Abstract
In order to acquire more knowledge of the performance of copper-bearing intrauterine devices (Cu-IUDs), corrosion behavior of copper in a simulated uterine fluid was investigated in the presence of proteins. The proteins studied included serum albumin, γ-globulin and hemoglobin. Electrochemical polarization resistance measurements indicated that, in all cases under study, the corrosion rate of copper declined with time and the proteins always increased the rate. Moreover, different kinds of protein showed different dependence of copper corrosion rate on protein level. Addition of serum albumin initially raised the copper corrosion rate; however, the higher albumin concentration resulted in less promotion of the corrosion. X-ray diffraction (XRD) of the specimen surface showed that, both in the presence and absence of serum albumin, cuprous oxide was the only corrosion product, even though at higher concentrations of albumin less cuprous oxide was formed. This implies that serum albumin does not alter the corrosion mechanism. Electrochemical cathodic reduction of the oxide film and chemical analysis of solution after corrosion testing proved that the proportion of soluble ionic copper in the whole corrosion products varied with the albumin level. The copper corrosion rate in the presence of γ-globulin or hemoglobin increased monotonically with increasing concentration of the protein. These three proteins shifted the corrosion potential of copper towards negative. It could be inferred that the proteins accelerated the anodic dissolution process of copper and hence enhanced its corrosion.
Similar content being viewed by others
References
Zhang CD, Xu NX, Yang BY. The corrosion behavior of copper in simulated uterine fluid. Corrosion Sci. 1996;38:635–41.
Xue HS, Xu NX, Zhang CD. Corrosion behavior of copper in a copper bearing uterine device in the presence of indomethacin. Contraception. 1998;57:49–53.
Xue HS, Xu NX, Zhang CD. Effect of stainless steel on corrosion behavior of copper in a copper-bearing intrauterine device. Adv Contracept. 1998;14:153–60.
Zhang CD, Xu NX, Lu JF, Ding CH, Yang BY. Study on corrosion of copper in artificially formulated fluid using electrochemical method. Reprod Contracept. 1995;15:28–32 (in Chinese).
Oster GK. Chemical reactions of the copper intrauterine device. Fertil Steril. 1972;23(1):18–23.
Lewis KM, Archer RD, Ginsberg AP, Rosencwaig A. The corrosion chemistry of copper intrauterine devices. Contraception. 1977;15(1):93–104.
Tsong YY, Nash HA. Effect of tarnish on copper release. Contraception. 1991;44(4):385–92.
Kosonen A. Corrosion of Copper in utero. In: Hafez ESE, Os van Wan, eds. Medicated Intrauterine Devices. Martinus Nijhoff Press, Amsterdam, pp. 22–9.
Kar AB, Engineer AD, Goel R, Kamboj VP, Dasgupta PR, Chowdhury SR. Effect of an intrauterine contraceptive device on biochemical composition of uterine fluid. Am J Obstet Gynecol. 1968;101(7):966–70.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Zhu, J., Xu, N. & Zhang, C. Characteristics of copper corrosion in simulated uterine fluid in the presence of protein. Advances in Contraception 15, 179–190 (1999). https://doi.org/10.1023/A:1006793231274
Issue Date:
DOI: https://doi.org/10.1023/A:1006793231274