Abstract
Pillared clay-based superabsorbents (PILC-SA) were synthesized by using Al pillared-montmorillonite K10 and KSF via graft copolymerization reaction of acrylic acid (AA). Swelling behavior of pillared clay-based superabsorbent films in distilled water and at different pH values were investigated at room temperature. It was also obtained that Al-KSF and Al-K10 based superabsorbents were pH dependent and showed a reversible swelling behavior. Water absorbency of Al-KSF based superabsorbent was higher than that of Al-K10 based one. SEM, FTIR, and XRD analysis were conducted for further characterization of the PILC-SA. FTIR analyses lead to ester formation between PILC and SA. XRD revealed the basal spacing of the pillared clays before and after in situ incorporation indicating that the morphology of the superabsorbent was exfoliated and the layers of clay dispersed on the composite.
Similar content being viewed by others
References
Li A, Zhang J, Wang A (2005) Synthesis, characterization and water absorbency properties of poly(acrylicacid)/sodium humate superabsorbent composite. Polym Adv Technol 16:675–680
Yao KJ, Zhou WJ (1994) Synthesis and water absorbency of the copolymer of acrylamide with anionic monomers. J Appl Polym Sci 53:1533–1538
Zhou WJ, Yao KJ, Kurth MJ (1996) Synthesis and swelling properties of the copolymer of acrylamide with anionic monomers. J Appl Polym Sci 62:911–915
Tsubakimoto T, Shimomura T, Kobabyashi H (1987) Japanese Patent 62,149-335
Miura Y, Hirano K, Nate T, Kambayashi T, Ohtsuka M, Nagai T (1991) European Patent 440: 256
Tanaka H, Kambayashi T, Sugiyama Y, Nagai T, Nagata K, Kubota K, Hirano K (1992) European Patent 501:482
Walker CO (1987) US Patent 4: 664 816
Colombo P (1993) Swelling-controlled release in hydrogel matrices for oral route. Adv Drug Deliv Rev 11:37–57
Dong LC, Hoffman AS (1991) A novel approach for preparation of pH-sensitive hydrogels for enteric drug delivery. J Control Release 15:141–152
Zhang J, Li A, Wang AQ (2005) Study on superabsorbent composite. V. Synthesis, swelling behaviors and application of poly(acrylic acid-co-acrylamide)/sodium humate/attapulgite superabsorbent composite. Polym Adv Technol 16:813–820
Wu JH, Wei YL, Lin SB (2003) Study on starch-graft-acrylamide/mineral powder superabsorbent composite. Polymer 44:6513–6520
Lee WF, Yang LG (2004) Superabsorbent polymeric materials. XII. Effect of montmorillonite on water absorbency for poly(sodium acrylate) and montmorillonite nanocomposite superabsorbents. J Appl Polym Sci 92:3422–3429
Kabiri K, Zohuriaan-Mehr MJ (2004) Porous superabsorbent hydrogel composites: synthesis, morphology and swelling rate. Macromol Mater Eng 289:653–661
Su XF, Zhang G, Xu K, Wang J, Song C, Wang P (2008) The effect of MMT/modified MMT on the structure and performance of the superabsorbent composite. Polym Bull 60:69–78
Li A, Wang AQ, Chen JM (2004) Studies on poly(acrylic acid)/attapulgite superabsorbent composite. I. Synthesis and characterization. J Appl Polym Sci 92:1596–1603
Wang WB, Zheng YA, Wang AQ (2008) Syntheses and properties of superabsorbent composites based on natural guar gum and attapulgite. Polym Adv Technol 19:1852–1859
Lin J, Wu J, Yang Z, Pu M (2001) Synthesis and properties of poly(acrylic acid)/mica superabsorbent nanocomposite. Macromol Rapid Commun 22:422–424
Wu J, Lin J, Zhou M, Wei C (2000) Synthesis and properties of starch-graft-polyacrylamide/clay superabsorbent composite. Macromol Rapid Commun 21:1032–1034
Zhang Y, Fan L, Zhao P, Zhang L, Chen H (2008) Preparation of nanocomposite superabsorbents based on hydrotalcite and poly (acrylic-co-acrylamide) by inverse suspension polymerization. Comp Interfaces 15(7–9):747–757
Lothenbach B, Furrer G, Schulin R (1997) Immobilisation of heavy metals by polynuclear aluminium and montmorillonite compounds. Environ Sci Technol 31:1452–1462
Ding Z, Zhu HY, Greenfield PF, Lu GQ (2001) Characterization of pore structure and coordination of titanium in TiO2 and SiO2-TiO2 sol-pillared clays. Colloid Interface Sci 238:267–272
Ding Z, Kloprogge JT, Frost R, Zhu LH (2001) Porous clays and pillared clays-based catalysts. Part 2: a review of the catalytic and molecular sieve applications. J Porous Mater 8:273–293
Wan T, Lin J, Li X, Xiao W (2008) Preparation of epoxy-silica-acrylate hybrid coatings. Polym Bull 59:749–758
Zhang Y, Fan L, Cheng L, Zhang L, Chen H (2009) Preparation and morphology of high-performance exfoliated poly (sodium acrylate)/hydrotalcite nanocomposite superabsorbents. Polym Eng Sci 49:264–271
El-Hamshary H (2007) Synthesis and water sorption studies of pH sensitive poly(acrylamide-co-itaconic acid) hydrogels. Eur Polym J 43:4830–4838
Kabiri K, Zohuriaan Mehr MJ (2003) Superabsorbent hydrogel composites. Polym Adv Technol 14:438–444
Seki Y, Torgürsül A, Yurdakoc K (2007) Preparation and characterization of poly(acrylic acid)-iron rich smectite superabsorbent composites. Polym Adv Technol 18:477–482
Zhang J, Wang A (2007) Study on superabsorbent composites. IX: synthesis, characterization and swelling behaviors of polyacrylamide/clay composites based on various clays. React Funct Polym 67(8):737–745
Acknowledgments
The authors thank the scholarship for Zehra Bekçi Molu supported by TÜBİTAK MÜNİR BİRSEL Foundation/Turkey. The authors are also grateful to Research Foundation of Dokuz Eylül University (Project No: 2007.KB.FEN.028) for financial support.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Molu, Z.B., Seki, Y. & Yurdakoç, K. Preparation and characterization of poly(acrylic acid)/pillared clay superabsorbent composite. Polym. Bull. 64, 171–183 (2010). https://doi.org/10.1007/s00289-009-0155-7
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00289-009-0155-7