Kinetics and mechanism of oxidation of silicon nitride bonded silicon carbide ceramic

Rent the article at a discount

Rent now

* Final gross prices may vary according to local VAT.

Get Access

Abstract

Thermogravimetry (TG) has been used to study the oxidation of a commercial silicon nitride bonded silicon carbide (SNBSC) ceramic. The oxidation was studied in air and carbon dioxide atmospheres between 800 and 1300°C. TG/mass spectrometry (MS) shows that the silicon nitride bonding phase oxidises first. The kinetics follow a multi-stage mechanism with diffusion control. Carbon dioxide was found to be a more powerful oxidant than air at temperatures above 1050°C.

Zusammenfassung

Mittels Thermogravimetrie wurde die Oxidation einer handelsüblichen, siliziumnitridgebundenen Siliziumcarbidkeramik (SNBSC) untersucht. Die Oxidation wurde sowohl in Luft als auch in einer Kohlendioxidatmosphäre zwischen 800 und 1300°C untersucht. TG/MS zeigt, daß die Siliziumnitridphase als erste oxidiert wird. Die Reaktionskinetik folgt einem diffusionsbestimmten Mehrstufenmechanismus. Oberhalb 1050°C erwies sich Kohlendioxid als stärkeres Oxidationsmittel als Luft.