Effect of molecular weight of urea–formaldehyde resins on their cure kinetics, interphase, penetration into wood, and adhesion in bonding wood

  • Original
  • Published:
Wood Science and Technology Aims and scope Submit manuscript

Abstract

In this study, the effect of the molecular weight (MW) of urea–formaldehyde (UF) resins on their cure kinetics, interphase, penetration into wood, and adhesion strength was evaluated for the first time, to understand their contribution to cohesion and adhesion in bonding wood. UF resins with two final formaldehyde-to-urea (F/U) molar ratios (1.0 and 1.2) were prepared as low-viscosity resin (LVR) and as high-viscosity resin (HVR) through viscosity control. Five LVR/HVR blending ratios (100:0, 75:25, 50:50, 25:75, and 0:100) were used to obtain UF resins with different MW distributions and average MWs and, hence, different viscosities for the two molar ratios. As the viscosity during the condensation phase increased, the MW increased while the gelation time and the low molecular weight fraction decreased. The resins with F/U molar ratio of 1.2 had higher MW and activation energy than those with F/U molar ratio of 1.0. Isoconversional analysis showed that the 1.0 F/U molar ratio resin went through a multiple-step process in their curing mechanism, unlike the 1.2 F/U molar ratio resin, whose cohesion during bond formation was likely affected by the higher F content. As the MW increased, the resins with 1.0 and 1.2 F/U molar ratios exhibited the highest maximum storage modulus (E′max), greatest depth of resin penetration, thinnest bond-line, and highest adhesive strength at apparent weight-averaged Mw of 2000–2400 g/mol for the 1.0 F/U molar ratio resins (according to mixing ratios LVR/HVR = 50:50 and 25:75) and 3500–4500 g/mol for the 1.2 F/U molar ratio resins (again according to mixing ratios LVR/HVR = 50:50 and 25:75). These results suggest that the MW of UF resins has a big impact on cure kinetics that contributes to their cohesion behavior, while it also affects E′max, the depth of resin penetration, and the bond-line thickness, which all contribute to their adhesion behavior.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10
Fig. 11
Fig. 12

Similar content being viewed by others

References

  • de Jong JI, de Jonge J (1952) The reaction of urea with formaldehyde. Rec Trav Chim Pays-Bas 71:643–661

    Article  Google Scholar 

  • de Jong JI, de Jonge J, Eden HAK (1953) The formation of trihydroxymethyl urea. Rec Trav Chim Pays-Bas 72:88–90

    Article  Google Scholar 

  • Dunky M (1998) Urea–formaldehyde (UF) adhesive resins for wood. Int J Adhes Adhes 18(2):95–107

    Article  CAS  Google Scholar 

  • Ellis S (1993) The performance of waferboard bonded with powdered phenol-formaldehyde resins with selected molecular weight distributions. For Prod J 43(2):66–68

    CAS  Google Scholar 

  • Fan D, Li J, Mao A (2006) Curing characteristics of low mole ratio urea–formaldehyde resins. J Adhes Interface 7(4):45–52

    Google Scholar 

  • Ferra JM, Henriques A, Mendes AM, Costa MRN, Carvalho LH, Magalhães FD (2012) Comparison of UF synthesis by alkaline-acid and strongly acid processes. J Appl Polym Sci 123(3):1764–1772

    Article  CAS  Google Scholar 

  • Gavrilović-Grmuša I, Dunky M, Miljković J, Djiporović-Momčilović M (2010a) Radial penetration of urea–formaldehyde adhesive resins into beech (Fagus Moesiaca). J Adhes Sci Technol 24(8–10):1753–1768

    Article  CAS  Google Scholar 

  • Gavrilović-Grmuša I, Miljković J, Ðiporović-Momčilović M (2010b) Influence of the degree of condensation on the radial penetration of urea–formaldehyde adhesives into silver fir (Abies alba, Mill.) Wood Tissue. J Adhes Sci Technol 24(8–10):1437–1453

    Article  CAS  Google Scholar 

  • Gavrilović-Grmuša I, Dunky M, Miljković J, Điporović-Momčilović M (2012) Influence of the viscosity of UF resins on the radial and tangential penetration into poplar wood and on the shear strength of adhesive joints. Holzforschung 66:849–856

