Tensile Properties of Unsaturated Polyester and Epoxy Resin Reinforced with Recycled Carbon-Fiber-Reinforced Plastic

  • Published:
Applied Composite Materials Aims and scope Submit manuscript

Abstract

To better understand the mechanical properties of recycled carbon-fiber-reinforced plastic (rCFRP), CFRP crushed into small pieces was mixed randomly in different proportions (0–30 wt%) with two different resins: unsaturated polyester and epoxy resin. Two different sizes of crushed CFRP were used: 0.1 mm × 0.007 mm (milled CFRP) and 30 mm × 2 mm (chopped CFRP). The tensile strength of rCFRP was found to depend on both the proportion and the size of the CFRP pieces. It increased with increasing proportion of chopped CFRP, but decreased with increasing proportion of milled CFRP. There was no clear dependence of the tensile strength on the resin that was used. A low fracture strain was found for rCFRP samples made with chopped CFRP, in contrast to those made with milled CFRP. The fracture strain was found to increase with increasing content of milled CFRP up to 20 wt%, at which point, coalescence of existing microvoids occurred. However, there was a reduction in fracture strain for rCFRP with 30 wt% of milled CFRP, owing to the formation of defects (blow holes). Overall, the fracture strain was higher for rCFRPs based on epoxy resin than for those based on unsaturated polyester with the same CFRP content, because of the high ductility of the epoxy resin. The different tensile properties reflected different failure characteristics, with the use of chopped CFRP leading to a complicated rough fracture surface and with milled CFRP causing ductile failure through the presence of tiny dimple-like fractures. However, for a high content of milled CFRP (30 wt%), large blow holes were observed, leading to low ductility.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5

Similar content being viewed by others

References

  1. Wang, Y., Cui, X., Ge, H., Yang, Y., Wang, Y., Zhang, C., Li, J., Deng, T., Qin, Z., Hou, X.: ACS Sustain. Chem. Eng. 3, 3332–3337 (2015)

    Article  Google Scholar 

  2. Yamaguchi, K., Kitano, A.: Development in composites technology for reduction of environmental load II: recycle method for CFRP. J. Soc. Mater. Sci. Jpn. 57, 747–752 (2008)

    Article  Google Scholar 

  3. Park, J.M., Kwon, D.-J., Wang, Z.-J., Gu, G.-Y., DeVries, K.L.: Effect of thermal treatment temperatures on the reinforcing and interfacial properties of recycled carbon fiber-phenolic composites. Compos. Part A. 47, 156–164 (2013)

    Article  Google Scholar 

  4. Ogi, K., Nishikawa, T., Okano, Y., Taketa, I.: Mechanical properties of ABS resin reinforced with recycled CFRP. Adv. Compos. Mater. 16, 181–194 (2007)

    Article  Google Scholar 

  5. Huh, J.S., Hwang, W.: Fatigue life prediction of circular notched CFRP laminates. Comput. Struct. 44, 163–168 (1999)

    Article  Google Scholar 

  6. Okayasu, M., Yamazaki, T., Ota, K., Ogi, K., Shiraishi, T.: Mechanical properties and failure characteristics of a recycled CFRP under tensile and cyclic loading. Int. J. Fatigue. 55, 257–267 (2013)

    Article  Google Scholar 

  7. Pimenta, S., Pinho, S.T.: Recycling carbon fibre reinforced polymers for structural applications: technology review and market outlook. Waste Manag. 31, 378–392 (2011)

    Article  Google Scholar 

Download references

Acknowledgments

The CFRP samples and technical support were provided by Nippon Steel and Sumikin Materials Co. Ltd. (Mr Yuya Hidekuma).

Author information

Authors and Affiliations

Authors

Corresponding author

Correspondence to Mitsuhiro Okayasu.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Okayasu, M., Kondo, Y. Tensile Properties of Unsaturated Polyester and Epoxy Resin Reinforced with Recycled Carbon-Fiber-Reinforced Plastic. Appl Compos Mater 25, 561–568 (2018). https://doi.org/10.1007/s10443-017-9635-3

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s10443-017-9635-3

Keywords

Navigation