Abstract
The phase formation and grain growth of (Tl,Pb,Bi)(Sr,Ba)2Ca2Cu3O9−δ ceramics were investigated in the temperature range between 860°C and 1000°C. It was found that partial melting seems to improve the texture of the samples. The phase purity, however, is limited due to an incomplete re-precipitation process due to the formation of a liquid phase, which is already present above 885°C. The resulting grain growth exponent n, however, appears to differ from the classical exponent of 1/3 for the coexistence of a liquid phase in the temperature range between 885°C and 920°C. For the first time, the activation energy for the high-Tc Tl-1223 phase has been determined showing faster grain growth kinetics than for Y-123 and Bi-2223.
Similar content being viewed by others
REFERENCES
T. Sasaoka, A. Nomoto, M. Seido, T. Doi, T. Kamo, Jpn. J. Appl. Phys. 30 (1991) L1868
W. Mexner, S. Heede, K. Heinemann, B. Ullmann, F. Ladenberger, E. Schwarzmann, H.C. Freyhardt, Proc. IWCC 1994, Alpbach, World Scientific (1994) 513
R.S. Liu, D.N. Zheng, S.P. Ashworth, Appl. Phys. Lett. 60 (1992) 1019
R.S. Liu, S.F. Wu, D.S. Shy, S.F. Hu, D.A. Jefferson, Physica C 222 (1994) 278
R.E. Gladyshevskii, A. Perin, B. Hensel, R. Flükiger, Inst. Phys. Conf. 148 (1995) 479
R.E. Gladyshevskii, A. Perin, B. Hensel, R. Flükiger, R. Abraham, K. Lebbou, M.Th. Cohen-Adad, J.-L. Jorda, Physica C 255 (1995) 113
P.E.D. Morgan, T. Doi, R.M. Housley, J.R. Porter, Proc. 5th Int. Symp. Supercond. (1993) 391
X.D. Liu, H.T. Peng, Si.H. Zhou, Q.Y. Peng, G.W. Yang, Physica C 256 (1996) 353
Y.F. Li, Z.Z. Sheng, N. Chen, S.E. Dorris, M.T. Lanagan, K.C. Goretta, Mater. Res. Bull. 29 (1994) 1057
P.E.D. Morgan, M. Okada, T. Matsumoto, A. Soeta, Proc. 2nd Int. Symp. Supercond. (1989) 436
F.R. Rhines and K.R. Craig, Metall. Trans. 5 (1974) 413
G. F. Bolling, W.C. Winegard, Acta Metall. 6 (1958) 283
C.T. Chu, B. Dunn, J.Mater. Res. 5 (1990) 1819
L.E. Richards, H.A. Hoff, P.K. Aggarwal, J. Electr. Mat. 22 (1993) 1233
G. S. Grest, D. J. Srolovitz, M. P. Anderson, Acta Metall. 33 (1985) 520
J.-C. Grivel, R. Flükiger, J. Alloys Comp. 235 (1996) 53
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Heede, S., Ullrich, M., Freyhardt, H. et al. Phase Formation and Grain Growth Kinetics of High-Tc Superconducting Tl-1223 Ceramics. Journal of Superconductivity 11, 97–101 (1998). https://doi.org/10.1023/A:1022658602286
Published:
Issue Date:
DOI: https://doi.org/10.1023/A:1022658602286