The catalytic activity of space versus terrestrial synthesized zeolite Beta catalysts in the Meerwein Ponndorf Verley Reactions: Support for PFAL as the Lewis active site for cis-alcohol selectivity

  • Published:
Microgravity - Science and Technology Aims and scope Submit manuscript

Abstract

The Lewis activity of the Meerwein-Ponndorf-Verley (MPV) reactions is hypothesized to be due to partial framework aluminum (PFAl) that is either octahedrally or tri-coordinated. Crystals grown in the free-fall environment of low earth orbit (LEO) are more uniform; that is, have fewer lattice “defects” compared to those grown in a gravity field (i.e., on earth). Therefore, crystals grown in orbit should be less catalytically active relative to their earth grown counterparts. The catalytic activity towards the MPV reaction, and the associated IR and XPS spectrum for zeolite Beta that was synthesized on earth (1g) and aboard the International Space Station (10−3–10−5g) were compared in their as-synthesized forms, and after applying heat treatment protocols designed to stress the crystal structure to generate Lewis acid sites (i.e., tri and octahedrally coordinated PFAl). The activity of the MPV reaction and cis-alcohol selectivity over the heat-treated flight samples was observed to be lower than the identically heat-treated terrestrial zeolite Beta samples. Higher MPV activity as well as cis-alcohol selectivity is related to both a higher number of partial framework Al atoms (PFAl), and a constrained pore volume. As PFAl are created by the destruction of the framework upon heat treatment, flight samples were shown to be thermally more stable with fewer lattice defects and less associated stress in zeolite Beta crystals. The changes observed in the IR spectra, as well as the XPS Al Auger and 2p peaks, of the terrestrial samples support this conclusion. Additionally, the flight samples showed higher tr-alcohol selectivity, which implies more pore volume and less channel blockage. This is consistent with the fact that crystals grown in space have less stress, fewer lattice defects, and thus there are fewer channel obstructions.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. Creyghton, E.J., Ganeshie, S.D., Downing, R.S., van Bekkum, H.: Stereoselective reduction of 4-tert-butylcyclohexanone tocis-4-tert-butyl-cyclohexanol catalysed by zeolite BEA. J. Chem. Soc. Chem. Commun. p. 1859 (1995)

  2. Jansen, J.C., Creyghton, E.J., Njo, S.L., van Koningsveld, H., van Bekkum, H.: On the remarkable behaviour of zeolite Beta in acid catalysis. Catal. Today, vol. 38, p. 205 (1997)

    Article  Google Scholar 

  3. van der Waal, J.C., Creyghton, E.J., Kunkeler, P.J., Tan, K. van Bekkum, H.: Beta-type zeolites as selective and regenerable catalysis in the Meerwein-Ponndorf-Verley reduction of carbonyl compounds. Topics Catal, vol. 4, p. 261 (1997)

    Article  Google Scholar 

  4. Creyghton, E.J., Ganeshie, S.D., Downing, R.S., van Bekkum, H.: Stereoselective Meerwein-Ponndorf-Verley and Oppenauer reactions catalysed by zeolite BEA. J. Mol. Catal. A. vol. 115, p. 457 (1997)

    Article  Google Scholar 

  5. Satterfield C.N.: Heterogeneous Catalysis in Industrial Practice, Krieger Publishing Company, Malabar, Florida, New York (1991)

    Google Scholar 

  6. Kunkeler, P.J., Zuurdeeg, B.J., van der Waal, J.C., van Bokhoven, J.A., Koningsberger, D.C., van Bekkum, H.: Zeolite Beta: The relationship between calcination procedure, aluminum configuration, and Lewis acidity. J. Catal. v. 180, p. 234 (1998)

    Article  Google Scholar 

  7. Bortnovsky, O., Sobalik, Z., Wichterlova, B., Bastl, Z.: Structure of Al-Lewos Site in Beta Zeolite Active in the Meerwein-Ponndorf-Verley Reduction of Ketone to Alcohol. J. Catal. v. 210, p. 171 (2002)

    Article  Google Scholar 

  8. Sand, L.B., Sacco, A., Thompson, R.W., Dixon, A.G.: Large zeolite crystals: their potential growth in space. Zeolites vol. 7, p. 387 (1987)

    Article  Google Scholar 

  9. Sacco Jr.,A.: Proc. Soc. Photo-opt. Instrum. Eng.: Large zeolites: why and how to grow in space. v. 1557, p. 6 (1991)

    Google Scholar 

  10. Akata, B., Yilmaz, B., Jirapongphan, S.S., Warywoda, J., Sacco Jr,A.: Characterization of zeolite Beta grown in microgravity. Micropor. Mesopor. Mater. v. 71, p. 1 (2004)

    Article  Google Scholar 

  11. Kiricsi, I., Flego, C., Pazzuconi, G., Parker Jr.W.O., Millini, R., Perego, C., Bellussi, G.: Progress toward Understanding Zeolite Beta Acidity: An IR and 27AI NMR Spectroscopic Study. J. Phys. Chem. v. 98, p. 4627 (1994)

