Shock-induced and self-propagating high-temperature synthesis reactions in two powder mixtures: 5:3 Atomic ratio Ti/Si and 1:1 Atomic ratio Ni/Si

  • Published:
Metallurgical Transactions A Aims and scope Submit manuscript

Abstract

The conditions for initiation and propagation of the reaction forming the intermetallic compounds Ti5Si3 and NiSi from mixtures of elemental powders of varying porosity have been investigated using shock waves of different pressure and at atmospheric pressure using hot wire ignition in air and in an argon atmosphere. In each case, the reaction either went to completion or the powder remained essentially unreacted. The conditions for the initiation of the reaction in Ti/Si are sensitive to the presence of air. Two regimes of porosity and shock pressure are found for the Ti/Si mixture which cause complete reaction. A low-energy regime with a high initial porosity (producing a low shock pressure) with 0.1 torr of residual air triggers the reaction, while no reaction is observed with a 128 pct higher shock energy and a lower initial porosity (producing a higher shock pressure) when the residual air is replaced with argon. Hot wire ignition of porous Ti/Si powder at room temperature initiates a self-propagating high-temperature synthesis (SHS) reaction more easily in air than in an argon atmosphere, while the Ni/Si powder must be heated to allow the SHS reaction to propagate in high- or low-porosity mixtures in air. These observations are compared to published work on self-sustaining reactions in multilayer films. Reasons for the difference in behavior of the two powder mixtures are discussed.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. B.R. Krueger, A.H. Mutz, and T. Vreeland, Jr.: J. Appl. Phys., 1991, in press.

  2. F. Bordeaux and A.R. Yavari: J. Mater. Res., 1990, vol. 5, pp. 1656–61.

    CAS  Google Scholar 

  3. R. Sinclair: Mater. Trans. Jpn. Inst. Met., 1990, vol. 31, pp. 628–35.

    CAS  Google Scholar 

  4. K. Holloway and R. Sinclair: J. Appl. Phys., 1987, vol. 61, pp. 1359–64.

    Article  CAS  Google Scholar 

  5. A.A. Zenin, A.G. Merzhanov, and G.A. Nersisyan: Combust. Explos. Shock Waves, (Engl. Trans.), 1981, vol. 17, pp. 63–71.

    Article  Google Scholar 

  6. T. Boddington, P.G. Laye, J. Tipping, and D. Whalley: Combust. Flame, 1986, vol. 63, pp. 359–68.

    Article  CAS  Google Scholar 

  7. R.B. Schwarz, P. Kasiraj, and T. Vreeland, Jr.: in Metallurgical Applications of Shock-Wave and High-Strain-Rate Phenomena, L.E. Murr, K.P. Staudhammer, and M.A. Meyers, eds., Marcel Dekker, New York, NY, 1986, pp. 313-27.

    Google Scholar 

  8. W.F. Henshaw, A. Niiler, and T. Leete: ARBRL-MR-03354, Ballistics Research Laboratory, Aberdeen Proving Ground, Aberdeen, MD, 1984.

  9. Smithell’s Metals Reference Book, 6th ed., E.A. Brandes, ed., eh. 8, pp. 24-27.

  10. O.L. Anderson: J. Phys. Chem. Solids, 1966, vol. 27, p. 547.

    Article  CAS  Google Scholar 

  11. LASL Shock Hugoniot Data, P.S. Marsh, ed., University of California Press, Berkeley, CA, 1980.

  12. A.L. Ruoff: J. Appl. Phys., 1967, vol. 38, pp. 4976–80.

    Article  CAS  Google Scholar 

  13. J.P. Watt: Rev. Geophys. Space Phys., 1976, vol. 14, pp. 541–63.

    CAS  Google Scholar 

Download references

Author information

Authors and Affiliations

Authors

Additional information

This paper is based on a presentation made in the symposium “Reaction Synthesis of Materials” presented during the TMS Annual Meeting, New Orleans, LA, February 17–21, 1991, under the auspices of the TMS Powder Metallurgy Committee.

Rights and permissions

Reprints and permissions

About this article

Cite this article

Krueger, B.R., Mutz, A.H. & Vreeland, T. Shock-induced and self-propagating high-temperature synthesis reactions in two powder mixtures: 5:3 Atomic ratio Ti/Si and 1:1 Atomic ratio Ni/Si. Metall Trans A 23, 55–58 (1992). https://doi.org/10.1007/BF02660851

Download citation

  • Issue Date:

  • DOI: https://doi.org/10.1007/BF02660851

Keywords

Navigation