    Article  Google Scholar 

  • Gavrilović-Grmuša I, Dunky M, Djiporović-Momčilović M, Popović M, Popović J (2016) Influence of pressure on the radial and tangential penetration of adhesive resin into poplar wood and on the shear strength of adhesive joints. BioResources 11(1):2238–2255

    Article  Google Scholar 

  • Gu JY, Higuchi M, Morita M, Hse CY (1995) Synthetic conditions and chemical structures of urea–formaldehyde resins. I. Properties of the resins synthesized by three different procedures. Mok Gakk 41(12):1115–1121

    CAS  Google Scholar 

  • He G, Riedl B (2003) Phenol–urea–formaldehyde cocondensed resol resins: their synthesis, curing kinetics, and network properties. J Polym Sci Part B Polym Phys 41(16):1929–1938

    Article  CAS  Google Scholar 

  • Hse CH (1971) Properties of phenolic adhesives as related to bond quality in southern pine plywood. For Prod J 21(1):44–52

    CAS  Google Scholar 

  • Hse CY, Xia ZY, Tomita B (1994) Effects of reaction pH on properties and performance of urea–formaldehyde resins. Holzforschung 48(6):527–532

    Article  CAS  Google Scholar 

  • Jeong B, Park BD (2016) Measurement of molecular weights of melamine-urea–formaldehyde resins and their influences to properties of medium density fiberboards. J Korean Wood Sci Technol 44(6):913–922

    Article  Google Scholar 

  • Jeong B, Park BD (2017) Effect of analytical parameters of gel permeation chromatography on molecular weight measurements of urea–formaldehyde resins. J Korean Wood Sci Technol 45(4):471–481

    Google Scholar 

  • Jeremejeff J (2012) Investigation of UF-resins-the effect of the formaldehyde/urea mole ratio during synthesis. Master of Science Thesis, KTH Royal Institute of Technology, Stockholm, Sweden

  • Johnson SE, Kamke FA (1992) Quantitative analysis of gross adhesive penetration in wood using fluorescence microscopy. J Adhes 40:47–61

    Article  CAS  Google Scholar 

  • Korean Standard Association (2016) Ordinary plywood, KS F 3101, KSA Seoul

  • Kumar RN, Han TL, Rozman HD, Daud WRW, Ibrahim MS (2007) Studies in the process optimization and characterization of low formaldehyde emission urea–formaldehyde resin by response surface methodology. J Appl Polym Sci 103(4):2709–2719

    Article  CAS  Google Scholar 

  • Laborie MPG, Salmén L, Frazier CE (2006) A morphological study of the wood/phenol–formaldehyde adhesive interphase. J Adhes Sci Technol 20(8):729–741

    Article  CAS  Google Scholar 

  • Meyer B, Johns WE, Woo JK (1980) Formaldehyde release from sulfur-modified urea–formaldehyde resin system. For Prod J 30:24–31

    CAS  Google Scholar 

  • Nearn WT (1974) Application of ultrastructure concept in industrial wood products research. Wood Sci 6(3):285–293

    Google Scholar 

  • Nuryawan A, Park BD, Singh AP (2014a) Comparison of thermal curing behavior of liquid and solid urea–formaldehyde resins with different formaldehyde/urea mole ratios. J Therm Anal Calorim 118(1):397–404

    Article  CAS  Google Scholar 

  • Nuryawan A, Park BD, Singh AP (2014b) Penetration of urea–formaldehyde resins with different formaldehyde/urea mole ratios into softwood tissues. Wood Sci Technol 48(5):889–902

    Article  CAS  Google Scholar 

  • Park BD, Causin V (2013) Crystallinity and domain size of cured urea–formaldehyde resin adhesives with different formaldehyde/urea mole ratios. Eur Polym 49:532–537

    Article  CAS  Google Scholar 

  • Park BD, Jeong HW (2011) Hydrolytic stability and crystallinity of cured urea–formaldehyde resin adhesives with different formaldehyde/urea mole ratios. Int J Adhes Adhes 31(6):524–529

