Phosphorus-containing reactive agent for UV-curable flame-retardant wood coating

  • Published:
Journal of Coatings Technology and Research Aims and scope Submit manuscript

Abstract

An attempt to develop a phosphorus-based flame-retardant UV-curable agent (UV-RA) for coating application led to the synthesis of a reactive compound which can be used as crosslinker along with UV-curable epoxy acrylate oligomer to form a coating. UV-RA was characterized via FTIR, NMR, hydroxyl, and iodine values. Study based on the effects of varying amount of UV-RA incorporated in the formulation was investigated by checking thermal, mechanical, and flame-retardant properties. An enhancement in all the properties was observed with an increase in concentration of UV-RA and each coating containing UV-RA successfully portrayed flame-retardant properties. The highest loss on ignition (LOI) value obtained was 27 while the initial and final degradation temperatures increased along with the char yield. The mechanical properties did not vary much except for the low values for 20UV-RA.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10

Similar content being viewed by others

References

  1. Granzow, A, “Flame Retardation by Phosphorus Compunds.” Acc. Chem. Res., 5 (11) 177–183 (1978). https://doi.org/10.1177/0734904110395469

    Article  Google Scholar 

  2. García, M, Hidalgo, J, Garmendia, I, “Composites: Part A Wood – Plastics Composites with Better Fire Retardancy and Durability Performance.” Compos Part A., 40 1772–1776 (2009). https://doi.org/10.1016/j.compositesa.2009.08.010

    Article  Google Scholar 

  3. Mark, H, “Flammability,” Encyclo. Polym. Sci. Tech. Con., Wiley (2013).

  4. Chambhare, SU, Lokhande, GP, Jagtap, RN, “UV-Curable Behavior of Phosphorus- and Nitrogen-Based Reactive Diluent for Epoxy Acrylate Oligomer Used for Flame-Retardant Wood Coating.” J. Coat. Technol. Res., 13 (4) 703–714 (2016). https://doi.org/10.1007/s11998-015-9777-x

    Article  Google Scholar 

  5. Nelson, G, Kinson, P, Quinn, C, “Fire Retardant Polymers.” Ann. Review Mater. Sci., 4 391–414 (1974). https://doi.org/10.1146/annurev.ms.04.080174.002135

    Article  Google Scholar 

  6. Bourbigot, S, Duquesne, S, “Fire Retardant Polymers: Recent Developments and Opportunities.” J. Mater. Chem., 17 2283–2300 (2007). https://doi.org/10.1039/b702511d

    Article  Google Scholar 

  7. Bourbigot, S, Flambard, X, “Heat Resistance and Flammability of High Performance Fibres: A Review.” Fire Mater., 168 155–168 (2002). https://doi.org/10.1002/fam.799

    Article  Google Scholar 

  8. Wang, Z, Han, E, Ke, W, “Influence of Nano-LDHs on Char Formation and Fire-Resistant Properties of Flame-Retardant Coating.” Prog. Org. Coat., 53 (1) 29–37 (2005). https://doi.org/10.1016/j.porgcoat.2005.01.004

    Article  Google Scholar 

  9. Pearce, E, Liepins, R, “Flame Retardants.” Enviro. Health Persp., 11 59–69 (1975)

    Google Scholar 

  10. Troitzsch, J, “Overview of Flame Retardants,” Chem. Today., 16 (1998)

  11. Chen, X, Hu, Y, Jiao, C, Song, L, “Thermal and UV-Curing Behavior of Phosphate Diacrylate Used for Flame Retardant Coatings.” Prog. Org. Coat., 59 (4) 318–323 (2007)

    Article  Google Scholar 

  12. Maiti, S, Banerjee, S, Palit, S, “Phosphorus Containing Polymers.” Prog. Polym. Sci., 18 227–261 (1993)

    Article  Google Scholar 

  13. Huang, W, Chen, K, Yeh, J, Chen, K, “Curing and Combustion Properties of a PU-Coating System with UV-Reactive Phosphazene.” J. App. Polym. Sci., 85 1980–1991 (2002). https://doi.org/10.1002/app.10776

  14. Patil, DM, Phalak, GA, Mhaske, ST, “Design and Synthesis of Bio-Based UV Curable PU Acrylate Resin from Itaconic Acid for Coating Applications.” Des. Monomers Polym., 20 269–282 (2017). https://doi.org/10.1080/15685551.2016.1231045

    Article  Google Scholar 

  15. Lokhande, G, Chambhare, S, Jagtap, R, “Synthesis and Properties of Phosphate-Based Diacrylate Reactive Diluent Applied to UV-Curable Flame-Retardant Wood Coating.” J. Coat. Technol. Res., 14 255–266 (2017). https://doi.org/10.1007/s11998-016-9849-6

    Article  Google Scholar 

  16. Shang, D, Sun, X, Hang, J, “Flame Resistance, Physical and Mechanical Properties Of UV-Cured Hybrid Coatings Containing Low-Hydroxyl-Content Sols Via an Anhydrous Sol-Gel Process.” Prog. Org. Coat., 105 267–276 (2017). https://doi.org/10.1016/j.porgcoat.2017.01.015

