Abstract
(1 − x)Nd(Co1/2Ti1/2)O3(NCT)–xCa0.8Sr0.2TiO3(CST) composite ceramics were prepared by the conventional solid-state reaction process. From the X-ray diffraction analysis, it indicates that the Nd(Co1/2Ti1/2)O3 phase coexists with Ca0.8Sr0.2TiO3 phase, and it is easy for the cobalt volatilization to form second-phase Nd2Ti2O7 as x = 0.5 and 0.7. As the content of CST increases from 0.1 to 0.9, the dielectric constant of the (1 − x)Nd(Co1/2Ti1/2)O3–xCa0.8Sr0.2TiO3 composite ceramics increases from 29.3 to 114.7, the Q × f value decreases from 60,000 to 8,500 GHz, and the τ f value varies from −33.8 to 271 ppm/oC. A near zero τ f could be achieved at 0.5NCT–0.5CST ceramics with ε r = 44.5 and Q × f = 20,000 (GHz) sintered at 1,340 °C for 4 h.
Similar content being viewed by others
References
Tseng CF, Hsu CH, Huang CL (2007) J Am Ceram Soc 90:1619
Seabra MP, Avdeev M, Ferreira VM, Pullar RC, Alford McNN (2003) J Eur Ceram Soc 23:2403
Hsu CS, Huang CL, Tseng JF, You CC (2004) Ceram Int 30:2067
Wise PL, Reaney IM, Lee WE, Price TJ, Iddles DM, Cannell DS (2001) J Eur Ceram Soc 21:1723
Yoon KH, Kim WS, Kim ES (2003) Mater Sci Eng B99:112
Huang CL, Liu SS (2008) Mater Lett 62:3205
Wakino K (1989) Ferroelectrics 91:69
Hakki BW, Coleman PD (1960) IEEE Trans Microw Theory Tech 8:402
Courtney WE (1970) IEEE Trans Microw Theory Tech 18:476
Bain JJ, Song GX, Yan K (2008) Ceram Int 34:893
Saagala DA, Nambu S (1992) J Am Ceram Soc 75:2573
Acknowledgement
This work was sponsored by the National Science Council of the Republic of China under grant NSC 99-2221-E-239-018.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Tseng, CF., Huang, CC. Microwave dielectric properties of (1 − x)Nd(Co1/2Ti1/2)O3–x(Ca0.8Sr0.2)TiO3 composite ceramics. J Mater Sci 47, 3982–3988 (2012). https://doi.org/10.1007/s10853-012-6251-3
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-012-6251-3