of Cu/Fe nanoparticles based films thickness. J. Electroanal. Chem. 749, 31–41 (2015)

    Article  Google Scholar 

  15. S. Ţălu, S. Stach, T. Ghodselahi, S. Solaymani, A. Ghaderi, A. Boochani, Ż. Garczyk, Topographic characterization of Cu–Ni NPs @ a-C: H films by AFM and multifractal analysis. J Phys. Chem. B 119(17), 5662–5670 (2015)

    Article  Google Scholar 

  16. S.T. Tan, B.J. Chen, X.W. Sun, W.J. Fan, H.S. Kwok, X.H. Zhang, S.J. Chua, Blueshift of optical band gap in ZnO thin films grown by metal-organic chemical-vapor deposition, J. Appl. Phys. 98 (2005)

  17. A. Ghaderi, S.M. Elahi, S. Solaymani, M. Naseri, M. Ahmadirad, S. Bahrami, A.E. Khalili, Thickness dependence of the structural and electrical properties of ZnO thermal-evaporated thin films. PRAMANA J. Phys 77(6), 1–8 (2011)

    Article  Google Scholar 

  18. P. Jin, S. Nakao, S.X. Wang, L.M. Wang, Localized epitaxial growth of α-Al2O3 thin films on Cr2O3 template by sputter deposition at low substrate temperature. Appl. Phys. Lett. 82, 1024–1026 (2003)

    Article  Google Scholar 

  19. T.L. Yang, D.H. Zhang, J. Ma, H.L. Ma, Y. Chen, Transparent conducting ZnO: Al films deposited on organic substrates deposited by r.f. magnetron-sputtering. Thin Solid Films 326, 60–62 (1998)

    Article  Google Scholar 

  20. Y. Lin, J. Xie, H. Wang, Y. Li, C. Chavez, S. Lee, S.R. Foltyn, S.A. Crooker, A.K. Burrell, T.M. McCleskey, Q.X. Jia, Green luminescent zinc oxide films prepared by polymer-assisted deposition with rapid thermal process. Thin Solid Films 492, 101–104 (2005)

    Article  Google Scholar 

  21. L.B. Duan, X.R. Zhao, J.M. Liu, W.C. Geng, H.Y. Xie, H.N. Sun, Effect of annealing ambient on the structural, optical and electrical properties of (Mg, Al)-codoped ZnO thin films. Phys. Scr. 85, 035709 (2012)

    Article  Google Scholar 

  22. Z. Liang, X. Yu, B. Lei, P. Liu, W. Mai, Novel blue-violet photoluminescence from sputtered ZnO thin films. J. Alloy. Compd. 509, 5437–5440 (2011)

    Article  Google Scholar 

  23. S. Cho, J. Ma, Y. Kim, Y. Sun, G.K.L. Wong, J.B. Ketterson, Photoluminescence and ultraviolet lasing of polycrystalline ZnO thin films prepared by the oxidation of the metallic Zn. Appl. Phys. Lett. 75, 2761–2763 (1999)

    Article  Google Scholar 

  24. H. Chen, H.-J. Jin, C.-B. Park, Influence of hydrogen on Al-doped ZnO thin films in the process of deposition and annealing. Trans. Electr. Electron. Mater. 10, 93–96 (2009)

    Article  Google Scholar 

  25. E.S. Shim, H.S. Kang, S.S. Pang, J.S. Kang, I. Yun, S.Y. Lee, Annealing effect on the structural and optical properties of ZnO thin film on InP. Mater. Sci. Eng. B 102, 366–369 (2003)

    Article  Google Scholar 

  26. F.K. Shan, G.X. Liu, W.J. Lee, B.C. Shin, The role of oxygen vacancies in epitaxial-deposited ZnO thin films. J. Appl. Phys. 101, 053106 (2007)

    Article  Google Scholar 

  27. B.D. Cuility, Elements of X-ray Diffraction (Addison-Wesley, Reading, Mass, 1959)

    Google Scholar 

  28. P. Chand, A. Gaur, A. Kumar, Structural, optical and ferroelectric behavior of CuO nanostructures synthesized at different pH values. Superlattices Microstruct. 60, 129–138 (2013)

    Article  Google Scholar 

  29. H. Morkoç, U. Özgür, Zinc oxide fundamentals, materials and device technology (Wiley-VCH, Weinheim, 2009)

    Google Scholar 

  30. J.M. Yuk, J.W. Shin, J.Y. Lee, D.I. Son, J.H. Jung, T.W. Kim, J.Y. Kim, W.K. Choi, Effect of thermal annealing on the formation of preferential c-axis orientation and an interfacial layer for ZnO thin films grown on an n-Si (001) substrate. J. Korean Phys. Soc. 50, 4 (2007)

    Google Scholar 

  31. S. Salleh, M.N. Dalimin, H.N. Rutt, Structural and surface characterization of cold deposited zinc sulfide thin films, in 3rd International Conference on Solid State Science and Technology (ICSSST2010), Universiti Malaysia Sarawak, 2010

  32. K.-S. Hwang, Y.-J. Lee, S. Hwangbo, Growth, structure and optical properties of amorphous or nano-crystalline ZnO thin films prepared by prefiring-final annealing. J. Ceram. Process. Res. 8, 7 (2007)

    Google Scholar 

  33. M. Fox, Optical properties of solids (OUP, Oxford, 2010)

    Google Scholar 

  34. J. Tauc, R. Grigorovici, A. Vancu, Optical properties and electronic structure of amorphous Germanium. Phys. Status Solidi 15, 627–637 (1966)

    Article  Google Scholar 

  35. M.H. Cohen, H. Fritzsche, S.R. Ovshinsky, Simple band model for amorphous semiconducting alloys. Phys. Rev. Lett. 22, 1065–1068 (1969)

    Article  Google Scholar 

  36. Y. Lin, J. Xie, H. Wang, Y. Li, C. Chavez, S. Lee, S.R. Foltyn, S.A. Crooker, A.K. Burrell, T.M. McCleskey, Q.X. Jia, Thin Solid Films 101, 492 (2005)

    Google Scholar 

  37. Sunglae Cho, Jing Ma, Yunki Kim, Yi Sun, G.K.L. George, J.B. Ketterson, Appl. Phys. Lett. 75, 2761 (1999)

    Article  Google Scholar 

Download references

Author information

Authors and Affiliations

Authors

Corresponding author

Correspondence to S. Mohammad Elahi.

Ethics declarations

Conflict of interest

The authors report no conflict of interests. The authors alone are responsible for the content and writing of the paper.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Dejam, L., Mohammad Elahi, S., Nazari, H.H. et al. Structural and optical characterization of ZnO and AZO thin films: the influence of post-annealing. J Mater Sci: Mater Electron 27, 685–696 (2016). https://doi.org/10.1007/s10854-015-3804-7

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s10854-015-3804-7

Keywords

Navigation