Abstract
A superplastic INCONEL 718 superalloy was brazed with a Ni-P and a Ni-Cr-P amorphous filler metal. The effects of applied pressure on the bonding strength, microhardness, and corrosion resistance were studied. The results showed that the brazements with Ni-Cr-P filler metal have higher bonding strength and better corrosion resistance than those with Ni-P filler metal using a conventional brazing method without applied pressure. When brazing was conducted under applied pressure, the bonding strength increased with applied pressure for the brazements with both filler metals. This was caused by a decrease of intermetallic phase through ejection of the liquid phase enriched with melting temperature depressants in the molten filler metals from the joint clearance. Corrosion tests show that these brazements failed at the brazed joint and at the grain boundaries in the region adjacent to the brazement.
Similar content being viewed by others
References
D. Bose, A. Datta, A. Rabinkin, and N.J. De Cristofaro: Weld. Res. Suppl., 1986, vol. 65, pp. 23s-29s.
B. Grushko and B.Z. Weiss: Metall. Trans. A, 1984, vol. 15A, pp. 609–20.
A. Rabinkin and S. Pounds: Weld. J., 1988, vol. 67, pp. 33–45.
R. Dammer: in Beitrag zur Bewertung Mechanischer Eigenschaften Hochtemperaturgelöteter Superlegierungen, Deutscher Verlag für Schweißtechnik (DVS), Düsseldorf, 1986, pp. 61–66.
G.D. Smith and H.L. Flower: Industrial Heat., 1995, Apr., pp. 47–49.
K.H. Holko and T.J. Moore: Weld. Res. Suppl., 1972, vol. 51, pp. 81s-89s.
Binary Alloy Phase Diagrams, T.B. Massalski, ed., ASM, Metals Park, OH, 1986, vol. 2, pp. 1738-39.
Principles of Soldering and Brazing, 1st ed., G. Humpston and D.M. Jacobson, eds., ASM INTERNATIONAL, Materials Park, OH, 1993, pp. 111–44.
M.H. Slobada: Weld. Met. Fabr., 1961, vol. 7, pp. 291–96.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Yeh, M.S., Chuang, T.H. Effects of applied pressure on the brazing of superplastic INCONEL 718 superalloy. Metall Mater Trans A 28, 1367–1376 (1997). https://doi.org/10.1007/s11661-997-0273-5
Received:
Issue Date:
DOI: https://doi.org/10.1007/s11661-997-0273-5