Effects of Zirconia Phase on the Synthesis of Methanol over Zirconia-Supported Copper

Abstract

A study has been conducted to identify the influence of zirconia phase and copper to zirconia surface area on the activity of Cu/ZrO₂ catalysts for the synthesis of methanol from either CO/H₂ or CO₂/H₂. To determine the effects of zirconia phase, a pair of Cu/ZrO₂ catalysts was prepared on tetragonal (t-) and monoclinic (m-) zirconia. The zirconia surface area and the Cu dispersion were essentially identical for these two catalysts. At 548 K, 0.65 MPa, and H₂/CO_x= 3 (x = 1, 2), the catalyst prepared on m-ZrO₂ was 4.5 times more active for methanol synthesis from CO₂/H₂ than that prepared on t-ZrO₂, and 7.5 times more active when CO/H₂ was used as the feed. Increasing the surface area of m-ZrO₂ and the ratio of Cu to ZrO₂ surface areas further increased the methanol synthesis activity. In situ infrared spectroscopy and transient-response experiments indicate that the higher rate of methanol synthesis from CO₂/H₂ over Cu/m-ZrO₂ is due solely to the higher concentration of active intermediates. By contrast, the higher rate of methanol synthesis from CO/H₂ is due to both a higher concentration of surface intermediates and the more rapid dynamics of their transformation over Cu/ZrO₂.