Abstract
The microstructural evolution and mechanical properties were examined in a Ni-based superalloy, TMW-4, with high Co and Ti contents at temperatures ranging from 700 °C to 1200 °C for various times up to 1000 hours. The results showed that solution treatments (temperatures: from 1100 °C to 1200 °C; time: 4 hours) essentially affected the fraction and size of primary and secondary γ′ precipitations and grain size. No η-Ni3Ti phase was observed in all solution heat-treatment samples. On the other hand, small amounts of η phase were observed in the samples after homogenization at 1220 °C and aging at temperatures ranging from 1000 °C to 1175 °C. Based on the investigations, a time-temperature-transition (TTT) curve for the η-phase formation was constructed. These microstructural effects were successfully combined to obtain an increase of tensile properties in terms of both strength and ductility.
Similar content being viewed by others
Notes
Inconel and Ninomic are trademarks of Inco. alloys International, Inc., Huntington, WV.
CMSX is a trademark of Cannon-Muskegon Co., Muskegon, MI
PHILIPS is a trademark of Philips Electronic Instruments Corp., Mahwah, NJ.
References
C.Y. Cui, Y.F. Gu, H. Harada, A. Sato: Metall. Mater. Trans. A, 2005, vol. 36A, pp. 2921–27
C.Y. Cui, Y.F. Gu, H. Harada, D.H. Ping, A. Sato: Metall. Mater. Trans. A, 2006, vol. 37A, pp. 3183–90
H. Harada, Y.F. Gu, C.Y. Cui, A. Sato, M. Osawa, and T. Kobayashi: Japanese Patent 2004–350116
C.Y. Cui, Y.F. Gu, D.H. Ping, H. Harada, T. Fukuda: Mater. Sci. Eng. A, 2008, vol. 485, pp. 651–56
M.C. Hardy, B. Zirbel, G. Shen, R. Shankar: in Superalloys, K.A. Green, T.M. Pollock, H. Harada, T.E. Howson, R.C. Reed, J.J. Schirra, S. Walston, eds., TMS, Warrendale, PA, 2004, pp. 83–90
T. Fukuda, A. Mitsuhashi, K. Kato, Y. Gu, and H. Harada: JIM Spring Meeting at Chiba, The Japan Institute Metals, Sendai Japan, 2007, p. 141
D. Raynor, J.M. Silcock: Met. Sci. J., 1970, vol. 4, pp. 121–29
Y. Gu, H. Harada, C. Cui, D. Ping, A. Sato, J. Fujioka: Scripta Mater., 2006, vol. 55 (9), pp. 815–18
J. Mao, K.M. Chang, W.H. Yang, K. Ray, S.P. Vaze, D. Furrer: Metall. Mater. Trans. A, 2001, vol. 32, pp. 2441–52
C.Y. Cui, Y.F. Gu, H. Harada, and T. Fukuda: TMS 2007 Annual Meeting & Exhib., TMS, Warrendale, PA, Feb. 25–Mar. 1, 2007, p. 107
J.C. Zhao, V. Ravikumar, A.M. Beltran: Metall. Mater. Trans. A, 2001, vol. 32A, pp. 1271–82
S.Q. Zhao, J.X. Dong, X.S. Xie, G. Smith, S.J. Patel: in Superalloys, K.A. Green, T.M. Pollock, H. Harada, T.E. Howson, R.C. Reed, J.J. Schirra, S. Walston, eds., TMS, Warrendale, PA, 2004, pp. 63–72
G.E. Fuchs, B.A. Boputwell: Mater. Sci. Eng. A, 2002, vol. 333A, pp. 72–79
ITOCHU Techno-Solustions Corporation, http://www.engineering-eye.com/THERMOCALC/db/index.html
C.T. Sims, N.S. Stoloff, W.C. Hagel: Superalloy II, John Wiley & Sons, New York, NY, 1987
S.M. Seo, I.S. Kim, J.H. Lee, C.Y. Jo, H. Miyahara, K. Ogi: Metall. Mater. Trans. A, 2007, vol. 38A, pp. 883–93
D. Furrer, H. Fecht: Scripta Mater., 1999, vol. 40 (11), pp. 1215–20
K. Harris, G.L. Erickson, R.E. Schwer: Superalloys, M. Gell, C.S. Kortovich, R.H. Bricknell, W.B. Knet, J.F. Radavich, eds., TMS, Warrendale, PA, 1984, pp. 221–30
J. Groh: Superalloys, T.M. Pollock, R.D. Kissinger, R.R. Bowman, K.A. Green, M. Mclean, S.L. Olson, J.J. Schirra, eds., TMS, Warrendale, PA, 2000, pp. 621–26
Author information
Authors and Affiliations
Corresponding author
Additional information
Manuscript submitted April 1, 2008.
Rights and permissions
About this article
Cite this article
Cui, C., Gu, Y., Ping, D. et al. Microstructural Evolution and Mechanical Properties of a Ni-Based Superalloy, TMW-4. Metall Mater Trans A 40, 282–291 (2009). https://doi.org/10.1007/s11661-008-9746-4
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11661-008-9746-4