Effect of tacticity on the cyclization of polyacrylonitrile copolymers

  • Original Contribution
  • Published:
Colloid and Polymer Science Aims and scope Submit manuscript

Abstract

This work investigated polyacrylonitrile copolymers synthesized using methyl acrylate (MA) and dimethyl itaconate (DMI) as second monomers by bulk polymerization in the presence of magnesium chloride as a reagent to control the tacticity of polyacrylonitrile copolymers. The copolymers synthesized by solution polymerization were used as a control group to study the tacticity effect. The 13C-NMR results confirm that the isotacticity by bulk polymerization is increased approximately double for either P(AN-co-MA) or P(AN-co-DMI). The X-ray diffraction (XRD) and the isothermal DSC results show that the P(AN-co-MA) produced by bulk process, as compared to that by solution polymerization, has higher domain size (L c ) and crystallinity (CI); moreover, its cyclization period is decreased significantly. It indicates that the increase of isotacticity for P(AN-co-MA) makes the crystalline domain larger and the cyclization takes place more easily. However, such positive correlations do not hold good for the P(AN-co-DMI) system. It is due to the high steric-hindrance effect for the DMI monomer, which has long reactive branches on both sides of the vinyl DMI monomer, complicating the mechanisms of crystallization and cyclization and resulting in diminishing the contribution of high isotacticity to lower the barrier of cyclization reaction.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10

Similar content being viewed by others

References

  1. Rwei SP, Way TF, Hsu YS (2013) Kinetics of cyclization reaction in poly(acrylonitrile/methyl acrylate/dimethyl itaconate) copolymer determined by a thermal analysis. Polym Degrad Stab 98:2072–2080

    Article  CAS  Google Scholar 

  2. Bahl OP, Mathur RB, Kundra KD (1981) Structure of PAN fibers and its relationship with resulting carbon fiber properties. Fiber Sci Technol 15:147–151

    Article  CAS  Google Scholar 

  3. Yang MC, Yu DG (1996) Influence of precursor structure on the properties of polyacrylonitrile-based activated carbon hollow fiber. J Appl Polym Sci 59:1725e31

    Article  Google Scholar 

  4. Donnet JB, Bansal RC (1990) Carbon fibers, 2nd edn. Marcel Dekker Inc., New York

    Google Scholar 

  5. Ouyang Q, Cheng L, Wang HJ, Li KX (2008) Mechanism and kinetics of the stabilization reactions of itaconic acid-modified polyacrylonitrile. Polym Degrad Stab 93:1415–1421

    Article  CAS  Google Scholar 

  6. Preta IFC, Sakata SK, Garcia G, Zimmermann JP, Galembeck F, Giovedi C (2007) Thermal behavior of polyacrylonitrile polymers synthesized under different conditions and comonomer compositions. J Therm Anal Calorim 87:657–659

    Article  Google Scholar 

  7. Sen K, Bajaj P, Speekumar TV (2003) Thermal behavior of drawn acrylic fibers. J Polym Sci B Polym Phys 41:2949–2958

    Article  CAS  Google Scholar 

  8. Devasia R, Reghunadhan Nair CP, Sivadasan P, Katherine BK, Ninan KN (2003) Cyclization reaction in poly(acrylonitrile/itaconic acid) copolymer: an isothermal differential scanning calorimetry kinetic study. J App Polym Sci 88:915–920

    Article  CAS  Google Scholar 

  9. Lei D, Devarayan K, Li X-D, Choi W-K, Seo M-K, Kim B-S (2014) Effects of comonomer with carboxylic group on stabilization of high molecular weight polyacrylonitrile nanofibrous copolymer. Carbon Letters 15:290–294

    Article  Google Scholar 

  10. Morgan P (2005) Carbon fibers and their composites. CRC Press, Taylor & Francis group, LLC, USA, pp. 125–126

    Book  Google Scholar 

  11. Coleman MM, Sivy GT, Painter PC, Snyder RW, Gordon III B (1983) Studies of the degradation of acrylonitrile/acrylamide copolymers as a function of composition and temperature. Carbon 21:255–267

    Article  CAS  Google Scholar 

  12. Chen SS, Herms J, Peebles Jr LH, Uhlmann DR (1981) Oxidative stabilization of acrylic fibres. J Mater Sci 16:1490–1510

    Article  CAS  Google Scholar 

  13. Bashir Z, Manns G, Service D. M, Bott DC, Herbert IR, Ibbett RN, Church SP (1991) Investigation of base induced cyclization and methine proton abstraction in polyacrylonitrile solutions. Polymer 32:1826–1833

    Article  CAS  Google Scholar 

  14. Minagawa M, Yamada H, Yamaguchi K, Yoshii F (1992) Gamma-ray irradiation canal polymerization conditions ensuring highly stereoregular (>80%) polyacrylonitrile. Macromolecules 25:503–510

    Article  CAS  Google Scholar 

  15. Jiang J, Lu X, Lu Y (2010) Preparation of polyacrylonitrile with improved isotacticity and low polydispersity. J Appl Polym Sci 116:2610–2616

    CAS  Google Scholar 

  16. Lutz J-F, Neugebauer D, Matyjaszewski K (2003) Stereoblock copolymers and tacticity control in controlled/living radical polymerization. J Am Chem Soc 2003(125):6986–6993

    Article  Google Scholar 

  17. Kuwabara H., Matsumura S. (2006) Japan patent publication No. JP2006-036908

  18. Biroš J, Larina T, Trekoval J, Pouchlý J (1982) Dependence of the glass transition temperature of poly (methyl methacrylates) on their tacticity. Colloid Polym Sci 260:27–30

    Article  Google Scholar 

  19. Minagawa M, Okada Y, Nouchi K, Sato Y, Yoshii F (2000) Tacticity, molecular weight, and molecular-weight-distribution relationships in stereoregular polyacrylonitrile prepared by electron beam irradiation canal polymerization. Colloid Polym Sci 278:757–763

    Article  CAS  Google Scholar 

  20. Krishnan SG, Burkanudeen A, Murali N, Phadnis H (2012) Facile synthesis of stereoregular carbon fiber precursor polymers by template assisted solid phase polymerization. Express Polymer Letts 6:729–738

    Article  Google Scholar 

  21. Ma J, Chen H, Zhang M, Wang C, Zhang Y, Qu R (2012) Use of Yb-based catalyst for AGET ATRP of acrylonitrile to simultaneously control molecular mass distribution and tacticity. Mater Sci Eng C 32:1699–1703

    Article  CAS  Google Scholar 

  22. Dalton S, Heatley F, Budd PM (1999) Thermal stabilization of polyacrylonitrile fibres. Polymer 40:5531–5543

    Article  CAS  Google Scholar 

Download references

Acknowledgements

The authors would like to thank the Ministry of Science and Technology of the Republic of China, Taiwan, for financially supporting this research under Contract No. MOST 104-2221-E-027-078-MY3.

Author information

Authors and Affiliations

Authors

Corresponding author

Correspondence to Syang-Peng Rwei.

Ethics declarations

Conflict of interest

The authors declare that they have no conflict of interest.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Rwei, SP., Way, TF., Chiang, WY. et al. Effect of tacticity on the cyclization of polyacrylonitrile copolymers. Colloid Polym Sci 295, 803–815 (2017). https://doi.org/10.1007/s00396-017-4062-4

Download citation

  • Received:

  • Revised:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s00396-017-4062-4

Keywords

Navigation