Structural and magnetic properties of zinc- and aluminum-substituted cobalt ferrite prepared by co-precipitation method

Article

DOI: 10.1007/s12043-008-0015-2

Cite this article as:
Alone, S.T. & Jadhav, K.M. Pramana - J Phys (2008) 70: 173. doi:10.1007/s12043-008-0015-2

Abstract

Spinal ferrites having the general formula Co1 − xZnxFe2 − xAlxO4 (x = 0.0, 0.1, 0.2, 0.3, 0.4, 0.5, 0.6) were prepared using the wet chemical co-operation technique. The samples were annealed at 800°C for 12 h and were studied by means of X-ray diffraction, magnetization and low field AC susceptibility measurements. The X-ray analysis showed that all the samples had single-phase cubic spinel structure. The variation of lattice constant with Zn and Al concentration deviates from Vegard’s law. The saturation magnetization σs and magneton number nB measured at 300 K using high field hysteresis loop technique decreases with increasing x, suggesting decrease in ferrimagnetic behaviour. Curie temperature TC deduced from AC susceptibility data decreases with x, suggesting a decrease in ferrimagnetic behaviour.

Keywords

Ferrite co-precipitation magnetization AC susceptibility 

PACS Nos

78.67.Bf 01.30.-y 85.70.Ge 

Copyright information

© Indian Academy of Sciences 2008

Authors and Affiliations

  1. 1.Shiv Chhatrapati CollegeAurangabadIndia
  2. 2.Department of PhysicsDr. B. A. Marathwada UniversityAurangabadIndia

Personalised recommendations