    Article  CAS  Google Scholar 

  • Park BD, Kim JW (2008) Dynamic mechanical analysis of urea–formaldehyde resin adhesives with different formaldehyde-to-urea molar ratios. J Appl Polym Sci 108:2045–2051

    Article  CAS  Google Scholar 

  • Park BD, Riedl B, Hsu EW, Shields J (1998) Effects of weight average molecular mass of phenol–formaldehyde adhesives on medium density fiberboard performance. Holz Roh-Werkst 56(3):155–161

    Article  CAS  Google Scholar 

  • Park BD, Kang EC, Park JY (2006a) Differential scanning calorimetry of urea–formaldehyde adhesive resins, synthesized under different pH conditions. J Appl Polym Sci 100(1):422–427

    Article  CAS  Google Scholar 

  • Park BD, Kang EC, Park JY (2006b) Effects of formaldehyde to urea mole ratio on thermal curing behavior of urea–formaldehyde resin and properties of particleboard. J Appl Polym Sci 101(3):1787–1792

    Article  CAS  Google Scholar 

  • Samaržija-Janović S, Javanović V, Konstantinović S, Marković G, Marinović-Cincović M (2011) Thermal behavior of modified urea–formaldehyde resins. J Therm Anal Calorim 104:1159–1166

    Article  CAS  Google Scholar 

  • Starink MJ (2003) The determination of activation energy from linear heating rate experiments: a comparison of the accuracy of isoconversion methods. Thermochim Acta 404:163–176

    Article  CAS  Google Scholar 

  • Stefke B, Dunky M (2006) Catalytic influence of wood on the hardening behavior of formaldehyde-based resin adhesives used for wood-based panels. J Adhes Sci Technol 20(8):761–785

    Article  CAS  Google Scholar 

  • Tarkow H, Feist WC, Southerland CF (1966) Penetration versus molecular size—interaction of wood with polymeric materials. For Prod J 16(10):61–65

    CAS  Google Scholar 

  • Vyazovkin S (2000) Kinetic concepts of thermally stimulated reactions in solids: a view from a historical perspective. Int Rev Phys Chem 19(1):45–60

    Article  CAS  Google Scholar 

  • Vyazovkin S (2001) Modification of the integral isoconversional method to account for variation in the activation energy. J Comput Chem 22(2):178–183

    Article  CAS  Google Scholar 

  • Vyazovkin S, Burnham AK, Criado JM, Perez-Maqueda LA, Popescu C, Sbirrazzuoli N (2011) ICTAC kinetics committee recommendations for performing kinetic computations on thermal analysis data. Thermochim Acta 520:1–19

    Article  CAS  Google Scholar 

  • Wilson JB, Krahmer RL (1978) The wetting and penetration of phenolic and lingo-sulfonate resins as possible indicators of bond strength for board. In: Proceedings of the 12th international particle, pp 305–315

  • Wisanrakkit G, Gillham JK (1990) The glass transition temperature (Tg) as an index of chemical conversion for a high-Tg amine/epoxy system: chemical and diffusion- controlled reaction kinetics. J Appl Polym Sci 41:2885–2929

    Article  CAS  Google Scholar 

Download references

Acknowledgements

This work was supported by the Basic Science Research Program through the National Research Foundation (NRF) of Korea, funded by the Ministry of Education, Science and Technology (Grant #2016R1D1A1A09917782).

Author information

Authors and Affiliations

  1. Department of Wood and Paper Sciences, Kyungpook National University, Daegu, 41566, Republic of Korea

    Bora Jeong & Byung-Dae Park

Authors
  1. Bora Jeong
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Byung-Dae Park
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Byung-Dae Park.

Additional information

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Jeong, B., Park, BD. Effect of molecular weight of urea–formaldehyde resins on their cure kinetics, interphase, penetration into wood, and adhesion in bonding wood. Wood Sci Technol 53, 665–685 (2019). https://doi.org/10.1007/s00226-019-01092-1

Download citation

  • Received:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s00226-019-01092-1

Search

Navigation