    Article  Google Scholar 

  17. Wang, P, Yang, F, Li, L, Cai, Z, “Flame Retardancy and Mechanical Properties of Epoxy Thermosets Modified with a Novel DOPO-Based Oligomer.” Polym. Degrad. Stab., 129 156–167 (2016). https://doi.org/10.1016/j.polymdegradstab.2016.04.005

    Article  Google Scholar 

  18. Sonnier, R, Dumazert, L, Livi, S, “Flame Retardancy of Phosphorus-Containing Ionic Liquid Based Epoxy Networks.” Polym. Degrad. Stab., 134 186–193 (2016). https://doi.org/10.1016/j.polymdegradstab.2016.10.009

    Article  Google Scholar 

  19. Jeng, RJ, Shau, SM, Lin, JJ, “Flame Retardant Epoxy Polymers Based on All Phosphorus-Containing Components.” Eur. Polym. J., 38 683–693 (2012). https://doi.org/10.1016/S0014-3057(01)00246-4

    Article  Google Scholar 

  20. Wang S, Xu C, Liu Y, et al., "Vanillin-Derived High-Performance Flame Retardant Epoxy Resins: Facile Synthesis and Properties." (2017). https://doi.org/10.1021/acs.macromol.7b00097

  21. Chen, X, Jiao, C, “Thermal Degradation Characteristics of a Novel Flame Retardant Coating Using TG-IR Technique.” Polym Degrad Stab, 93 2222–2225 (2008). https://doi.org/10.1016/j.polymdegradstab.2008.09.005

    Article  Google Scholar 

  22. Quin, L, Ye, L, Xu, G, Liu, J, Polym Degrad Stab, 96 1118–1124 (2011)

    Article  Google Scholar 

  23. Chuan, S, Ying, L, Polymer (Guildf), 43 4277–4284 (2002)

    Article  Google Scholar 

  24. Choia, J, Seob, J, Khanc, S, Prog. Org. Coat., 71 110–116 (2011)

    Article  Google Scholar 

  25. Liu Y, Hsiue G, Lan C, Chiu Y, 8-Flame-Retardant Polyurethanes from Phosphorus-Containing. 1769–1780 (1996)

  26. Liu, YL, Hsiue, GH, Lan, CW, Chiu, YS, “Phosphorus-Containing Epoxy for Flame Retardance: IV. Kinetics and Mechanism of Thermal Degradation.” Polym Degrad Stab, 56 291–299 (1997). https://doi.org/10.1016/S0141-3910(96)00177-2

    Article  Google Scholar 

  27. Banerjee, S, Palit, SK, Maiti, S, “Phosphorus Containing Polymers. 3. Polyimidophosphonates.” J Polym Sci Part A - Polym Chem, 32 219–227 (1994)

    Article  Google Scholar 

  28. Castilla, E, Martín, N, Pardo, L, “Minimum Phi-Divergence Estimators for Multinomial Logistic Regression with Complex Sample Design.” AStA Adv Stat Anal, 102 381–411 (2018). https://doi.org/10.1007/s10182-017-0311-6

    Article  Google Scholar 

  29. Liu YL, Hsiue GH, Chiu YS, et al., "Synthesis and Flame-retardant Properties of Phosphorus-containing Polymers Based on Poly(4-hydroxystyrene)." J Appl Polym Sci, 59:1619–1625 (1996). https://doi.org/10.1002/(SICI)1097-4628(19960307)59:10<1619::AID-APP14>3.0.CO;2-R

  30. Liu Y, Hsiue G, Chiu Y, Properties of Phosphate-Based Epoxy Resins. Phosphate-based Epoxy Resins 565–574 (1996)

  31. Chao, P, Li, Y, Gu, X, et al., “Novel Phosphorus-Nitrogen-Silicon Flame Retardants and Their Application in Cycloaliphatic Epoxy Systems.” Polym Chem, 6 2977–2985 (2015). https://doi.org/10.1039/c4py01724b

    Article  Google Scholar 

  32. Qian, X, Song, L, Bihe, Y, et al., “Organic/Inorganic Flame Retardants Containing Phosphorus, Nitrogen and Silicon: Preparation and Their Performance on the Flame Retardancy of Epoxy Resins as a Novel Intumescent Flame Retardant System.” Mater Chem Phys, 143 1243–1252 (2014). https://doi.org/10.1016/j.matchemphys.2013.11.029

    Article  Google Scholar 

Download references

Author information

Authors and Affiliations

  1. Department of Polymer and Surface Engineering, Institute of Chemical Technology, Mumbai, India

    Saket Mulge, Siddhesh Mestry, Durva Naik & Shashank Mhaske

Authors
  1. Saket Mulge
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Siddhesh Mestry
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Durva Naik
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Shashank Mhaske
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Shashank Mhaske.

Additional information

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Mulge, S., Mestry, S., Naik, D. et al. Phosphorus-containing reactive agent for UV-curable flame-retardant wood coating. J Coat Technol Res 16, 1493–1502 (2019). https://doi.org/10.1007/s11998-019-00224-3

Download citation

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s11998-019-00224-3

Keywords

Search

Navigation