Zinc Ferrite Nanoparticles: New Preparation Method and Magnetic Properties

  • Original Paper
  • Published:
Journal of Superconductivity and Novel Magnetism Aims and scope Submit manuscript

Abstract

In this work, single phase zinc ferrite (ZnFe2 O 4) nanoparticles with a mean crystallite size of 12 nm were successfully prepared just by high energy wet milling of metallic Zn and Fe powders and water as the raw materials, without any subsequent heat treatments. Variation of the magnetization with respect to temperature was studied by Faraday balance. Room temperature M–H curve of the as-milled powder has an s-shape, which shows it has ferrimagnetic order. To investigate the effect of annealing on magnetic properties of the as-milled powder, it was annealed at different temperatures from 150 to 800 °C and characterized by XRD and magnetometry. The results show that cation distribution of the as-milled nanoparticles is different from that of the bulk zinc ferrite (normal spinel) and by annealing it changes drastically, and finally, it changes to that of the bulk one.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Fig. 1
Fig. 2
Fig. 3
Fig. 4

Similar content being viewed by others

References

  • Šepelák, V., Baabe, D., Mienert, D., Schultze, D., Krumeich, F., Litterst, F.J., Becker, K.D.: J. Magn. Magn. Mater. 257, 377 (2003)

    Article  ADS  Google Scholar 

  • Smit, J., Wijn, H.P.J.: Ferrites. Philips Technical Library, Eindhoven (1959)

  • Šepelák, V., Indris, S., Heitjans, P., Becker, K.D.: J. Alloys Compd. 776, 434–435 (2007)

    Google Scholar 

  • Shah, S. A., Hashim, M.U., Alam, S., Shamim, A.: J. Magn. Magn. Mater. 322, 375 (2010)

    Article  ADS  Google Scholar 

  • Tung, L.D., Kolesnichenko, V., Caruntu, G., Caruntu, D.: Physica B 319, 116 (2002)

    Article  ADS  Google Scholar 

  • Mukherjee, K., Majumder, S. B.: J. Appl. Phys. 106 (064), 912 (2009)

    Google Scholar 

  • Daqiang, G., Zhenhua, S., Yan, X., Jing, Z., Guijin, Y., Jinlin, Z., Xinhua, W., Desheng, X.: Nanoscale Res. Lett. 5, 1289 (2010)

    Article  Google Scholar 

  • Tamaura, Y., Kaneko, H.: Sol. Energy 78, 616 (2005)

    Article  ADS  Google Scholar 

  • Hongjin, L., Liang, M., Peng, Z., Dingning, K., Tianyou, P.: J. Mater. Chem. 20, 3665 (2010)

    Article  Google Scholar 

  • Yang, H., Xin-Yong, L., Qi-Dong, Z., Xie, Q., Guo-Hua, C.: Adv. Funct. Mater. 20, 2165 (2010)

    Article  Google Scholar 

  • Azam, A., Chaman, M., Naqvi, A.H.: Int. J. Nanoparticles 2, 388 (2009)

    Article  Google Scholar 

  • Wang, A.R., Li, J., Zhang, Q.M., Miao, H.: Adv. Mater. Res. 177, 32 (2011)

    Article  Google Scholar 

  • Maletin, M., Moshopoulou, E.G., Kontos, A.G., Devlin, E., Delimitis, A., Zaspalis, V.T., Nalbandian, L., Srdić, V.V.: J. Eur. Ceram. Soc. 27, 4391 (2007)

    Article  Google Scholar 

  • Changwa, Y., Qiaoshi, Z., Goya, G. F., Torres, T., Jinfang, L., Haiping, W., Mingyuan, G., Yuewu, Z., Youwen, W., Jiang, J. Z.: J. Phys. Chem. C. 111, 12274 (2007)

    Article  Google Scholar 

  • Yu, S., Fujino, T., Yoshimura, M.: J. Magn. Magn. Mater. 256, 420 (2003)

    Article  ADS  Google Scholar 

  • Li, F., Wang, H., Wang, L., Wang, J.: J. Magn. Magn. Mater. 309, 295 (2007)

    Article  ADS  Google Scholar 

  • Ozcan, S., Kaynar, B., Mutlu Can, M., Fırat, T.: Mater. Sci. Eng. B 121, 278 (2005)

    Article  Google Scholar 

  • Cullity, B.D.: Elements of X-ray Diffraction. Addison-Wesley, Reading, MA (1978)

    MATH  Google Scholar 

  • Roy, M.K., Verma, H.C.: J. Magn. Magn. Mater. 306, 98 (2006)

    Article  ADS  Google Scholar 

  • Šepelák, V., Wilde, L., Steinike, U., Becker, K. D.: Mater. Sci. Eng. A 865, 375–377 (2004)

    Google Scholar 

  • Šepelák, V., Becker, K.D.: Mater. Sci. Eng. A 861, 375–377 (2004)

    Google Scholar 

  • Šepelák, V., Tkacova, K., Boldyrev, V.V., Wigmann, S., Becker, K.D.: Physica B 617, 234–236 (1997)

    Google Scholar 

  • Atif, M., Hasanain, S.K., Nadeem, M.: Solid State Commun. 138, 416 (2006)

    Article  ADS  Google Scholar 

  • Shenoy, S.D., Joy, P.A., Anantharaman, M.R.: J. Magn. Magn. Mater. 269, 217 (2004)

    Article  ADS  Google Scholar 

Download references

Author information

Authors and Affiliations

Authors

Corresponding author

Correspondence to M. Mozaffari.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Mozaffari, M., Masoudi, H. Zinc Ferrite Nanoparticles: New Preparation Method and Magnetic Properties. J Supercond Nov Magn 27, 2563–2567 (2014). https://doi.org/10.1007/s10948-014-2625-x

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s10948-014-2625-x

Keywords

Navigation