    Article  Google Scholar 

  12. Perez-Pariente, J., Martens, J.A., Jacobs, P.A.: Crystallization Mechanism of Zeolite Beta From (TEA)//2O, NA//2O and K//2O Containing Aluminosilicate Gels. Applied Catal. v. 31, p. 35 (1987)

    Article  Google Scholar 

  13. Kaushik, V.K., Bhat, S.G.T., Corbin, D.R.: Surface composition and electronic structure of zeolites using X-ray photoelectron spectroscopy. Zeolites v. 13, p. 671 (1993)

    Article  Google Scholar 

  14. Collignon, F., Jacobs, P.A., Gorbet, P., Poncelet, G.: Investigation of the coordination state of aluminum in β zeolites by X-ray photoelectron spectroscopy. J. Phys. Chem. B v. 105, p. 6812 (2001)

    Article  Google Scholar 

  15. Borade, R., Sayari, A., Adnot, A., Kaliaguine, S.: XPS study of acid sites in dehydroxylated Y zeolites. J. Phys. Chem. v. 94, p. 5989 (1990)

    Article  Google Scholar 

  16. Akata, B., Warzywoda, J., Sacco Jr,A.: Gas Phase Meerwein-Ponndorf-Verley Reaction: Correlation of the 3665 cm-1 IR Band with theCis-Alcohol Selectivity. J. Catal. v. 222, p. 397 (2004)

    Article  Google Scholar 

  17. Bourgeat-Lami, E., Massiani, P., Di Renzo, F., Espiau, P., Fajula, F., des Courieres, T.: Study of the state of aluminum in zeolite-Beta. Appl. Catal. v. 72, p. 139 (1991)

    Article  Google Scholar 

  18. Kunkeler, P.J., Zuurdeeg, B.J., van der Waal, J.C., van Bokhoven, J.A., Koningsberger, D.C., van Bekkum, H.: Zeolite Beta: The relationship between Calcination Procedure, Aluminum Configuration, and Lewis Acidity. J. Catal. v. 180, p. 234 (1998)

    Article  Google Scholar 

  19. van Bokhoven, J.A., Koningsberger, D.C., Kunkeler, P., van Bekkum, H.: Influence of Steam Activation on Pore Structure and Acidity of Zeolite Beta: An Al K Edge XANES Study of Aluminum Coordination. J. Catal. v. 211, p. 540 (2002)

    Article  Google Scholar 

  20. Yang, C. Xu, Q.: States of aluminum in zeolite Beta and influence of acidic or basic medium. Zeolites v. 19, p. 404 (1997)

    Article  Google Scholar 

  21. Vimont, A., Thibault-Starzyk, F., Lavalley, J.C.: Infrared Spectroscopic Study of the Acidobasic Properties of Beta Zeolite. J. Phys. Chem. B. v. 104, p. 286 (2000)

    Article  Google Scholar 

  22. Jia, C., Massiani, C.P., Barthomeuf, D.: Characterization by infrared and nuclear magnetic resonance spectroscopies of calcined beta zeolite. J. Chem Soc. Faraday Trans. v. 89, p. 3659 (1993)

    Article  Google Scholar 

  23. Loeffler, E., Lohse, U., Peuker, C., Oehlmann, G., Kustov, L.M., Zholobenko, V.L., Kazansky, V.B.: Study of different states of nonframework aluminum in hydrothermally dealuminated HZSM-5 zeolites using diffuse reflectance i.r. spectroscopy. Zeolites v. 10, p. 266 (1990)

    Article  Google Scholar 

Download references

Author information

Authors and Affiliations

  1. Center for Advanced Microgravity Materials Processing, Department of Chemical Engineering, Northeastern University, 147 Snell Engineering Center, 02115, Boston, MA, USA

    Katherine S. Ziemer & Albert Sacco

  2. Central Laboratory, Middle East Technical University, 06531, Ankara, Turkey

    Burcu Akata

  3. Department of Chemical Engineering, Northeastern University, 342 Snell Engineering Center, 02115, Boston, MA, USA

    Trevor L. Goodrich

Authors
  1. Burcu Akata
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Trevor L. Goodrich
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Katherine S. Ziemer
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Albert Sacco
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Albert Sacco.

Rights and permissions

Reprints and permissions

About this article

Cite this article

Akata, B., Goodrich, T.L., Ziemer, K.S. et al. The catalytic activity of space versus terrestrial synthesized zeolite Beta catalysts in the Meerwein Ponndorf Verley Reactions: Support for PFAL as the Lewis active site for cis-alcohol selectivity. Microgravity sci. Technol. 19, 5–11 (2007). https://doi.org/10.1007/BF02911862

Download citation

  • Received:

  • Revised:

  • Accepted:

  • Issue Date:

  • DOI: https://doi.org/10.1007/BF02911862

Keywords

Search

Navigation